General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Density | 20.0 °C | 2.8 g/cm³ Show Material materials with Density of 2.8 g/cm³ | T76511 | WL 3.4364-1, DIN 1725-1 | Profile, Rod |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Bulk Modulus | 20.0 °C | 72.5 GPa Show Material materials with Bulk Modulus of 72.5 GPa | T76511 | WL 3.4364-1, DIN 1725-1 | Profile, Rod | |
Elastic modulus | 20.0 °C | 71.0 GPa Show Material materials with Elastic modulus of 71.0 GPa | T76511 | WL 3.4364-1, DIN 1725-1 | Profile, Rod | |
Elongation | 20.0 °C | 3.0 % Show Material materials with Elongation of 3.0 % | T76511 | WL 3.4364-1, DIN 1725-1 | Rod | Transverse |
20.0 °C | 4.0 % Show Material materials with Elongation of 4.0 % | T76511 | WL 3.4364-1, DIN 1725-1 | Profile, Rod | Transverse | |
20.0 °C | 7.0 % Show Material materials with Elongation of 7.0 % | T76511 | WL 3.4364-1, DIN 1725-1 | Rod | Transverse | |
20.0 °C | 7.0 % Show Material materials with Elongation of 7.0 % | T76511 | WL 3.4364-1, DIN 1725-1 | Profile | ||
Hardness, Brinell | 20.0 °C | 135.0 [-] Show Material materials with Hardness, Brinell of 135.0 [-] | T76511 | WL 3.4364-1, DIN 1725-1 | Profile, Rod | Transverse |
20.0 °C | 135.0 [-] Show Material materials with Hardness, Brinell of 135.0 [-] | T76511 | WL 3.4364-1, DIN 1725-1 | Profile | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 7000 Series Aluminium | ||||
Shear modulus | 26.4 - 27.1 GPa Show Material materials with Shear modulus of 26.4 - 27.1 GPa | Typical for Wrought 7000 Series Aluminium | ||||
Tensile strength | 20.0 °C | 450.0 MPa Show Material materials with Tensile strength of 450.0 MPa | T76511 | WL 3.4364-1, DIN 1725-1 | Profile | Transverse |
20.0 °C | 460.0 MPa Show Material materials with Tensile strength of 460.0 MPa | T76511 | WL 3.4364-1, DIN 1725-1 | Rod | Transverse | |
20.0 °C | 470.0 MPa Show Material materials with Tensile strength of 470.0 MPa | T76511 | WL 3.4364-1, DIN 1725-1 | Profile, Rod | Transverse | |
20.0 °C | 505.0 MPa Show Material materials with Tensile strength of 505.0 MPa | T76511 | WL 3.4364-1, DIN 1725-1 | Profile | ||
20.0 °C | 510.0 MPa Show Material materials with Tensile strength of 510.0 MPa | T76511 | WL 3.4364-1, DIN 1725-1 | Rod | Transverse | |
20.0 °C | 515.0 MPa Show Material materials with Tensile strength of 515.0 MPa | T76511 | WL 3.4364-1, DIN 1725-1 | Rod | Transverse | |
20.0 °C | 515.0 MPa Show Material materials with Tensile strength of 515.0 MPa | T76511 | WL 3.4364-1, DIN 1725-1 | Profile |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 2.1e-05 - 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1e-05 - 2.4e-05 1/K | Typical for Wrought 7000 Series Aluminium |
Melting point | 465.0 - 655.0 °C Show Material materials with Melting point of 465.0 - 655.0 °C | Typical for Wrought 7000 Series Aluminium |
Specific heat capacity | 795.0 - 1050.0 J/(kg·K) Show Material materials with Specific heat capacity of 795.0 - 1050.0 J/(kg·K) | Typical for Wrought 7000 Series Aluminium |
Thermal conductivity | 121.0 - 170.0 W/(m·K) Show Material materials with Thermal conductivity of 121.0 - 170.0 W/(m·K) | Typical for Wrought 7000 Series Aluminium |
Electrical
Property | Value | Comment |
---|---|---|
Electrical conductivity | 18000000.0 - 34000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 34000000.0 S/m | Typical for Wrought 7000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5.6e-08 Ω·m Show Material materials with Electrical resistivity of 2.9e-08 - 5.6e-08 Ω·m | Typical for Wrought 7000 Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Chromium | 0.18 - 0.28 % Show Material materials with Chromium of 0.18 - 0.28 % | T76511 | WL 3.4364-1, DIN 1725-1 | Profile, Rod |
Copper | 1.2 - 2.0 % Show Material materials with Copper of 1.2 - 2.0 % | T76511 | WL 3.4364-1, DIN 1725-1 | Profile, Rod |
Iron | 0.5 Show Material materials with Iron of 0.5 | T76511 | WL 3.4364-1, DIN 1725-1 | Profile, Rod |
Magnesium | 2.1 - 2.9 % Show Material materials with Magnesium of 2.1 - 2.9 % | T76511 | WL 3.4364-1, DIN 1725-1 | Profile, Rod |
Manganese | 0.3 Show Material materials with Manganese of 0.3 | T76511 | WL 3.4364-1, DIN 1725-1 | Profile, Rod |
Silicon | 0.4 Show Material materials with Silicon of 0.4 | T76511 | WL 3.4364-1, DIN 1725-1 | Profile, Rod |
Titanium | 0.2 Show Material materials with Titanium of 0.2 | T76511 | WL 3.4364-1, DIN 1725-1 | Profile, Rod |
Zinc | 5.1 - 6.1 % Show Material materials with Zinc of 5.1 - 6.1 % | T76511 | WL 3.4364-1, DIN 1725-1 | Profile, Rod |
Technological properties
Property | ||
---|---|---|
Brazing | Excellent |