DIN 1725-1 Grade 3.0515 H18

Want to keep this datasheet? Save it now in your required format

Description

Valid for tube with ribbs - outer diameter of ribbed parts of tubes: 36,0 to 70,0 mm - wall thicknes of ribbed parts of tubes: 1,0 to 8,5 mm - spacing of ribbs: 2,2 to 5,1 mm - high of ribbs: 6,5 to 16 mm - average thickness of ribbs: 0,4 to 1,0 mm Melting: - inductive - gaseous heated melting oven Application: - steam boiler with pressure ab to 10 bar Further processing: - no heat treatment

Related Standards

Equivalent Materials

This material data has been provided by WIAM,AluKey.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density		2.73 g/cm³ Show Material materials with Density of 2.73 g/cm³	H18	EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754
	20.0 °C	2.73 g/cm³ Show Material materials with Density of 2.73 g/cm³	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Flat, Wire

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Bending Fatigue Strength		75.0 MPa Show Material materials with Bending Fatigue Strength of 75.0 MPa	H18	EN 573-3, EN 1301, EN 485, EN 683, EN 754
Bending angle 90°		1.5 °/t Show Material materials with Bending angle 90° of 1.5 °/t	H18	EN 573-3, EN 485
		2.5 °/t Show Material materials with Bending angle 90° of 2.5 °/t	H18	EN 573-3, EN 485
		3.0 °/t Show Material materials with Bending angle 90° of 3.0 °/t	H18	EN 573-3, EN 485
Elastic modulus		69.5 GPa Show Material materials with Elastic modulus of 69.5 GPa	H18	EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754
	20.0 °C	60.0 - 65.0 GPa Show Material materials with Elastic modulus of 60.0 - 65.0 GPa	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Flat, Wire
Elongation	-196.0 °C	30.0 % Show Material materials with Elongation of 30.0 %	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4
	-80.0 °C	18.0 % Show Material materials with Elongation of 18.0 %	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4
	-20.0 °C	16.0 % Show Material materials with Elongation of 16.0 %	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4
		1.0 % Show Material materials with Elongation of 1.0 %	H18	EN 573-3, EN 485, EN 546, EN 683		A50
		2.0 % Show Material materials with Elongation of 2.0 %	H18	EN 573-3, EN 1592		A100
		2.0 % Show Material materials with Elongation of 2.0 %	H18	EN 573-3, EN 485, EN 754		A50
		3.0 % Show Material materials with Elongation of 3.0 %	H18	EN 573-3, EN 1301
		3.0 % Show Material materials with Elongation of 3.0 %	H18	EN 573-3, EN 754		A100
	20.0 °C	1.0 % Show Material materials with Elongation of 1.0 %	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Wire	A100
	20.0 °C	3.0 % Show Material materials with Elongation of 3.0 %	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Flat, Wire	A10
	20.0 °C	4.0 % Show Material materials with Elongation of 4.0 %	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Flat
	20.0 °C	10.0 % Show Material materials with Elongation of 10.0 %	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4
	100.0 °C	10.0 % Show Material materials with Elongation of 10.0 %	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4
	150.0 °C	11.0 % Show Material materials with Elongation of 11.0 %	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4
	200.0 °C	18.0 % Show Material materials with Elongation of 18.0 %	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4
	260.0 °C	60.0 % Show Material materials with Elongation of 60.0 %	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4
	320.0 °C	70.0 % Show Material materials with Elongation of 70.0 %	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4
	370.0 °C	70.0 % Show Material materials with Elongation of 70.0 %	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4
Hardness, Brinell		58.0 [-] Show Material materials with Hardness, Brinell of 58.0 [-]	H18	EN 573-3, EN 485
	20.0 °C	45.0 [-] Show Material materials with Hardness, Brinell of 45.0 [-]	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Wire
	20.0 °C	50.0 [-] Show Material materials with Hardness, Brinell of 50.0 [-]	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Flat
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 3000 Series Aluminium
Poisson's ratio		0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-]				Typical for Wrought 3000 Series Aluminium
Shear modulus		26.1 GPa Show Material materials with Shear modulus of 26.1 GPa	H18	EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754
	20.0 °C	24.0 - 26.5 GPa Show Material materials with Shear modulus of 24.0 - 26.5 GPa	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Flat, Wire
Tensile strength	-196.0 °C	298.0 MPa Show Material materials with Tensile strength of 298.0 MPa	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4
	-80.0 °C	225.0 MPa Show Material materials with Tensile strength of 225.0 MPa	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4
	-20.0 °C	214.0 MPa Show Material materials with Tensile strength of 214.0 MPa	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4
		170.0 MPa Show Material materials with Tensile strength of 170.0 MPa	H18	EN 573-3, EN 1301
		180.0 MPa Show Material materials with Tensile strength of 180.0 MPa	H18	EN 573-3, EN 754
		185.0 MPa Show Material materials with Tensile strength of 185.0 MPa	H18	EN 573-3, EN 485, EN 683
		185.0 - 230.0 MPa Show Material materials with Tensile strength of 185.0 - 230.0 MPa	H18	EN 573-3, EN 546
		190.0 MPa Show Material materials with Tensile strength of 190.0 MPa	H18	EN 573-3, EN 1592
	20.0 °C	100.0 MPa Show Material materials with Tensile strength of 100.0 MPa	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513	Tube
	20.0 °C	160.0 MPa Show Material materials with Tensile strength of 160.0 MPa	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4	Wire
	20.0 °C	165.0 - 205.0 MPa Show Material materials with Tensile strength of 165.0 - 205.0 MPa	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4	Flat
	20.0 °C	204.0 MPa Show Material materials with Tensile strength of 204.0 MPa	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4
	100.0 °C	183.0 MPa Show Material materials with Tensile strength of 183.0 MPa	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4
	150.0 °C	163.0 MPa Show Material materials with Tensile strength of 163.0 MPa	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4
	200.0 °C	98.0 MPa Show Material materials with Tensile strength of 98.0 MPa	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4
	260.0 °C	53.0 MPa Show Material materials with Tensile strength of 53.0 MPa	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4
	320.0 °C	28.0 MPa Show Material materials with Tensile strength of 28.0 MPa	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4
	370.0 °C	21.0 MPa Show Material materials with Tensile strength of 21.0 MPa	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape
Coefficient of thermal expansion	20 °C	2.35e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.35e-05 1/K	H18	EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754
	100 °C	2.35e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.35e-05 1/K	H18	EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754
Melting point		645.0 - 655.0 °C Show Material materials with Melting point of 645.0 - 655.0 °C	H18	EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754
Specific heat capacity		893.0 J/(kg·K) Show Material materials with Specific heat capacity of 893.0 J/(kg·K)	H18	EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754
	20.0 °C	893.0 J/(kg·K) Show Material materials with Specific heat capacity of 893.0 J/(kg·K)	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4	Flat, Wire
Thermal conductivity	20.0 °C	160.0 - 200.0 W/(m·K) Show Material materials with Thermal conductivity of 160.0 - 200.0 W/(m·K)	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754	Flat, Wire

