Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.71 g/cm³ Show Material materials with Density of 2.71 g/cm³ | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
2.71 g/cm³ Show Material materials with Density of 2.71 g/cm³ | H18 | ||
2.8 g/cm³ Show Material materials with Density of 2.8 g/cm³ | H18 |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 60.0 MPa Show Material materials with Bending Fatigue Strength of 60.0 MPa | H18 | AA Standards | ||
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | ||
69 GPa Show Material materials with Elastic modulus of 69 GPa | H18 | ||||
Elongation | -195 °C | 30 % Show Material materials with Elongation of 30 % | H18 | Elongation in 50 mm | |
-80 °C | 16 % Show Material materials with Elongation of 16 % | H18 | Elongation in 50 mm | ||
1.0 % Show Material materials with Elongation of 1.0 % | H18 | AA Standards, ASTM B209 | A50 | ||
2.0 % Show Material materials with Elongation of 2.0 % | H18 | AA Standards, ASTM B209, ASTM B313 | A50 | ||
4.0 % Show Material materials with Elongation of 4.0 % | H18 | AA Standards, ASTM B209, ASTM B313 | A50 | ||
5.0 % Show Material materials with Elongation of 5.0 % | H18 | AA Standards | A50 | ||
6.5 % Show Material materials with Elongation of 6.5 % | H18 | ||||
13.0 % Show Material materials with Elongation of 13.0 % | H18 | AA Standards | A100 | ||
0 °C | 15 % Show Material materials with Elongation of 15 % | H18 | Elongation in 50 mm | ||
24 °C | 15 % Show Material materials with Elongation of 15 % | H18 | Elongation in 50 mm | ||
100 °C | 15 % Show Material materials with Elongation of 15 % | H18 | Elongation in 50 mm | ||
150 °C | 20 % Show Material materials with Elongation of 20 % | H18 | Elongation in 50 mm | ||
205 °C | 65 % Show Material materials with Elongation of 65 % | H18 | Elongation in 50 mm | ||
260 °C | 75 % Show Material materials with Elongation of 75 % | H18 | Elongation in 50 mm | ||
315 °C | 80 % Show Material materials with Elongation of 80 % | H18 | Elongation in 50 mm | ||
370 °C | 85 % Show Material materials with Elongation of 85 % | H18 | Elongation in 50 mm | ||
Fatigue strength | 62 MPa Show Material materials with Fatigue strength of 62 MPa | H18 | for 5x10⁸ cycles | ||
Hardness, Brinell | 44.0 [-] Show Material materials with Hardness, Brinell of 44.0 [-] | H18 | AA Standards | ||
44.0 [-] Show Material materials with Hardness, Brinell of 44.0 [-] | H18 | 500 kg load, 10 mm ball | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 1000 Series Aluminium | |||
Shear modulus | 25.0 GPa Show Material materials with Shear modulus of 25.0 GPa | H18 | |||
Shear strength | 85.0 MPa Show Material materials with Shear strength of 85.0 MPa | H18 | |||
Tensile strength | -195 °C | 235 MPa Show Material materials with Tensile strength of 235 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 180 MPa Show Material materials with Tensile strength of 180 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150.0 MPa Show Material materials with Tensile strength of 150.0 MPa | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |||
165.0 MPa Show Material materials with Tensile strength of 165.0 MPa | H18 | AA Standards | |||
170.0 MPa Show Material materials with Tensile strength of 170.0 MPa | H18 | ||||
0 °C | 172 MPa Show Material materials with Tensile strength of 172 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 165 MPa Show Material materials with Tensile strength of 165 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 145 MPa Show Material materials with Tensile strength of 145 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 125 MPa Show Material materials with Tensile strength of 125 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 40 MPa Show Material materials with Tensile strength of 40 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 28 MPa Show Material materials with Tensile strength of 28 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 20 MPa Show Material materials with Tensile strength of 20 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 14 MPa Show Material materials with Tensile strength of 14 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
Yield strength | -196 °C | 180 MPa Show Material materials with Yield strength of 180 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 160 MPa Show Material materials with Yield strength of 160 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 160 MPa Show Material materials with Yield strength of 160 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
140.0 MPa Show Material materials with Yield strength of 140.0 MPa | H18 | AA Standards, ASTM B210, ASTM B483 | RP02 | ||
150.0 MPa Show Material materials with Yield strength of 150.0 MPa | H18 | AA Standards | RP02 | ||
150.0 MPa Show Material materials with Yield strength of 150.0 MPa | H18 | ||||
24 °C | 150 MPa Show Material materials with Yield strength of 150 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 130 MPa Show Material materials with Yield strength of 130 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 97 MPa Show Material materials with Yield strength of 97 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 24 MPa Show Material materials with Yield strength of 24 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 18 MPa Show Material materials with Yield strength of 18 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 14 MPa Show Material materials with Yield strength of 14 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 11 MPa Show Material materials with Yield strength of 11 MPa | H18 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K | H18 | ||
20 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
100 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
Melting point | 640.0 - 655.0 °C Show Material materials with Melting point of 640.0 - 655.0 °C | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
640.0 °C Show Material materials with Melting point of 640.0 °C | H18 | |||
Specific heat capacity | 900.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 J/(kg·K) | H18 | ||
Thermal conductivity | 218.0 - 222.0 W/(m·K) Show Material materials with Thermal conductivity of 218.0 - 222.0 W/(m·K) | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
220.0 W/(m·K) Show Material materials with Thermal conductivity of 220.0 W/(m·K) | H18 | |||
Electrical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Electrical conductivity | 33000000.0 - 34000000.0 S/m Show Material materials with Electrical conductivity of 33000000.0 - 34000000.0 S/m | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
33000000 S/m Show Material materials with Electrical conductivity of 33000000 S/m | H18 | Typical value | ||
Electrical resistivity | 2.94e-08 - 3.03e-08 Ω·m Show Material materials with Electrical resistivity of 2.94e-08 - 3.03e-08 Ω·m | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 | |
3.02e-08 Ω·m Show Material materials with Electrical resistivity of 3.02e-08 Ω·m | H18 | Typical value | ||
Specific Electrical conductivity | 57.0 % IACS Show Material materials with Specific Electrical conductivity of 57.0 % IACS | H18 | Typical/Derived value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 99.0 % Show Material materials with Aluminium of 99.0 % | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
99.0 - 100.0 % Show Material materials with Aluminium of 99.0 - 100.0 % | H18 | ||
Copper | 0.05 - 0.2 % Show Material materials with Copper of 0.05 - 0.2 % | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Iron | 1.0 % Show Material materials with Iron of 1.0 % | H18 | |
Manganese | 0.05 % Show Material materials with Manganese of 0.05 % | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Other | 0.15 % Show Material materials with Other of 0.15 % | H18 | |
Silicon | 1.0 % Show Material materials with Silicon of 1.0 % | H18 | |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H18 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
| Workability | general (condition): good (O, H12, H14), acceptable (H16), poor(H18) | |