AA Standards Grade 2017 T4

View suppliers (30)
Want to keep this datasheet? Save it now in your required format

Description

Aluminum AA 2017 is a heat treatable wrought alloy that offers decent strength, ductility, and good machinability. Aluminum AA 2017 offers more strength than Aluminum 2011, and has fair workability and corrosion resistance. As with many aluminum alloys, Aluminum AA 2017 should not be welded as it reduces the alloy’s corrosion resistance.

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials,WroughtAl_ElectricalResistivity.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.79 g/cm³

Show Material materials with Density of 2.79 g/cm³

T4

AA Standards, ASTM B211, ASTM B316

2.79 g/cm³

Show Material materials with Density of 2.79 g/cm³

T4

3.0 g/cm³

Show Material materials with Density of 3.0 g/cm³

T4

Mechanical

PropertyTemperatureValueConditionRelated StandardsComment

Bending Fatigue Strength

125.0 MPa

Show Material materials with Bending Fatigue Strength of 125.0 MPa

T4

AA Standards

Elastic modulus

72 GPa

Show Material materials with Elastic modulus of 72 GPa

T4

73.0 GPa

Show Material materials with Elastic modulus of 73.0 GPa

T4

AA Standards, ASTM B211, ASTM B316

Elongation

-195 °C

28 %

Show Material materials with Elongation of 28 %

T4

Elongation in 50 mm

-195 °C

30 %

Show Material materials with Elongation of 30 %

T4

Elongation in 50 mm

-80 °C

24 %

Show Material materials with Elongation of 24 %

T4

Elongation in 50 mm

-80 °C

29 %

Show Material materials with Elongation of 29 %

T4

Elongation in 50 mm

10.0 %

Show Material materials with Elongation of 10.0 %

T4

AA Standards, ASTM B211, ASTM B316

A100

12.0 %

Show Material materials with Elongation of 12.0 %

T4

AA Standards, ASTM B211

A50

19.0 %

Show Material materials with Elongation of 19.0 %

T4

20.0 %

Show Material materials with Elongation of 20.0 %

T4

AA Standards

A100

0 °C

23 %

Show Material materials with Elongation of 23 %

T4

Elongation in 50 mm

0 °C

28 %

Show Material materials with Elongation of 28 %

T4

Elongation in 50 mm

24 °C

22 %

Show Material materials with Elongation of 22 %

T4

Elongation in 50 mm

24 °C

27 %

Show Material materials with Elongation of 27 %

T4

Elongation in 50 mm

100 °C

16 %

Show Material materials with Elongation of 16 %

T4

Elongation in 50 mm

100 °C

18 %

Show Material materials with Elongation of 18 %

T4

Elongation in 50 mm

150 °C

15 %

Show Material materials with Elongation of 15 %

T4

Elongation in 50 mm

150 °C

20 %

Show Material materials with Elongation of 20 %

T4

Elongation in 50 mm

205 °C

35 %

Show Material materials with Elongation of 35 %

T4

Elongation in 50 mm

260 °C

45 %

Show Material materials with Elongation of 45 %

T4

Elongation in 50 mm

260 °C

55 %

Show Material materials with Elongation of 55 %

T4

Elongation in 50 mm

315 °C

65 %

Show Material materials with Elongation of 65 %

T4

Elongation in 50 mm

315 °C

80 %

Show Material materials with Elongation of 80 %

T4

Elongation in 50 mm

370 °C

70 %

Show Material materials with Elongation of 70 %

T4

Elongation in 50 mm

370 °C

110 %

Show Material materials with Elongation of 110 %

T4

Elongation in 50 mm

Hardness, Brinell

105.0 [-]

Show Material materials with Hardness, Brinell of 105.0 [-]

T4

AA Standards

105.0 [-]

Show Material materials with Hardness, Brinell of 105.0 [-]

T4

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 2000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 2000 Series Aluminium

Shear modulus

27.5 GPa

Show Material materials with Shear modulus of 27.5 GPa

T4

28.0 GPa

Show Material materials with Shear modulus of 28.0 GPa

T4

Shear strength

262.0 MPa

Show Material materials with Shear strength of 262.0 MPa

T4

Tensile strength

-195 °C

385 MPa

Show Material materials with Tensile strength of 385 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-195 °C

550 MPa

Show Material materials with Tensile strength of 550 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

310 MPa

Show Material materials with Tensile strength of 310 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80 °C

448 MPa

Show Material materials with Tensile strength of 448 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

0 °C

303 MPa

Show Material materials with Tensile strength of 303 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

380.0 MPa

Show Material materials with Tensile strength of 380.0 MPa

T4

AA Standards, ASTM B211, ASTM B316

420.0 MPa

Show Material materials with Tensile strength of 420.0 MPa

T4

425.0 MPa

Show Material materials with Tensile strength of 425.0 MPa

T4

AA Standards

0 °C

440 MPa

Show Material materials with Tensile strength of 440 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

24 °C

295 MPa

Show Material materials with Tensile strength of 295 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

24 °C

427 MPa

Show Material materials with Tensile strength of 427 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C

248 MPa

Show Material materials with Tensile strength of 248 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100 °C

393 MPa

Show Material materials with Tensile strength of 393 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

