Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Density | 20.0 °C | 2.71 g/cm³ Show Material materials with Density of 2.71 g/cm³ | F12 | DIN 1712-3, EN 573-3, EN 573-4 |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 60.0 - 65.0 GPa Show Material materials with Elastic modulus of 60.0 - 65.0 GPa | F12 | DIN 1712-3, EN 573-3, EN 573-4 | |
Elongation | -196.0 °C | 45.0 % Show Material materials with Elongation of 45.0 % | F12 | DIN 1712-3, EN 573-3, EN 573-4 | |
-80.0 °C | 24.0 % Show Material materials with Elongation of 24.0 % | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
-28.0 °C | 20.0 % Show Material materials with Elongation of 20.0 % | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
20.0 °C | 20.0 % Show Material materials with Elongation of 20.0 % | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
100.0 °C | 20.0 % Show Material materials with Elongation of 20.0 % | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
150.0 °C | 23.0 % Show Material materials with Elongation of 23.0 % | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
200.0 °C | 26.0 % Show Material materials with Elongation of 26.0 % | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
260.0 °C | 75.0 % Show Material materials with Elongation of 75.0 % | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
315.0 °C | 80.0 % Show Material materials with Elongation of 80.0 % | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
370.0 °C | 85.0 % Show Material materials with Elongation of 85.0 % | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 1000 Series Aluminium | |||
Shear modulus | 20.0 °C | 24.0 - 26.0 GPa Show Material materials with Shear modulus of 24.0 - 26.0 GPa | F12 | DIN 1712-3, EN 573-3, EN 573-4 | |
Tensile strength | -196.0 °C | 210.0 MPa Show Material materials with Tensile strength of 210.0 MPa | F12 | DIN 1712-3, EN 573-3, EN 573-4 | |
-80.0 °C | 140.0 MPa Show Material materials with Tensile strength of 140.0 MPa | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
-28.0 °C | 130.0 MPa Show Material materials with Tensile strength of 130.0 MPa | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
20.0 °C | 125.0 MPa Show Material materials with Tensile strength of 125.0 MPa | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
100.0 °C | 110.0 MPa Show Material materials with Tensile strength of 110.0 MPa | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
150.0 °C | 95.0 MPa Show Material materials with Tensile strength of 95.0 MPa | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
200.0 °C | 70.0 MPa Show Material materials with Tensile strength of 70.0 MPa | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
260.0 °C | 30.0 MPa Show Material materials with Tensile strength of 30.0 MPa | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
315.0 °C | 20.0 MPa Show Material materials with Tensile strength of 20.0 MPa | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
370.0 °C | 15.0 MPa Show Material materials with Tensile strength of 15.0 MPa | F12 | DIN 1712-3, EN 573-3, EN 573-4 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | -50.0 °C | 2.17e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.17e-05 1/K | F12 | DIN 1712-3, EN 573-3, EN 573-4 | |
100.0 °C | 2.35e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.35e-05 1/K | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
200.0 °C | 2.44e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.44e-05 1/K | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
300.0 °C | 2.54e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.54e-05 1/K | F12 | DIN 1712-3, EN 573-3, EN 573-4 | ||
Melting point | 645.0 - 660.0 °C Show Material materials with Melting point of 645.0 - 660.0 °C | Typical for Wrought 1000 Series Aluminium | |||
Specific heat capacity | 900.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium | |||
Thermal conductivity | 20.0 °C | 205.0 - 210.0 W/(m·K) Show Material materials with Thermal conductivity of 205.0 - 210.0 W/(m·K) | F12 | DIN 1712-3, EN 573-3, EN 573-4 |
Electrical
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 34400000.0 - 35500000.0 S/m Show Material materials with Electrical conductivity of 34400000.0 - 35500000.0 S/m | F12 | DIN 1712-3, EN 573-3, EN 573-4 | |
Electrical resistivity | 2.7e-08 - 3e-08 Ω·m Show Material materials with Electrical resistivity of 2.7e-08 - 3e-08 Ω·m | Typical for Wrought 1000 Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Copper | 0.05 Show Material materials with Copper of 0.05 | F12 | DIN 1712-3, EN 573-3, EN 573-4 |
Magnesium | 0.05 Show Material materials with Magnesium of 0.05 | F12 | DIN 1712-3, EN 573-3, EN 573-4 |
Manganese | 0.05 Show Material materials with Manganese of 0.05 | F12 | DIN 1712-3, EN 573-3, EN 573-4 |
Titanium | 0.05 Show Material materials with Titanium of 0.05 | F12 | DIN 1712-3, EN 573-3, EN 573-4 |
Zinc | 0.1 Show Material materials with Zinc of 0.1 | F12 | DIN 1712-3, EN 573-3, EN 573-4 |
Technological properties
Property | ||
---|---|---|
Brazing | Excellent | |
Workability | Excellent workability. |