General
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastic modulus | 73.0 GPa Show Material materials with Elastic modulus of 73.0 GPa | T3 | AA Standards, ASTM B209 | |
Elongation | 14.0 % Show Material materials with Elongation of 14.0 % | T3 | AA Standards, ASTM B209 | A50 |
14.0 % Show Material materials with Elongation of 14.0 % | T3 | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Shear modulus | 26.0 - 27.5 GPa Show Material materials with Shear modulus of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||
Tensile strength | 405.0 MPa Show Material materials with Tensile strength of 405.0 MPa | T3 | AA Standards, ASTM B209 | |
450.0 MPa Show Material materials with Tensile strength of 450.0 MPa | T3 | |||
Yield strength | 240.0 MPa Show Material materials with Yield strength of 240.0 MPa | T3 | AA Standards, ASTM B209 | RP02 |
250.0 MPa Show Material materials with Yield strength of 250.0 MPa | T3 | AA Standards, ASTM B209 | RP02 | |
290.0 MPa Show Material materials with Yield strength of 290.0 MPa | T3 |
Thermal
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T3 | ||
20 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T3 | AA Standards, ASTM B209 | |
100 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T3 | AA Standards, ASTM B209 | |
Melting point | 505.0 - 635.0 °C Show Material materials with Melting point of 505.0 - 635.0 °C | T3 | AA Standards, ASTM B209 | |
510.0 °C Show Material materials with Melting point of 510.0 °C | T3 | |||
Specific heat capacity | 870.0 J/(kg·K) Show Material materials with Specific heat capacity of 870.0 J/(kg·K) | T3 | ||
Thermal conductivity | 134.0 - 193.0 W/(m·K) Show Material materials with Thermal conductivity of 134.0 - 193.0 W/(m·K) | T3 | AA Standards, ASTM B209 | |
150.0 W/(m·K) Show Material materials with Thermal conductivity of 150.0 W/(m·K) | T3 |
Electrical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Electrical conductivity | 19700000 S/m Show Material materials with Electrical conductivity of 19700000 S/m | T3 | Typical/derived value | |
20000000.0 - 29000000.0 S/m Show Material materials with Electrical conductivity of 20000000.0 - 29000000.0 S/m | T3 | AA Standards, ASTM B209 | ||
Electrical resistivity | 3.45e-08 - 5e-08 Ω·m Show Material materials with Electrical resistivity of 3.45e-08 - 5e-08 Ω·m | T3 | AA Standards, ASTM B209 | |
5.0999999999999993e-08 Ω·m Show Material materials with Electrical resistivity of 5.0999999999999993e-08 Ω·m | T3 | Typical value | ||
Specific Electrical conductivity | 34.0 % IACS Show Material materials with Specific Electrical conductivity of 34.0 % IACS | T3 | Typical value |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 90.4 - 95.0 % Show Material materials with Aluminium of 90.4 - 95.0 % | T3 | |
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | T3 | AA Standards, ASTM B209 |
Copper | 3.9 - 5.0 % Show Material materials with Copper of 3.9 - 5.0 % | T3 | AA Standards, ASTM B209 |
Iron | 0.70 % Show Material materials with Iron of 0.70 % | T3 | AA Standards, ASTM B209 |
0.7 % Show Material materials with Iron of 0.7 % | T3 | ||
Magnesium | 0.2 - 0.8 % Show Material materials with Magnesium of 0.2 - 0.8 % | T3 | AA Standards, ASTM B209 |
Manganese | 0.4 - 1.2 % Show Material materials with Manganese of 0.4 - 1.2 % | T3 | AA Standards, ASTM B209 |
Other | 0.15 % Show Material materials with Other of 0.15 % | T3 | |
Silicon | 0.5 - 1.2 % Show Material materials with Silicon of 0.5 - 1.2 % | T3 | AA Standards, ASTM B209 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | T3 | AA Standards, ASTM B209 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T3 | AA Standards, ASTM B209 |
Zirconium | 0.2 % Show Material materials with Zirconium of 0.2 % | T3 |
Technological properties
Property | ||
---|---|---|
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected | |
General machinability | General: poor (O), good to acceptable | |
Workability | general (condition): poor(T3, T4, T451), not suitable (T6, T651, T6510, T6511) |