Want to keep this datasheet? Save it now in your required format

Description

AA 2014 is an alloy with strength, machinability and welding capabilities, Aluminum Alloy AA 2014 is an excellent option. It is a precipitation hardening alloy that maintains strength after heat treatment.

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials,WroughtAl_ElectricalResistivity.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.8 g/cm³

Show Material materials with Density of 2.8 g/cm³

T651

AA Standards, ASTM B209, ASTM B211

2.8 g/cm³

Show Material materials with Density of 2.8 g/cm³

T651

3.0 g/cm³

Show Material materials with Density of 3.0 g/cm³

T651

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Bending Fatigue Strength

125.0 MPa

Show Material materials with Bending Fatigue Strength of 125.0 MPa

T651

AA Standards

Elastic modulus

73.0 GPa

Show Material materials with Elastic modulus of 73.0 GPa

T651

AA Standards, ASTM B209, ASTM B211

73 GPa

Show Material materials with Elastic modulus of 73 GPa

T651

Elongation

-195 °C

14 %

Show Material materials with Elongation of 14 %

T651

Elongation in 50 mm

-80 °C

13 %

Show Material materials with Elongation of 13 %

T651

Elongation in 50 mm

1.0 %

Show Material materials with Elongation of 1.0 %

T651

AA Standards, ASTM B209

A100

3.0 %

Show Material materials with Elongation of 3.0 %

T651

AA Standards, ASTM B209

A100

5.0 %

Show Material materials with Elongation of 5.0 %

T651

AA Standards, ASTM B209

A100

7.0 %

Show Material materials with Elongation of 7.0 %

T651

AA Standards, ASTM B211

A100

7.0 %

Show Material materials with Elongation of 7.0 %

T651

AA Standards, ASTM B209

A50

7.1 %

Show Material materials with Elongation of 7.1 %

T651

8.0 %

Show Material materials with Elongation of 8.0 %

T651

AA Standards, ASTM B211

A50

11.0 %

Show Material materials with Elongation of 11.0 %

T651

AA Standards

A100

0 °C

13 %

Show Material materials with Elongation of 13 %

T651

Elongation in 50 mm

24 °C

13 %

Show Material materials with Elongation of 13 %

T651

Elongation in 50 mm

100 °C

15 %

Show Material materials with Elongation of 15 %

T651

Elongation in 50 mm

150 °C

20 %

Show Material materials with Elongation of 20 %

T651

Elongation in 50 mm

205 °C

38 %

Show Material materials with Elongation of 38 %

T651

Elongation in 50 mm

260 °C

52 %

Show Material materials with Elongation of 52 %

T651

Elongation in 50 mm

315 °C

65 %

Show Material materials with Elongation of 65 %

T651

Elongation in 50 mm

370 °C

72 %

Show Material materials with Elongation of 72 %

T651

Elongation in 50 mm

Hardness, Brinell

135.0 [-]

Show Material materials with Hardness, Brinell of 135.0 [-]

T651

AA Standards

Plane-Strain Fracture Toughnes

-196 °C

28.5 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 28.5 MPa·√m

T651

For plate in T-L direction

24 °C

23.2 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 23.2 MPa·√m

T651

For plate in T-L direction

Unlock all property charts

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 2000 Series Aluminium

Shear modulus

28.0 GPa

Show Material materials with Shear modulus of 28.0 GPa

T651

Tensile strength

-195 °C

580 MPa

Show Material materials with Tensile strength of 580 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

510 MPa

Show Material materials with Tensile strength of 510 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

405.0 MPa

Show Material materials with Tensile strength of 405.0 MPa

T651

AA Standards, ASTM B209

435.0 MPa

Show Material materials with Tensile strength of 435.0 MPa

T651

AA Standards, ASTM B209

450.0 MPa

Show Material materials with Tensile strength of 450.0 MPa

T651

AA Standards, ASTM B209, ASTM B211

460.0 MPa

Show Material materials with Tensile strength of 460.0 MPa

T651

AA Standards, ASTM B209

485.0 MPa

Show Material materials with Tensile strength of 485.0 MPa

T651

AA Standards

490.0 MPa

Show Material materials with Tensile strength of 490.0 MPa

T651

0 °C

495 MPa

Show Material materials with Tensile strength of 495 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

24 °C

483 MPa

Show Material materials with Tensile strength of 483 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C

435 MPa

Show Material materials with Tensile strength of 435 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

275 MPa

Show Material materials with Tensile strength of 275 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205 °C

110 MPa

Show Material materials with Tensile strength of 110 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

