General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Density | 2.68 g/cm³ Show Material materials with Density of 2.68 g/cm³ | H12 | EN 573-3, EN 1592, EN 485, EN 754 | ||
20.0 °C | 2.68 g/cm³ Show Material materials with Density of 2.68 g/cm³ | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Flat, Wire |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Bending angle 180° | 2.0 °/t Show Material materials with Bending angle 180° of 2.0 °/t | H12 | EN 573-3, EN 485 | |||
Bending angle 90° | 1.0 °/t Show Material materials with Bending angle 90° of 1.0 °/t | H12 | EN 573-3, EN 485 | |||
1.5 °/t Show Material materials with Bending angle 90° of 1.5 °/t | H12 | EN 573-3, EN 485 | ||||
2.5 °/t Show Material materials with Bending angle 90° of 2.5 °/t | H12 | EN 573-3, EN 485 | ||||
Elastic modulus | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | H12 | EN 573-3, EN 1592, EN 485, EN 754 | |||
20.0 °C | 70.0 GPa Show Material materials with Elastic modulus of 70.0 GPa | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Flat, Wire | ||
Elongation | 3.0 % Show Material materials with Elongation of 3.0 % | H12 | EN 573-3, EN 485 | A50 | ||
4.0 % Show Material materials with Elongation of 4.0 % | H12 | EN 573-3, EN 485, EN 754 | A50 | |||
5.0 % Show Material materials with Elongation of 5.0 % | H12 | EN 573-3, EN 754 | A100 | |||
5.0 % Show Material materials with Elongation of 5.0 % | H12 | EN 573-3, EN 485 | A50 | |||
8.0 % Show Material materials with Elongation of 8.0 % | H12 | EN 573-3, EN 1592 | A100 | |||
8.0 % Show Material materials with Elongation of 8.0 % | H12 | EN 573-3, EN 485 | A50 | |||
10.0 % Show Material materials with Elongation of 10.0 % | H12 | EN 573-3, EN 485 | A100 | |||
10.0 % Show Material materials with Elongation of 10.0 % | H12 | EN 573-3, EN 485 | A50 | |||
20.0 °C | 4.0 % Show Material materials with Elongation of 4.0 % | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Wire | A100 | |
20.0 °C | 7.0 % Show Material materials with Elongation of 7.0 % | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Wire | A10 | |
20.0 °C | 8.0 % Show Material materials with Elongation of 8.0 % | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Flat | A10 | |
20.0 °C | 10.0 % Show Material materials with Elongation of 10.0 % | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Flat | ||
Hardness, Brinell | 58.0 [-] Show Material materials with Hardness, Brinell of 58.0 [-] | H12 | EN 573-3, EN 485 | |||
20.0 °C | 50.0 [-] Show Material materials with Hardness, Brinell of 50.0 [-] | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Wire | ||
20.0 °C | 60.0 [-] Show Material materials with Hardness, Brinell of 60.0 [-] | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Flat | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||||
Shear modulus | 26.3 GPa Show Material materials with Shear modulus of 26.3 GPa | H12 | EN 573-3, EN 1592, EN 485, EN 754 | |||
20.0 °C | 26.5 GPa Show Material materials with Shear modulus of 26.5 GPa | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Flat, Wire | ||
Shear strength | 20.0 °C | 120.0 MPa Show Material materials with Shear strength of 120.0 MPa | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Wire | |
Tensile strength | 180.0 - 220.0 MPa Show Material materials with Tensile strength of 180.0 - 220.0 MPa | H12 | EN 573-3, EN 754 | |||
190.0 - 230.0 MPa Show Material materials with Tensile strength of 190.0 - 230.0 MPa | H12 | EN 573-3, EN 485 | ||||
210.0 MPa Show Material materials with Tensile strength of 210.0 MPa | H12 | EN 573-3, EN 1592 | ||||
20.0 °C | 190.0 MPa Show Material materials with Tensile strength of 190.0 MPa | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Wire | ||
20.0 °C | 205.0 - 245.0 MPa Show Material materials with Tensile strength of 205.0 - 245.0 MPa | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Flat |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3699999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3699999999999997e-05 1/K | H12 | EN 573-3, EN 1592, EN 485, EN 754 | ||
100 °C | 2.3699999999999997e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3699999999999997e-05 1/K | H12 | EN 573-3, EN 1592, EN 485, EN 754 | |||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | ||||
Melting point | 610.0 - 650.0 °C Show Material materials with Melting point of 610.0 - 650.0 °C | H12 | EN 573-3, EN 1592, EN 485, EN 754 | |||
Specific heat capacity | 20.0 °C | 921.0 J/(kg·K) Show Material materials with Specific heat capacity of 921.0 J/(kg·K) | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Flat, Wire | |
Thermal conductivity | 140.0 - 160.0 W/(m·K) Show Material materials with Thermal conductivity of 140.0 - 160.0 W/(m·K) | H12 | EN 573-3, EN 1592, EN 485, EN 754 | |||
20.0 °C | 167.0 W/(m·K) Show Material materials with Thermal conductivity of 167.0 W/(m·K) | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Flat, Wire |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Electrical conductivity | 25000000.0 - 30000000.0 S/m Show Material materials with Electrical conductivity of 25000000.0 - 30000000.0 S/m | H12 | EN 573-3, EN 1592, EN 485, EN 754 | ||
20.0 °C | 26000000.0 S/m Show Material materials with Electrical conductivity of 26000000.0 S/m | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Flat, Wire | |
Electrical resistivity | 3.33e-08 - 4e-08 Ω·m Show Material materials with Electrical resistivity of 3.33e-08 - 4e-08 Ω·m | H12 | EN 573-3, EN 1592, EN 485, EN 754 |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Chromium | 0.15 % Show Material materials with Chromium of 0.15 % | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Flat, Wire |
Copper | 0.15 % Show Material materials with Copper of 0.15 % | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Flat, Wire |
Iron | 0.5 % Show Material materials with Iron of 0.5 % | H12 | DIN 1725-1, EN 573-3, EN 573-4 | Flat, Wire |
0.50 % Show Material materials with Iron of 0.50 % | H12 | EN 573-3, EN 1592, EN 485, EN 754 | ||
Magnesium | 1.7 - 2.4 % Show Material materials with Magnesium of 1.7 - 2.4 % | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Flat, Wire |
Manganese | 0.1 - 0.5 % Show Material materials with Manganese of 0.1 - 0.5 % | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Flat, Wire |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Flat, Wire |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Flat, Wire |
Zinc | 0.15 % Show Material materials with Zinc of 0.15 % | H12 | DIN 1725-1, EN 573-3, EN 573-4, EN 1592, EN 485, EN 754 | Flat, Wire |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: sufficient, Protective: very good | |
Brazing | hard brazing (with flux/ without flux): sufficient / poor, friction soldering: good, soft brazing with flux: sufficient | |
Corrosion properties | Seawater: good, weathering: very good | |
Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / acceptable (H12) |