General
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 72.5 GPa Show Material materials with Elastic modulus of 72.5 GPa | T3 | EN 573-3, EN 754 | |||
20.0 °C | 65.0 - 73.5 GPa Show Material materials with Elastic modulus of 65.0 - 73.5 GPa | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Profile, Rod, Sheet, Flat, Tube, Wire | ||
Elongation | 8.0 % Show Material materials with Elongation of 8.0 % | T3 | EN 573-3, EN 754 | A50 | ||
10.0 % Show Material materials with Elongation of 10.0 % | T3 | EN 573-3, EN 754 | A100 | |||
20.0 °C | 2.0 % Show Material materials with Elongation of 2.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire | A100 | |
20.0 °C | 6.0 % Show Material materials with Elongation of 6.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire | A10 | |
20.0 °C | 6.0 % Show Material materials with Elongation of 6.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Rod | ||
20.0 °C | 7.0 % Show Material materials with Elongation of 7.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Rod | ||
20.0 °C | 8.0 % Show Material materials with Elongation of 8.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Profile, Rod | A10 | |
20.0 °C | 10.0 % Show Material materials with Elongation of 10.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Tube | A10 | |
20.0 °C | 10.0 % Show Material materials with Elongation of 10.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Profile, Rod | ||
20.0 °C | 11.0 % Show Material materials with Elongation of 11.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Flat | A10 | |
20.0 °C | 12.0 % Show Material materials with Elongation of 12.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Tube | A10 | |
20.0 °C | 12.0 % Show Material materials with Elongation of 12.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Tube, Sheet | ||
20.0 °C | 13.0 % Show Material materials with Elongation of 13.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Flat, Sheet | ||
20.0 °C | 14.0 % Show Material materials with Elongation of 14.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Tube | ||
Hardness, Brinell | 20.0 °C | 95.0 [-] Show Material materials with Hardness, Brinell of 95.0 [-] | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Profile, Tube, Sheet | |
20.0 °C | 95.0 - 100.0 [-] Show Material materials with Hardness, Brinell of 95.0 - 100.0 [-] | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Sheet | ||
20.0 °C | 100.0 [-] Show Material materials with Hardness, Brinell of 100.0 [-] | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Flat, Sheet | ||
20.0 °C | 105.0 [-] Show Material materials with Hardness, Brinell of 105.0 [-] | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Tube, Wire | ||
20.0 °C | 110.0 [-] Show Material materials with Hardness, Brinell of 110.0 [-] | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Rod | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||||
Shear modulus | 27.2 GPa Show Material materials with Shear modulus of 27.2 GPa | T3 | EN 573-3, EN 754 | |||
20.0 °C | 26.0 - 28.5 GPa Show Material materials with Shear modulus of 26.0 - 28.5 GPa | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Profile, Rod, Sheet, Flat, Tube, Wire | ||
Tensile strength | 400.0 MPa Show Material materials with Tensile strength of 400.0 MPa | T3 | EN 573-3, EN 754 | |||
20.0 °C | 330.0 MPa Show Material materials with Tensile strength of 330.0 MPa | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Rod | ||
20.0 °C | 360.0 MPa Show Material materials with Tensile strength of 360.0 MPa | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Rod | ||
20.0 °C | 370.0 MPa Show Material materials with Tensile strength of 370.0 MPa | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Tube | ||
20.0 °C | 380.0 MPa Show Material materials with Tensile strength of 380.0 MPa | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Profile, Rod, Tube | ||
20.0 °C | 385.0 MPa Show Material materials with Tensile strength of 385.0 MPa | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Sheet | ||
20.0 °C | 390.0 MPa Show Material materials with Tensile strength of 390.0 MPa | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Tube, Sheet | ||
20.0 °C | 395.0 MPa Show Material materials with Tensile strength of 395.0 MPa | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Flat | ||
20.0 °C | 400.0 MPa Show Material materials with Tensile strength of 400.0 MPa | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Rod | ||
20.0 °C | 420.0 MPa Show Material materials with Tensile strength of 420.0 MPa | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Wire |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T3 | EN 573-3, EN 754 | |
100 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | T3 | EN 573-3, EN 754 | ||
Melting point | 512.0 - 650.0 °C Show Material materials with Melting point of 512.0 - 650.0 °C | T3 | EN 573-3, EN 754 | ||
Specific heat capacity | 20.0 °C | 921.0 J/(kg·K) Show Material materials with Specific heat capacity of 921.0 J/(kg·K) | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Profile, Rod, Sheet, Flat, Tube, Wire |
Thermal conductivity | 20.0 °C | 130.0 - 200.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 - 200.0 W/(m·K) | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 754 | Profile, Rod, Sheet, Flat, Tube, Wire |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 18000000.0 - 28000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 28000000.0 S/m | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 754 | Profile, Rod, Sheet, Flat, Tube, Wire |
Electrical resistivity | 3.57e-08 - 5.56e-08 Ω·m Show Material materials with Electrical resistivity of 3.57e-08 - 5.56e-08 Ω·m | T3 | EN 573-3, EN 754 |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 754 | Profile, Rod, Sheet, Flat, Tube, Wire |
Copper | 3.5 - 4.5 % Show Material materials with Copper of 3.5 - 4.5 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 754 | Profile, Rod, Sheet, Flat, Tube, Wire |
Iron | 0.7 % Show Material materials with Iron of 0.7 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1 | Profile, Rod, Sheet, Flat, Tube, Wire |
0.70 % Show Material materials with Iron of 0.70 % | T3 | EN 573-3, EN 754 | ||
Magnesium | 0.4 - 1.0 % Show Material materials with Magnesium of 0.4 - 1.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 754 | Profile, Rod, Sheet, Flat, Tube, Wire |
Manganese | 0.4 - 1.0 % Show Material materials with Manganese of 0.4 - 1.0 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 754 | Profile, Rod, Sheet, Flat, Tube, Wire |
Silicon | 0.2 - 0.8 % Show Material materials with Silicon of 0.2 - 0.8 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 754 | Profile, Rod, Sheet, Flat, Tube, Wire |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | T3 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.1324-1, EN 754 | Profile, Rod, Sheet, Flat, Tube, Wire |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: not suitable, Protective: good | |
Brazing | hard brazing (with flux/ without flux): not suitable / not suitable, friction soldering: acceptable, soft brazing with flux: not suitable | |
Corrosion properties | Seawater: poor, weathering: sufficient | |
Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) acceptable (O) / acceptable (O) |