AA Standards Grade 2014 T652

View suppliers (54)
Want to keep this datasheet? Save it now in your required format

Description

AA 2014 is an alloy with strength, machinability and welding capabilities, Aluminum Alloy AA 2014 is an excellent option. It is a precipitation hardening alloy that maintains strength after heat treatment.

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,WroughtAl_ElectricalResistivity.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.8 g/cm³

Show Material materials with Density of 2.8 g/cm³

T652

AA Standards, ASTM B247

3.0 g/cm³

Show Material materials with Density of 3.0 g/cm³

T652

Mechanical

PropertyValueConditionRelated StandardsComment

Elastic modulus

73.0 GPa

Show Material materials with Elastic modulus of 73.0 GPa

T652

AA Standards, ASTM B247

Elongation

1.0 %

Show Material materials with Elongation of 1.0 %

T652

AA Standards, ASTM B247

A100

1.5 %

Show Material materials with Elongation of 1.5 %

T652

2.0 %

Show Material materials with Elongation of 2.0 %

T652

AA Standards, ASTM B247

A50

2.0 %

Show Material materials with Elongation of 2.0 %

T652

AA Standards, ASTM B247

A100

5.0 %

Show Material materials with Elongation of 5.0 %

T652

AA Standards, ASTM B247

A100

6.0 %

Show Material materials with Elongation of 6.0 %

T652

AA Standards, ASTM B247

A50

6.0 %

Show Material materials with Elongation of 6.0 %

T652

AA Standards, ASTM B247

A100

7.0 %

Show Material materials with Elongation of 7.0 %

T652

AA Standards, ASTM B247

A100

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 2000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 2000 Series Aluminium

Shear modulus

26.0 - 27.5 GPa

Show Material materials with Shear modulus of 26.0 - 27.5 GPa

Typical for Wrought 2000 Series Aluminium

Tensile strength

395.0 MPa

Show Material materials with Tensile strength of 395.0 MPa

T652

AA Standards, ASTM B247

400.0 MPa

Show Material materials with Tensile strength of 400.0 MPa

T652

AA Standards, ASTM B247

405.0 MPa

Show Material materials with Tensile strength of 405.0 MPa

T652

AA Standards, ASTM B247

415.0 MPa

Show Material materials with Tensile strength of 415.0 MPa

T652

AA Standards, ASTM B247

420.0 MPa

Show Material materials with Tensile strength of 420.0 MPa

T652

AA Standards, ASTM B247

425.0 MPa

Show Material materials with Tensile strength of 425.0 MPa

T652

AA Standards, ASTM B247

435.0 MPa

Show Material materials with Tensile strength of 435.0 MPa

T652

AA Standards, ASTM B247

440.0 MPa

Show Material materials with Tensile strength of 440.0 MPa

T652

AA Standards, ASTM B247

450.0 MPa

Show Material materials with Tensile strength of 450.0 MPa

T652

AA Standards, ASTM B247

460.0 MPa

Show Material materials with Tensile strength of 460.0 MPa

T652

Yield strength

330.0 MPa

Show Material materials with Yield strength of 330.0 MPa

T652

AA Standards, ASTM B247

RP02

340.0 MPa

Show Material materials with Yield strength of 340.0 MPa

T652

AA Standards, ASTM B247

RP02

345.0 MPa

Show Material materials with Yield strength of 345.0 MPa

T652

AA Standards, ASTM B247

RP02

350.0 MPa

Show Material materials with Yield strength of 350.0 MPa

T652

AA Standards, ASTM B247

RP02

360.0 MPa

Show Material materials with Yield strength of 360.0 MPa

T652

AA Standards, ASTM B247

RP02

365.0 MPa

Show Material materials with Yield strength of 365.0 MPa

T652

AA Standards, ASTM B247

RP02

370.0 MPa

Show Material materials with Yield strength of 370.0 MPa

T652

AA Standards, ASTM B247

RP02

380.0 MPa

Show Material materials with Yield strength of 380.0 MPa

T652

AA Standards, ASTM B247

RP02

385.0 MPa

Show Material materials with Yield strength of 385.0 MPa

T652

AA Standards, ASTM B247

RP02

390.0 MPa

Show Material materials with Yield strength of 390.0 MPa

T652

Thermal

PropertyTemperatureValueConditionRelated Standards

Coefficient of thermal expansion

2.3e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K

T652

20 °C

2.3e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K

T652

AA Standards, ASTM B247

100 °C

2.3e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K

T652

AA Standards, ASTM B247

Melting point

505.0 - 635.0 °C

Show Material materials with Melting point of 505.0 - 635.0 °C

T652

AA Standards, ASTM B247

510.0 °C

Show Material materials with Melting point of 510.0 °C

T652

Specific heat capacity

870.0 J/(kg·K)

Show Material materials with Specific heat capacity of 870.0 J/(kg·K)

T652

Thermal conductivity

134.0 - 193.0 W/(m·K)

Show Material materials with Thermal conductivity of 134.0 - 193.0 W/(m·K)

T652

AA Standards, ASTM B247

150.0 W/(m·K)

Show Material materials with Thermal conductivity of 150.0 W/(m·K)

T652

Electrical

PropertyValueConditionRelated StandardsComment

Electrical conductivity

20000000.0 - 29000000.0 S/m

Show Material materials with Electrical conductivity of 20000000.0 - 29000000.0 S/m

T652

AA Standards, ASTM B247

23000000 S/m

Show Material materials with Electrical conductivity of 23000000 S/m

T652

Typical/derived value

Electrical resistivity

3.45e-08 - 5e-08 Ω·m

Show Material materials with Electrical resistivity of 3.45e-08 - 5e-08 Ω·m

T652

AA Standards, ASTM B247

4.3e-08 Ω·m

Show Material materials with Electrical resistivity of 4.3e-08 Ω·m

T652

Typical value

Specific Electrical conductivity

40.0 % IACS

Show Material materials with Specific Electrical conductivity of 40.0 % IACS

T652

Typical value

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

90.4 - 95.0 %

Show Material materials with Aluminium of 90.4 - 95.0 %

T652

Chromium

0.1 %

Show Material materials with Chromium of 0.1 %

T652

AA Standards, ASTM B247

Copper

3.9 - 5.0 %

Show Material materials with Copper of 3.9 - 5.0 %

T652

AA Standards, ASTM B247

Iron

0.70 %

Show Material materials with Iron of 0.70 %

T652

AA Standards, ASTM B247

0.7 %

Show Material materials with Iron of 0.7 %

T652

Magnesium

0.2 - 0.8 %

Show Material materials with Magnesium of 0.2 - 0.8 %

T652

AA Standards, ASTM B247

Manganese

0.4 - 1.2 %

Show Material materials with Manganese of 0.4 - 1.2 %

T652

AA Standards, ASTM B247

Other

0.15 %

Show Material materials with Other of 0.15 %

T652

Silicon

0.5 - 1.2 %

Show Material materials with Silicon of 0.5 - 1.2 %

T652

AA Standards, ASTM B247

Titanium

0.15 %

Show Material materials with Titanium of 0.15 %

T652

AA Standards, ASTM B247

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

T652

AA Standards, ASTM B247

Zirconium

0.2 %

Show Material materials with Zirconium of 0.2 %

T652

Technological properties

Property
Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected

General machinability

General: poor (O), good to acceptable

Workability

general (condition): poor(T3, T4, T451), not suitable (T6, T651, T6510, T6511)