General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Density | 20.0 °C | 2.71 g/cm³ Show Material materials with Density of 2.71 g/cm³ | H1x | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 69.0 - 72.0 GPa Show Material materials with Elastic modulus of 69.0 - 72.0 GPa | Typical for Wrought 8000 Series Aluminium | ||||
Elongation | 20.0 °C | 1.0 % Show Material materials with Elongation of 1.0 % | H1x | DIN 1725-1, EN 573-3, EN 573-4 | Flat | A100 |
20.0 °C | 2.0 % Show Material materials with Elongation of 2.0 % | H1x | DIN 1725-1, EN 573-3, EN 573-4 | Flat | A10 | |
20.0 °C | 3.0 % Show Material materials with Elongation of 3.0 % | H1x | DIN 1725-1, EN 573-3, EN 573-4 | Flat | ||
Hardness, Brinell | 20.0 °C | 55.0 [-] Show Material materials with Hardness, Brinell of 55.0 [-] | H1x | DIN 1725-1, EN 573-3, EN 573-4 | Flat | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 8000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 8000 Series Aluminium | ||||
Tensile strength | 20.0 °C | 190.0 MPa Show Material materials with Tensile strength of 190.0 MPa | H1x | DIN 1725-1, EN 573-3, EN 573-4 | Flat | |
20.0 °C | 200.0 MPa Show Material materials with Tensile strength of 200.0 MPa | H1x | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coefficient of thermal expansion | 1.9e-05 - 2.1e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.9e-05 - 2.1e-05 1/K | Typical for Wrought 8000 Series Aluminium | ||||
Melting point | 645.0 - 655.0 °C Show Material materials with Melting point of 645.0 - 655.0 °C | Typical for Wrought 8000 Series Aluminium | ||||
Specific heat capacity | 920.0 J/(kg·K) Show Material materials with Specific heat capacity of 920.0 J/(kg·K) | Typical for Wrought 8000 Series Aluminium | ||||
Thermal conductivity | 20.0 °C | 210.0 - 220.0 W/(m·K) Show Material materials with Thermal conductivity of 210.0 - 220.0 W/(m·K) | H1x | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 34000000.0 - 35000000.0 S/m Show Material materials with Electrical conductivity of 34000000.0 - 35000000.0 S/m | H1x | DIN 1725-1, EN 573-3, EN 573-4 | Flat | |
Electrical resistivity | 2.8e-08 - 3.5e-08 Ω·m Show Material materials with Electrical resistivity of 2.8e-08 - 3.5e-08 Ω·m | Typical for Wrought 8000 Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Copper | 0.1 Show Material materials with Copper of 0.1 | H1x | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Iron | 0.5 - 1.0 % Show Material materials with Iron of 0.5 - 1.0 % | H1x | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Manganese | 0.1 Show Material materials with Manganese of 0.1 | H1x | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Silicon | 0.4 - 0.8 % Show Material materials with Silicon of 0.4 - 0.8 % | H1x | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Titanium | 0.05 Show Material materials with Titanium of 0.05 | H1x | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Zinc | 0.1 Show Material materials with Zinc of 0.1 | H1x | DIN 1725-1, EN 573-3, EN 573-4 | Flat |