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape
Electrical conductivity	20.0 °C	22000000.0 - 28000000.0 S/m Show Material materials with Electrical conductivity of 22000000.0 - 28000000.0 S/m	H18	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 513, VdTÜV WB 420-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754	Flat, Wire
Electrical resistivity		3.57e-08 - 4.55e-08 Ω·m Show Material materials with Electrical resistivity of 3.57e-08 - 4.55e-08 Ω·m	H18	EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chromium	0.1 % Show Material materials with Chromium of 0.1 %	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754	Tube, Flat, Wire
Copper	0.1 % Show Material materials with Copper of 0.1 %	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754	Tube, Flat, Wire
Iron	0.7 % Show Material materials with Iron of 0.7 %	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4	Tube, Flat, Wire
	0.70 % Show Material materials with Iron of 0.70 %	H18	EN 573-3, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754
Magnesium	0.3 % Show Material materials with Magnesium of 0.3 %	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754	Tube, Flat, Wire
Manganese	0.9 - 1.5 % Show Material materials with Manganese of 0.9 - 1.5 %	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754	Tube, Flat, Wire
Silicon	0.5 % Show Material materials with Silicon of 0.5 %	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754	Tube, Flat, Wire
Titanium	0.1 Show Material materials with Titanium of 0.1	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4	Tube, Flat, Wire
Zinc	0.2 % Show Material materials with Zinc of 0.2 %	H18	DIN 1725-1, VdTÜV WB 420-4, VdTÜV WB 513, EN 573-3, EN 573-4, EN 1301, EN 1592, EN 485, EN 546, EN 683, EN 754	Tube, Flat, Wire

Technological properties

Property

Workability

Good workability.