EN 573-3 Grade AW-3103A O

Want to keep this datasheet? Save it now in your required format

Description

Stronger and harder than 1200, yet retains comparable ductility and corrosion resistance.

Related Standards

Equivalent Materials

Ashby charts

See where EN 573-3 Grade AW-3103A O falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.73 g/cm³ at 20 °C

Dimension

Thickness

t

0.2 - 4 mm

Mechanical

Bending angle 180°

θ180

0 °/t at 20 °C

Show 3000 Series materials with Bending angle 180° of 0 °/t at 20 °C

Bending angle 90°

θ90

0 °/t at 20 °C

Show 3000 Series materials with Bending angle 90° of 0 °/t at 20 °C

Elastic modulus

E

70 GPa at 20 °C

Show 3000 Series materials with Elastic modulus of 70 GPa at 20 °C

Elongation

A

22 % at 20 °C

Show 3000 Series materials with Elongation of 22 % at 20 °C

Elongation A50

A50

1 - 23 % at 20 °C

Show 3000 Series materials with Elongation A50 of 1 - 23 % at 20 °C

Hardness, HBW

HBW

27 [-] at 20 °C

Show 3000 Series materials with Hardness, HBW of 27 [-] at 20 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Show 3000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 20 °C

Typical for Wrought 3000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Show 3000 Series materials with Poisson's ratio of 0.33 [-] at 20 °C

Typical for Wrought 3000 Series Aluminium

Shear modulus

G

26.5 GPa at 20 °C

Show 3000 Series materials with Shear modulus of 26.5 GPa at 20 °C

Tensile strength

Rm

90 - 100 MPa at 20 °C

Show 3000 Series materials with Tensile strength of 90 - 100 MPa at 20 °C

Yield strength

YS

35 MPa at 20 °C

Show 3000 Series materials with Yield strength of 35 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

35 MPa at 20 °C

Show 3000 Series materials with Yield strength Rp0.2 of 35 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.3E-5 1/K at 100 °C

20-100°C

Melting point

Tm

629 - 654 °C

Typical for Wrought 3000 Series Aluminium

Specific heat capacity

cp

893 - 920 J/(kg·K) at 20 °C

Typical for Wrought 3000 Series Aluminium

Thermal conductivity

λ

176 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

2.30E+7 - 2.90E+7 S/m at 20 °C

Typical for Wrought 3000 Series Aluminium

Electrical resistivity

ρel

4.3E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Fe

0.7 %

Mn

0.7 - 1.4 %

Si

0.5 %

Mg

0.3 %

Zn

0.2 %

More

Technological properties

Anodizing

Very Good

Application areas

Facades: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Roofing: Single sheet, Sheets for composites/ sandwich Panels; Doors: Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Interiors and ceilings: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Furniture, Plinths, Blinds: Single sheet, Intermediate transformation/interior use; Anodizing Quality; Heat exchangers: Fins, Heat exchangers; Tubes: Flexible tube, Pipes; Cosmetics: Cosmetics pieces; Semi-rigid and corrugated: Smooth wall; Components: Automotive fins, Heat exchangers

Brazing

Excellent

Corrosion properties

Very Good

Welding

Very Good

Workability

Very Good

This material data has been provided by Aludium,WIAM.