207 MPa

Show Material materials with Tensile strength of 207 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150 °C

275 MPa

Show Material materials with Tensile strength of 275 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205 °C

110 MPa

Show Material materials with Tensile strength of 110 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

52 MPa

Show Material materials with Tensile strength of 52 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260 °C

62 MPa

Show Material materials with Tensile strength of 62 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

32 MPa

Show Material materials with Tensile strength of 32 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315 °C

40 MPa

Show Material materials with Tensile strength of 40 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

370 °C

20 MPa

Show Material materials with Tensile strength of 20 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

370 °C

30 MPa

Show Material materials with Tensile strength of 30 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Yield strength

-195 °C

365 MPa

Show Material materials with Yield strength of 365 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-80 °C

290 MPa

Show Material materials with Yield strength of 290 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

-28 °C

283 MPa

Show Material materials with Yield strength of 283 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

220.0 MPa

Show Material materials with Yield strength of 220.0 MPa

T4

AA Standards, ASTM B211, ASTM B316

RP02

260.0 MPa

Show Material materials with Yield strength of 260.0 MPa

T4

275.0 MPa

Show Material materials with Yield strength of 275.0 MPa

T4

AA Standards

RP02

24 °C

275 MPa

Show Material materials with Yield strength of 275 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

100 °C

270 MPa

Show Material materials with Yield strength of 270 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

150 °C

207 MPa

Show Material materials with Yield strength of 207 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

205 °C

90 MPa

Show Material materials with Yield strength of 90 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

260 °C

50 MPa

Show Material materials with Yield strength of 50 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

315 °C

35 MPa

Show Material materials with Yield strength of 35 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

371 °C

3.5 MPa

Show Material materials with Yield strength of 3.5 MPa

T4

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02

Thermal

PropertyTemperatureValueConditionRelated Standards

Coefficient of thermal expansion

2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

T4

20 °C

2.36e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K

T4

AA Standards, ASTM B211, ASTM B316

100 °C

2.36e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K

T4

AA Standards, ASTM B211, ASTM B316

Melting point

510.0 - 640.0 °C

Show Material materials with Melting point of 510.0 - 640.0 °C

T4

AA Standards, ASTM B211, ASTM B316

510.0 °C

Show Material materials with Melting point of 510.0 °C

T4

Specific heat capacity

870.0 J/(kg·K)

Show Material materials with Specific heat capacity of 870.0 J/(kg·K)

T4

Thermal conductivity

134.0 - 193.0 W/(m·K)

Show Material materials with Thermal conductivity of 134.0 - 193.0 W/(m·K)

T4

AA Standards, ASTM B211, ASTM B316

140.0 W/(m·K)

Show Material materials with Thermal conductivity of 140.0 W/(m·K)

T4

Electrical

PropertyValueConditionRelated StandardsComment

Electrical conductivity

20000000.0 - 29000000.0 S/m

Show Material materials with Electrical conductivity of 20000000.0 - 29000000.0 S/m

T4

AA Standards, ASTM B211, ASTM B316

20000000 S/m

Show Material materials with Electrical conductivity of 20000000 S/m

T4

Typical value

Electrical resistivity

3.45e-08 - 5e-08 Ω·m

Show Material materials with Electrical resistivity of 3.45e-08 - 5e-08 Ω·m

T4

AA Standards, ASTM B211, ASTM B316

5.1500000000000005e-08 Ω·m

Show Material materials with Electrical resistivity of 5.1500000000000005e-08 Ω·m

T4

Typical value

Specific Electrical conductivity

34.0 % IACS

Show Material materials with Specific Electrical conductivity of 34.0 % IACS

T4

Typical/Derived value

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

91.6 - 95.5 %

Show Material materials with Aluminium of 91.6 - 95.5 %

T4

Chromium

0.1 %

Show Material materials with Chromium of 0.1 %

T4

AA Standards, ASTM B211, ASTM B316

Copper

3.5 - 4.5 %

Show Material materials with Copper of 3.5 - 4.5 %

T4

AA Standards, ASTM B211, ASTM B316

Iron

0.70 %

Show Material materials with Iron of 0.70 %

T4

AA Standards, ASTM B211, ASTM B316

0.7 %

Show Material materials with Iron of 0.7 %

T4

Magnesium

0.4 - 0.8 %

Show Material materials with Magnesium of 0.4 - 0.8 %

T4

AA Standards, ASTM B211, ASTM B316

Manganese

0.4 - 1.0 %

Show Material materials with Manganese of 0.4 - 1.0 %

T4

AA Standards, ASTM B211, ASTM B316

Other

0.15 %

Show Material materials with Other of 0.15 %

T4

Silicon

0.2 - 0.8 %

Show Material materials with Silicon of 0.2 - 0.8 %

T4

AA Standards, ASTM B211, ASTM B316

Titanium

0.15 %

Show Material materials with Titanium of 0.15 %

T4

AA Standards, ASTM B211, ASTM B316

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

T4

AA Standards, ASTM B211, ASTM B316

Technological properties

Property
Brazing

general: no brazing is known or developed

Corrosion properties

Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected

General machinability

General: good to acceptable

Workability

general (condition): poor(T4, T451)