General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Density | 20.0 °C | 2.72 g/cm³ Show Material materials with Density of 2.72 g/cm³ | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 65.0 - 71.0 GPa Show Material materials with Elastic modulus of 65.0 - 71.0 GPa | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat | |
Elongation | 20.0 °C | 4.0 % Show Material materials with Elongation of 4.0 % | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat | A10 |
20.0 °C | 5.0 % Show Material materials with Elongation of 5.0 % | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat | ||
Hardness, Brinell | 20.0 °C | 70.0 [-] Show Material materials with Hardness, Brinell of 70.0 [-] | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | ||||
Shear modulus | 20.0 °C | 25.0 - 27.0 GPa Show Material materials with Shear modulus of 25.0 - 27.0 GPa | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat | |
Tensile strength | 20.0 °C | 240.0 - 280.0 MPa Show Material materials with Tensile strength of 240.0 - 280.0 MPa | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coefficient of thermal expansion | -50.0 °C | 2.15e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.15e-05 1/K | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat | |
100.0 °C | 2.32e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.32e-05 1/K | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat | ||
200.0 °C | 2.41e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.41e-05 1/K | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat | ||
300.0 °C | 2.51e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.51e-05 1/K | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat | ||
Melting point | 629.0 - 654.0 °C Show Material materials with Melting point of 629.0 - 654.0 °C | Typical for Wrought 3000 Series Aluminium | ||||
Specific heat capacity | 20.0 °C | 893.0 J/(kg·K) Show Material materials with Specific heat capacity of 893.0 J/(kg·K) | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat | |
Thermal conductivity | 20.0 °C | 160.0 - 190.0 W/(m·K) Show Material materials with Thermal conductivity of 160.0 - 190.0 W/(m·K) | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 20000000.0 - 24000000.0 S/m Show Material materials with Electrical conductivity of 20000000.0 - 24000000.0 S/m | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat | |
Electrical resistivity | 3.4e-08 - 4.2e-08 Ω·m Show Material materials with Electrical resistivity of 3.4e-08 - 4.2e-08 Ω·m | Typical for Wrought 3000 Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Copper | 0.25 Show Material materials with Copper of 0.25 | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Iron | 0.7 Show Material materials with Iron of 0.7 | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Magnesium | 0.8 - 1.3 % Show Material materials with Magnesium of 0.8 - 1.3 % | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Manganese | 1.0 - 1.5 % Show Material materials with Manganese of 1.0 - 1.5 % | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Silicon | 0.3 Show Material materials with Silicon of 0.3 | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Zinc | 0.25 Show Material materials with Zinc of 0.25 | T6 | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Technological properties
Property | ||
---|---|---|
Workability | Good workability. |