General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Density | 2.71 g/cm³ Show Material materials with Density of 2.71 g/cm³ | H14 | EN 573-3, EN 485 | ||
2.72 g/cm³ Show Material materials with Density of 2.72 g/cm³ | H14 | EN 573-3, EN 485 | |||
20.0 °C | 2.71 g/cm³ Show Material materials with Density of 2.71 g/cm³ | H14 | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Bending angle 180° | 2.5 °/t Show Material materials with Bending angle 180° of 2.5 °/t | H14 | EN 573-3, EN 485 | |||
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H14 | EN 573-3, EN 485 | |||
70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | H14 | EN 573-3, EN 485 | ||||
Hardness, Brinell | 48.0 [-] Show Material materials with Hardness, Brinell of 48.0 [-] | H14 | EN 573-3, EN 485 | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||||
Shear modulus | 25.0 - 26.0 GPa Show Material materials with Shear modulus of 25.0 - 26.0 GPa | Typical for Wrought 3000 Series Aluminium | ||||
Tensile strength | 150.0 - 200.0 MPa Show Material materials with Tensile strength of 150.0 - 200.0 MPa | H14 | EN 573-3, EN 485 | |||
20.0 °C | 170.0 - 210.0 MPa Show Material materials with Tensile strength of 170.0 - 210.0 MPa | H14 | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | H14 | EN 573-3, EN 485 | ||
100 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | H14 | EN 573-3, EN 485 | |||
Melting point | 635.0 - 655.0 °C Show Material materials with Melting point of 635.0 - 655.0 °C | H14 | EN 573-3, EN 485 | |||
640.0 - 655.0 °C Show Material materials with Melting point of 640.0 - 655.0 °C | H14 | EN 573-3, EN 485 | ||||
Specific heat capacity | 893.0 - 920.0 J/(kg·K) Show Material materials with Specific heat capacity of 893.0 - 920.0 J/(kg·K) | Typical for Wrought 3000 Series Aluminium | ||||
Thermal conductivity | 160.0 - 190.0 W/(m·K) Show Material materials with Thermal conductivity of 160.0 - 190.0 W/(m·K) | H14 | EN 573-3, EN 485 | |||
172 W/(m·K) Show Material materials with Thermal conductivity of 172 W/(m·K) | H14 | EN 573-3, EN 485 | ||||
20.0 °C | 180.0 - 190.0 W/(m·K) Show Material materials with Thermal conductivity of 180.0 - 190.0 W/(m·K) | H14 | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Electrical conductivity | 23000000.0 - 26000000.0 S/m Show Material materials with Electrical conductivity of 23000000.0 - 26000000.0 S/m | H14 | EN 573-3, EN 485 | ||
26000000.0 S/m Show Material materials with Electrical conductivity of 26000000.0 S/m | H14 | EN 573-3, EN 485 | |||
20.0 °C | 25000000.0 - 27000000.0 S/m Show Material materials with Electrical conductivity of 25000000.0 - 27000000.0 S/m | H14 | DIN 1725-1, EN 573-3, EN 573-4 | Flat | |
Electrical resistivity | 3.85e-08 Ω·m Show Material materials with Electrical resistivity of 3.85e-08 Ω·m | H14 | EN 573-3, EN 485 | ||
3.85e-08 - 4.35e-08 Ω·m Show Material materials with Electrical resistivity of 3.85e-08 - 4.35e-08 Ω·m | H14 | EN 573-3, EN 485 |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Chromium | 0.2 % Show Material materials with Chromium of 0.2 % | H14 | DIN 1725-1, EN 573-3, EN 573-4, EN 485 | Flat |
Copper | 0.3 % Show Material materials with Copper of 0.3 % | H14 | DIN 1725-1, EN 573-3, EN 573-4, EN 485 | Flat |
Iron | 0.7 % Show Material materials with Iron of 0.7 % | H14 | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
0.70 % Show Material materials with Iron of 0.70 % | H14 | EN 573-3, EN 485 | ||
Magnesium | 0.2 - 0.8 % Show Material materials with Magnesium of 0.2 - 0.8 % | H14 | DIN 1725-1, EN 573-3, EN 573-4, EN 485 | Flat |
Manganese | 0.3 - 0.8 % Show Material materials with Manganese of 0.3 - 0.8 % | H14 | DIN 1725-1, EN 573-3, EN 573-4, EN 485 | Flat |
Silicon | 0.6 % Show Material materials with Silicon of 0.6 % | H14 | DIN 1725-1, EN 573-3, EN 573-4, EN 485 | Flat |
Titanium | 0.1 % Show Material materials with Titanium of 0.1 % | H14 | DIN 1725-1, EN 573-3, EN 573-4, EN 485 | Flat |
Zinc | 0.4 % Show Material materials with Zinc of 0.4 % | H14 | DIN 1725-1, EN 573-3, EN 573-4, EN 485 | Flat |
Technological properties
Property | ||
---|---|---|
Workability | Good workability. |