DIN 1725-1 Grade 3.3206 T3

Want to keep this datasheet? Save it now in your required format

Description

This cold and hot hardenable material reaches mechanical strength from 200 to 250 MPa with A5-elongation at break of approx. 10 %. In the warm and cold-hardened state this alloy is only limited ductile, in the soft material condition however well. Weldability, corrosion resistance and anodising of this material are good. Due to the special suitability of this alloy for the extrusion those are present lot of profile cross-sectional shapes for application in static loading case in the automobile construction or in the building industry. The company Erbsloeh Aluminum leads under evenly this material number among other things the trade name AlMgSi0,3. It pay attention that only two further trade names (6030 and 466) of this company to this designation are to be assigned. Heat treatment for hardening: solution annealing: 525 to 540 °C, quenching on air or in water cold ageing: 5 to 8 d at ambient temperatures hot ageing: 4 to 16 h at 155 to 190 °C. Application: Window, doors, window walls, front plates, roller shutter, roll gates, bearing constructions, heat exchanger (gilled pipes), commercial motor vehicle superstructures, machine tables, metal goods, food industry, equipment of rail-mounted vehicles (stroke sun roofs, railroad car doors), optics, reflectors, operating sectors of hydraulic/pneumatics in mechanical engineering, trunk superstructures in the boat and shipbuilding, sail masts, road signs, trim in the automobile engineering, shower cubicles, fences and partitions, pipings in compressed gas tanks, camping furniture.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density	20.0 °C	2.7 g/cm³ Show Material materials with Density of 2.7 g/cm³	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube, Wire

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus	20.0 °C	67.0 GPa Show Material materials with Elastic modulus of 67.0 GPa	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube, Wire
Elongation	20.0 °C	3.0 % Show Material materials with Elongation of 3.0 %	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Wire	A100
	20.0 °C	6.0 % Show Material materials with Elongation of 6.0 %	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Wire	A10
	20.0 °C	6.0 % Show Material materials with Elongation of 6.0 %	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Wire	A100
	20.0 °C	10.0 % Show Material materials with Elongation of 10.0 %	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Wire	A10
	20.0 °C	13.0 % Show Material materials with Elongation of 13.0 %	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube	A10
	20.0 °C	15.0 % Show Material materials with Elongation of 15.0 %	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube
Hardness, Brinell	20.0 °C	45.0 [-] Show Material materials with Hardness, Brinell of 45.0 [-]	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube
	20.0 °C	60.0 [-] Show Material materials with Hardness, Brinell of 60.0 [-]	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Wire
	20.0 °C	80.0 [-] Show Material materials with Hardness, Brinell of 80.0 [-]	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Wire
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m				Typical for Wrought 6000 Series Aluminium
Poisson's ratio		0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-]				Typical for Wrought 6000 Series Aluminium
Shear modulus	20.0 °C	25.0 GPa Show Material materials with Shear modulus of 25.0 GPa	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube, Wire
Tensile strength	20.0 °C	130.0 MPa Show Material materials with Tensile strength of 130.0 MPa	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube
	20.0 °C	200.0 MPa Show Material materials with Tensile strength of 200.0 MPa	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Wire
	20.0 °C	270.0 MPa Show Material materials with Tensile strength of 270.0 MPa	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Wire

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coefficient of thermal expansion		1.6e-05 - 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.6e-05 - 2.4e-05 1/K				Typical for Wrought 6000 Series Aluminium
Melting point		555.0 - 655.0 °C Show Material materials with Melting point of 555.0 - 655.0 °C				Typical for Wrought 6000 Series Aluminium
Specific heat capacity		887.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 887.0 - 963.0 J/(kg·K)				Typical for Wrought 6000 Series Aluminium
Thermal conductivity	20.0 °C	220.0 W/(m·K) Show Material materials with Thermal conductivity of 220.0 W/(m·K)	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube, Wire

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Electrical conductivity	20.0 °C	30000000.0 - 32000000.0 S/m Show Material materials with Electrical conductivity of 30000000.0 - 32000000.0 S/m	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube, Wire
Electrical resistivity		2.9e-08 - 5e-08 Ω·m Show Material materials with Electrical resistivity of 2.9e-08 - 5e-08 Ω·m				Typical for Wrought 6000 Series Aluminium

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chromium	0.05 Show Material materials with Chromium of 0.05	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube, Wire
Copper	0.1 Show Material materials with Copper of 0.1	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube, Wire
Iron	0.1 - 0.3 % Show Material materials with Iron of 0.1 - 0.3 %	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube, Wire
Magnesium	0.35 - 0.6 % Show Material materials with Magnesium of 0.35 - 0.6 %	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube, Wire
Manganese	0.1 Show Material materials with Manganese of 0.1	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube, Wire
Silicon	0.3 - 0.6 % Show Material materials with Silicon of 0.3 - 0.6 %	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube, Wire
Titanium	0.1 Show Material materials with Titanium of 0.1	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube, Wire
Zinc	0.15 Show Material materials with Zinc of 0.15	T3	DIN 1725-1, EN 573-3, EN 573-4, VdTÜV WB 492, VdTÜV WB 420-4	Profile, Rod, Tube, Wire

Technological properties

Property

Workability

Excellent workability.

Looking for suppliers of this material? Click to see 6 supplier of DIN 1725-1 Grade 3.3206 T3 on Matmatch

DIN 1725-1 Grade 3.3206 T3

Description

Related Standards

Equivalent Materials

Ashby charts

There are 3 other suppliers for this grade.

Preview all suppliers

Suggested reading

Properties