General
Property | Value | Comment |
---|---|---|
Density | 2.75 - 2.84 g/cm³ Show Material materials with Density of 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 70.0 - 73.0 GPa Show Material materials with Elastic modulus of 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | ||||
Elongation | 20.0 °C | 3.0 % Show Material materials with Elongation of 3.0 % | T652 | WL 3.1254-1 | Forging | Transverse |
20.0 °C | 4.0 % Show Material materials with Elongation of 4.0 % | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 5.0 % Show Material materials with Elongation of 5.0 % | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 6.0 % Show Material materials with Elongation of 6.0 % | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 7.0 % Show Material materials with Elongation of 7.0 % | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 8.0 % Show Material materials with Elongation of 8.0 % | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 8.0 % Show Material materials with Elongation of 8.0 % | T652 | WL 3.1254-1 | Forging | ||
Hardness, Brinell | 20.0 °C | 130.0 [-] Show Material materials with Hardness, Brinell of 130.0 [-] | T652 | WL 3.1254-1 | Forging | Transverse |
20.0 °C | 130.0 [-] Show Material materials with Hardness, Brinell of 130.0 [-] | T652 | WL 3.1254-1 | Forging | ||
Plane-Strain Fracture Toughnes | 20.0 °C | 19.9 - 31.6 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 19.9 - 31.6 MPa·√m | T652 | WL 3.1254-1 | ||
20.0 °C | 19.9 - 24.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 19.9 - 24.0 MPa·√m | T652 | WL 3.1254-1 | |||
20.0 °C | 19.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 19.9 MPa·√m | T652 | WL 3.1254-1 | |||
20.0 °C | 24.0 - 31.6 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 24.0 - 31.6 MPa·√m | T652 | WL 3.1254-1 | |||
20.0 °C | 24.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 24.0 MPa·√m | T652 | WL 3.1254-1 | |||
20.0 °C | 31.6 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 31.6 MPa·√m | T652 | WL 3.1254-1 | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||||
Shear modulus | 26.0 - 27.5 GPa Show Material materials with Shear modulus of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||||
Tensile strength | 20.0 °C | 395.0 MPa Show Material materials with Tensile strength of 395.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse |
20.0 °C | 400.0 MPa Show Material materials with Tensile strength of 400.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 405.0 MPa Show Material materials with Tensile strength of 405.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 405.0 MPa Show Material materials with Tensile strength of 405.0 MPa | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 415.0 MPa Show Material materials with Tensile strength of 415.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 415.0 MPa Show Material materials with Tensile strength of 415.0 MPa | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 420.0 MPa Show Material materials with Tensile strength of 420.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 420.0 MPa Show Material materials with Tensile strength of 420.0 MPa | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 425.0 MPa Show Material materials with Tensile strength of 425.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 430.0 MPa Show Material materials with Tensile strength of 430.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 430.0 MPa Show Material materials with Tensile strength of 430.0 MPa | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 435.0 MPa Show Material materials with Tensile strength of 435.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 435.0 MPa Show Material materials with Tensile strength of 435.0 MPa | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 440.0 MPa Show Material materials with Tensile strength of 440.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse | |
20.0 °C | 440.0 MPa Show Material materials with Tensile strength of 440.0 MPa | T652 | WL 3.1254-1 | Forging | ||
20.0 °C | 450.0 MPa Show Material materials with Tensile strength of 450.0 MPa | T652 | WL 3.1254-1 | Forging | Transverse |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Melting point | 500.0 - 650.0 °C Show Material materials with Melting point of 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Specific heat capacity | 816.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Thermal conductivity | 112.0 - 251.0 W/(m·K) Show Material materials with Thermal conductivity of 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Electrical
Property | Value | Comment |
---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m Show Material materials with Electrical resistivity of 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Chromium | 0.1 Show Material materials with Chromium of 0.1 | T652 | WL 3.1254-1 | Forging |
Copper | 3.9 - 5.0 % Show Material materials with Copper of 3.9 - 5.0 % | T652 | WL 3.1254-1 | Forging |
Iron | 0.3 Show Material materials with Iron of 0.3 | T652 | WL 3.1254-1 | Forging |
Magnesium | 0.2 - 0.8 % Show Material materials with Magnesium of 0.2 - 0.8 % | T652 | WL 3.1254-1 | Forging |
Manganese | 0.4 - 1.2 % Show Material materials with Manganese of 0.4 - 1.2 % | T652 | WL 3.1254-1 | Forging |
Silicon | 0.5 - 1.2 % Show Material materials with Silicon of 0.5 - 1.2 % | T652 | WL 3.1254-1 | Forging |
Titanium | 0.15 Show Material materials with Titanium of 0.15 | T652 | WL 3.1254-1 | Forging |
Zinc | 0.25 Show Material materials with Zinc of 0.25 | T652 | WL 3.1254-1 | Forging |
Technological properties
Property | ||
---|---|---|
Workability | Moderate Workability |