66 MPa

Show Material materials with Tensile strength of 66 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

45 MPa

Show Material materials with Tensile strength of 45 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

370 °C

30 MPa

Show Material materials with Tensile strength of 30 MPa

T651

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Unlock all property charts

Yield strength

380.0 MPa

Show Material materials with Yield strength of 380.0 MPa

T651

AA Standards, ASTM B209, ASTM B211

RP02

395.0 MPa

Show Material materials with Yield strength of 395.0 MPa

T651

AA Standards, ASTM B209

RP02

400.0 MPa

Show Material materials with Yield strength of 400.0 MPa

T651

AA Standards, ASTM B209

RP02

405.0 MPa

Show Material materials with Yield strength of 405.0 MPa

T651

AA Standards, ASTM B209

RP02

415.0 MPa

Show Material materials with Yield strength of 415.0 MPa

T651

AA Standards

RP02

430.0 MPa

Show Material materials with Yield strength of 430.0 MPa

T651

Thermal

PropertyTemperatureValueConditionRelated Standards

Coefficient of thermal expansion

2.3e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K

T651

20 °C

2.3e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K

T651

AA Standards, ASTM B209, ASTM B211

100 °C

2.3e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K

T651

AA Standards, ASTM B209, ASTM B211

Unlock all property charts

Melting point

505.0 - 635.0 °C

Show Material materials with Melting point of 505.0 - 635.0 °C

T651

AA Standards, ASTM B209, ASTM B211

510.0 °C

Show Material materials with Melting point of 510.0 °C

T651

Specific heat capacity

870.0 J/(kg·K)

Show Material materials with Specific heat capacity of 870.0 J/(kg·K)

T651

Thermal conductivity

134.0 - 193.0 W/(m·K)

Show Material materials with Thermal conductivity of 134.0 - 193.0 W/(m·K)

T651

AA Standards, ASTM B209, ASTM B211

150.0 W/(m·K)

Show Material materials with Thermal conductivity of 150.0 W/(m·K)

T651

Electrical

PropertyValueConditionRelated StandardsComment

Electrical conductivity

20000000.0 - 29000000.0 S/m

Show Material materials with Electrical conductivity of 20000000.0 - 29000000.0 S/m

T651

AA Standards, ASTM B209, ASTM B211

23000000 S/m

Show Material materials with Electrical conductivity of 23000000 S/m

T651

Typical/derived value

Electrical resistivity

3.45e-08 - 5e-08 Ω·m

Show Material materials with Electrical resistivity of 3.45e-08 - 5e-08 Ω·m

T651

AA Standards, ASTM B209, ASTM B211

4.3e-08 Ω·m

Show Material materials with Electrical resistivity of 4.3e-08 Ω·m

T651

Typical value

Specific Electrical conductivity

40.0 % IACS

Show Material materials with Specific Electrical conductivity of 40.0 % IACS

T651

Typical value

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

90.4 - 95.0 %

Show Material materials with Aluminium of 90.4 - 95.0 %

T651

Chromium

0.1 %

Show Material materials with Chromium of 0.1 %

T651

AA Standards, ASTM B209, ASTM B211

Copper

3.9 - 5.0 %

Show Material materials with Copper of 3.9 - 5.0 %

T651

AA Standards, ASTM B209, ASTM B211

Iron

0.70 %

Show Material materials with Iron of 0.70 %

T651

AA Standards, ASTM B209, ASTM B211

0.7 %

Show Material materials with Iron of 0.7 %

T651

Magnesium

0.2 - 0.8 %

Show Material materials with Magnesium of 0.2 - 0.8 %

T651

AA Standards, ASTM B209, ASTM B211

Manganese

0.4 - 1.2 %

Show Material materials with Manganese of 0.4 - 1.2 %

T651

AA Standards, ASTM B209, ASTM B211

Other

0.15 %

Show Material materials with Other of 0.15 %

T651

Silicon

0.5 - 1.2 %

Show Material materials with Silicon of 0.5 - 1.2 %

T651

AA Standards, ASTM B209, ASTM B211

Titanium

0.15 %

Show Material materials with Titanium of 0.15 %

T651

AA Standards, ASTM B209, ASTM B211

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

T651

AA Standards, ASTM B209, ASTM B211

Zirconium

0.2 %

Show Material materials with Zirconium of 0.2 %

T651

Technological properties

Property
Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected

General machinability

General: poor (O), good to acceptable

Workability

general (condition): poor(T3, T4, T451), not suitable (T6, T651, T6510, T6511)