AA Standards Grade 2014 O

Want to keep this datasheet? Save it now in your required format

Description

Related Standards

Equivalent Materials

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.8 - 3 g/cm³ at 23 °C

Dimension

Dimensions

Wanddicke

Mechanical

Bending Fatigue Strength

SNf

90 MPa at 23 °C

Show 2000 Series materials with Bending Fatigue Strength of 90 MPa at 23 °C

Elastic modulus

E

73 GPa at 23 °C

Show 2000 Series materials with Elastic modulus of 73 GPa at 23 °C

Elongation

A

14 - 18 % at 23 °C

Show 2000 Series materials with Elongation of 14 - 18 % at 23 °C

Elongation A100

A100

9 - 16 % at 23 °C

Show 2000 Series materials with Elongation A100 of 9 - 16 % at 23 °C

Elongation A50

A50

12 - 16 % at 23 °C

Show 2000 Series materials with Elongation A50 of 12 - 16 % at 23 °C

Fatigue strength

SNf

90 MPa at 23 °C

Show 2000 Series materials with Fatigue strength of 90 MPa at 23 °C

for 5x10⁸ cycles

Hardness, Brinell

HB

45 [-] at 23 °C

Show 2000 Series materials with Hardness, Brinell of 45 [-] at 23 °C

500 kg load, 10 mm ball

Hardness, Rockwell H

HRH

87 - 98 [-] at 23 °C

Show 2000 Series materials with Hardness, Rockwell H of 87 - 98 [-] at 23 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 23 °C

Show 2000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23 °C

Typical for Wrought 2000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 23 °C

Show 2000 Series materials with Poisson's ratio of 0.33 [-] at 23 °C

Typical for Wrought 2000 Series Aluminium

Shear modulus

G

28 GPa at 23 °C

Show 2000 Series materials with Shear modulus of 28 GPa at 23 °C

Shear strength

τ

125 MPa at 23 °C

Show 2000 Series materials with Shear strength of 125 MPa at 23 °C

Tensile strength

Rm

185 - 240 MPa at 23 °C

Show 2000 Series materials with Tensile strength of 185 - 240 MPa at 23 °C

Yield strength

YS

100 MPa at 23 °C

Show 2000 Series materials with Yield strength of 100 MPa at 23 °C

Yield strength Rp0.2

Rp0.2

95 - 125 MPa at 23 °C

Show 2000 Series materials with Yield strength Rp0.2 of 95 - 125 MPa at 23 °C

Thermal

Coefficient of thermal expansion

α

2.3E-5 1/K at 20 °C

Hide chart

Melting point

Tm

505 - 635 °C

Specific heat capacity

cp

870 J/(kg·K) at 23 °C

Thermal conductivity

λ

134 - 193 W/(m·K) at 23 °C

Electrical

Electrical conductivity

σel

2.00E+7 - 2.90E+7 S/m at 23 °C

Typical value

Electrical resistivity

ρel

3.4E-8 - 5E-8 Ω·m at 23 °C

Typical value

Specific Electrical conductivity

50 % IACS

Typical/Derived value

Chemical properties

Element

Weight %

Comment

Al

90.4 - 95 %

Cu

3.9 - 5 %

Si

0.5 - 1.2 %

Mn

0.4 - 1.2 %

Mg

0.2 - 0.8 %

More

Technological properties

Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected

General machinability

General: poor (O), good to acceptable

Workability

general (condition): poor(T3, T4, T451), not suitable (T6, T651, T6510, T6511)

This material data has been provided by MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials,WroughtAl_ElectricalResistivity,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.