Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Density | 20.0 °C | 2.8 g/cm³ Show Material materials with Density of 2.8 g/cm³ | H14 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 65.0 - 73.5 GPa Show Material materials with Elastic modulus of 65.0 - 73.5 GPa | H14 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire | |
Hardness, Brinell | 20.0 °C | 65.0 [-] Show Material materials with Hardness, Brinell of 65.0 [-] | H14 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||||
Shear modulus | 20.0 °C | 26.0 - 28.5 GPa Show Material materials with Shear modulus of 26.0 - 28.5 GPa | H14 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire | |
Tensile strength | 20.0 °C | 220.0 - 300.0 MPa Show Material materials with Tensile strength of 220.0 - 300.0 MPa | H14 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium | ||||
Melting point | 500.0 - 650.0 °C Show Material materials with Melting point of 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium | ||||
Specific heat capacity | 20.0 °C | 921.0 J/(kg·K) Show Material materials with Specific heat capacity of 921.0 J/(kg·K) | H14 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire | |
Thermal conductivity | 20.0 °C | 130.0 - 200.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 - 200.0 W/(m·K) | H14 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 18000000.0 - 28000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 28000000.0 S/m | H14 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire | |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m Show Material materials with Electrical resistivity of 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Chromium | 0.1 Show Material materials with Chromium of 0.1 | H14 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire |
Copper | 3.5 - 4.5 % Show Material materials with Copper of 3.5 - 4.5 % | H14 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire |
Iron | 0.7 Show Material materials with Iron of 0.7 | H14 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire |
Magnesium | 0.4 - 1.0 % Show Material materials with Magnesium of 0.4 - 1.0 % | H14 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire |
Manganese | 0.4 - 1.0 % Show Material materials with Manganese of 0.4 - 1.0 % | H14 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire |
Silicon | 0.2 - 0.8 % Show Material materials with Silicon of 0.2 - 0.8 % | H14 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire |
Zinc | 0.25 Show Material materials with Zinc of 0.25 | H14 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire |
Technological properties
Property | ||
---|---|---|
Workability | Moderate Workability |