EN 573-3 Grade AW-5005A H12

Want to keep this datasheet? Save it now in your required format

Description

Naturally hard AlMg alloy. The alloy is food safe.

Related Standards

Equivalent Materials

Ashby charts

See where EN 573-3 Grade AW-5005A H12 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.69 - 2.7 g/cm³ at 20 °C

Dimension

Dimensions

Dicke

Mechanical

Bending angle 180°

θ180

1 - 1.5 °/t at 20 °C

Show 5000 Series materials with Bending angle 180° of 1 - 1.5 °/t at 20 °C

Bending angle 90°

θ90

0 - 2 °/t at 20 °C

Show 5000 Series materials with Bending angle 90° of 0 - 2 °/t at 20 °C

Elastic modulus

E

69.5 GPa at 20 °C

Show 5000 Series materials with Elastic modulus of 69.5 GPa at 20 °C

Elongation A50

A50

2 - 7 % at 20 °C

Show 5000 Series materials with Elongation A50 of 2 - 7 % at 20 °C

Elongation A50, transverse

A50,trans

2 - 7 % at 20 °C

Show 5000 Series materials with Elongation A50, transverse of 2 - 7 % at 20 °C

Hardness, Brinell

HB

39 [-] at 20 °C

Show 5000 Series materials with Hardness, Brinell of 39 [-] at 20 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Show 5000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 20 °C

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Show 5000 Series materials with Poisson's ratio of 0.33 [-] at 20 °C

Shear modulus

G

25 - 26.1 GPa at 20 °C

Show 5000 Series materials with Shear modulus of 25 - 26.1 GPa at 20 °C

Tensile strength

Rm

125 - 165 MPa at 20 °C

Show 5000 Series materials with Tensile strength of 125 - 165 MPa at 20 °C

Tensile strength, transverse

Rm,trans

125 - 165 MPa at 20 °C

Show 5000 Series materials with Tensile strength, transverse of 125 - 165 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

95 MPa at 20 °C

Show 5000 Series materials with Yield strength Rp0.2 of 95 MPa at 20 °C

Yield strength Rp0.2, transverse

Rp0.2,trans

95 MPa at 20 °C

Show 5000 Series materials with Yield strength Rp0.2, transverse of 95 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.18E-5 1/K at -50 °C

Hide chart

Max service temperature

Tmax

150 °C

Typical for Wrought 5000 Series Aluminium

Melting point

Tm

630 - 650 °C

Specific heat capacity

cp

879 - 899 J/(kg·K) at 20 °C

Thermal conductivity

λ

160 - 220 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

2.30E+7 - 3.10E+7 S/m at 20 °C

Electrical resistivity

ρel

3.23E-8 - 4.35E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Other

-

each 0.05, total 0.15, Rest Al

Mg

0.7 - 1.1 %

Fe

0.45 %

Si

0.3 %

Zn

0.2 %

More

Technological properties

Anodizing

decorative: gut (EQ: sehr gut), Protective: very good

Brazing

hard brazing (with flux/ without flux): sufficient - poor / sufficient, friction soldering: good, soft brazing with flux: acceptable

Corrosion properties

Seawater: good, weathering: very good

Workability

Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / good (H12)

This material data has been provided by WIAM,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.