Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 20.0 °C | 2.8 g/cm³ Show Material materials with Density of 2.8 g/cm³ | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 70.0 - 73.0 GPa Show Material materials with Elastic modulus of 70.0 - 73.0 GPa | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | |
Elongation | 20.0 °C | 3.0 % Show Material materials with Elongation of 3.0 % | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | |
20.0 °C | 4.0 % Show Material materials with Elongation of 4.0 % | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
20.0 °C | 6.0 % Show Material materials with Elongation of 6.0 % | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
Hardness, Brinell | 20.0 °C | 115.0 [-] Show Material materials with Hardness, Brinell of 115.0 [-] | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | |
20.0 °C | 120.0 [-] Show Material materials with Hardness, Brinell of 120.0 [-] | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 7000 Series Aluminium | ||||
Shear modulus | 20.0 °C | 25.0 - 27.0 GPa Show Material materials with Shear modulus of 25.0 - 27.0 GPa | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | |
Tensile strength | 20.0 °C | 410.0 MPa Show Material materials with Tensile strength of 410.0 MPa | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | |
20.0 °C | 420.0 MPa Show Material materials with Tensile strength of 420.0 MPa | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
20.0 °C | 440.0 MPa Show Material materials with Tensile strength of 440.0 MPa | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
20.0 °C | 450.0 MPa Show Material materials with Tensile strength of 450.0 MPa | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | -50.0 °C | 2.16e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.16e-05 1/K | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | |
100.0 °C | 2.34e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.34e-05 1/K | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
200.0 °C | 2.43e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.43e-05 1/K | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
300.0 °C | 2.52e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.52e-05 1/K | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | ||
Melting point | 465.0 - 655.0 °C Show Material materials with Melting point of 465.0 - 655.0 °C | Typical for Wrought 7000 Series Aluminium | ||||
Specific heat capacity | 20.0 °C | 862.0 J/(kg·K) Show Material materials with Specific heat capacity of 862.0 J/(kg·K) | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | |
Thermal conductivity | 20.0 °C | 130.0 - 160.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 - 160.0 W/(m·K) | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 19000000.0 - 23000000.0 S/m Show Material materials with Electrical conductivity of 19000000.0 - 23000000.0 S/m | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging | |
Electrical resistivity | 2.9e-08 - 5.6e-08 Ω·m Show Material materials with Electrical resistivity of 2.9e-08 - 5.6e-08 Ω·m | Typical for Wrought 7000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.18 - 0.28 % Show Material materials with Chromium of 0.18 - 0.28 % | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging |
Copper | 1.2 - 2.0 % Show Material materials with Copper of 1.2 - 2.0 % | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging |
Iron | 0.5 Show Material materials with Iron of 0.5 | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging |
Magnesium | 2.1 - 2.9 % Show Material materials with Magnesium of 2.1 - 2.9 % | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging |
Manganese | 0.3 Show Material materials with Manganese of 0.3 | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging |
Silicon | 0.4 Show Material materials with Silicon of 0.4 | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging |
Titanium | 0.2 Show Material materials with Titanium of 0.2 | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging |
Zinc | 5.1 - 6.1 % Show Material materials with Zinc of 5.1 - 6.1 % | T5 | DIN 1725-1, EN 573-3, EN 573-4, WL 3.4364-1 | Forging |
Technological properties
| Property | ||
|---|---|---|
| Brazing | Excellent | |