DIN 1725-1 Grade 3.4365 T79511

View suppliers (6)
Want to keep this datasheet? Save it now in your required format

Description

DIN 3.4365 is a high-strength alloy that offers good stress-corrosion cracking resistance. Known as a mainstay in the aerospace industry since it was introduced, Aluminum 7075 brings moderate toughness as well as an excellent strength-to-weight ratio. It is also important to note that at sub-zero temperatures Aluminum 7075 increases in strength.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueConditionRelated StandardsShape

Density

20.0 °C

2.8 g/cm³

Show Material materials with Density of 2.8 g/cm³

T79511

WL 3.4364-1, DIN 1725-1

Profile

Mechanical

PropertyTemperatureValueConditionRelated StandardsShapeComment

Bulk Modulus

20.0 °C

72.5 GPa

Show Material materials with Bulk Modulus of 72.5 GPa

T79511

WL 3.4364-1, DIN 1725-1

Profile

Elastic modulus

20.0 °C

71.0 GPa

Show Material materials with Elastic modulus of 71.0 GPa

T79511

WL 3.4364-1, DIN 1725-1

Profile

Elongation

20.0 °C

6.0 %

Show Material materials with Elongation of 6.0 %

T79511

WL 3.4364-1, DIN 1725-1

Profile

20.0 °C

8.0 %

Show Material materials with Elongation of 8.0 %

T79511

WL 3.4364-1, DIN 1725-1

Profile

Hardness, Brinell

20.0 °C

140.0 [-]

Show Material materials with Hardness, Brinell of 140.0 [-]

T79511

WL 3.4364-1, DIN 1725-1

Profile

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 7000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 7000 Series Aluminium

Shear modulus

26.4 - 27.1 GPa

Show Material materials with Shear modulus of 26.4 - 27.1 GPa

Typical for Wrought 7000 Series Aluminium

Tensile strength

20.0 °C

520.0 MPa

Show Material materials with Tensile strength of 520.0 MPa

T79511

WL 3.4364-1, DIN 1725-1

Profile

20.0 °C

540.0 MPa

Show Material materials with Tensile strength of 540.0 MPa

T79511

WL 3.4364-1, DIN 1725-1

Profile

Thermal

PropertyValueComment

Coefficient of thermal expansion

2.1e-05 - 2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.1e-05 - 2.4e-05 1/K

Typical for Wrought 7000 Series Aluminium

Melting point

465.0 - 655.0 °C

Show Material materials with Melting point of 465.0 - 655.0 °C

Typical for Wrought 7000 Series Aluminium

Specific heat capacity

795.0 - 1050.0 J/(kg·K)

Show Material materials with Specific heat capacity of 795.0 - 1050.0 J/(kg·K)

Typical for Wrought 7000 Series Aluminium

Thermal conductivity

121.0 - 170.0 W/(m·K)

Show Material materials with Thermal conductivity of 121.0 - 170.0 W/(m·K)

Typical for Wrought 7000 Series Aluminium

Electrical

PropertyValueComment

Electrical conductivity

18000000.0 - 34000000.0 S/m

Show Material materials with Electrical conductivity of 18000000.0 - 34000000.0 S/m

Typical for Wrought 7000 Series Aluminium

Electrical resistivity

2.9e-08 - 5.6e-08 Ω·m

Show Material materials with Electrical resistivity of 2.9e-08 - 5.6e-08 Ω·m

Typical for Wrought 7000 Series Aluminium

Chemical properties

PropertyValueConditionRelated StandardsShape

Chromium

0.18 - 0.28 %

Show Material materials with Chromium of 0.18 - 0.28 %

T79511

WL 3.4364-1, DIN 1725-1

Profile

Copper

1.2 - 2.0 %

Show Material materials with Copper of 1.2 - 2.0 %

T79511

WL 3.4364-1, DIN 1725-1

Profile

Iron

0.5

Show Material materials with Iron of 0.5

T79511

WL 3.4364-1, DIN 1725-1

Profile

Magnesium

2.1 - 2.9 %

Show Material materials with Magnesium of 2.1 - 2.9 %

T79511

WL 3.4364-1, DIN 1725-1

Profile

Manganese

0.3

Show Material materials with Manganese of 0.3

T79511

WL 3.4364-1, DIN 1725-1

Profile

Silicon

0.4

Show Material materials with Silicon of 0.4

T79511

WL 3.4364-1, DIN 1725-1

Profile

Titanium

0.2

Show Material materials with Titanium of 0.2

T79511

WL 3.4364-1, DIN 1725-1

Profile

Zinc

5.1 - 6.1 %

Show Material materials with Zinc of 5.1 - 6.1 %

T79511

WL 3.4364-1, DIN 1725-1

Profile

Technological properties

Property
Brazing

Excellent