General
Property | Value | Comment |
---|---|---|
Density | 2.7 - 2.85 g/cm³ Show Material materials with Density of 2.7 - 2.85 g/cm³ | Typical for Wrought 7000 Series Aluminium |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 69.0 - 72.0 GPa Show Material materials with Elastic modulus of 69.0 - 72.0 GPa | Typical for Wrought 7000 Series Aluminium | ||||
Elongation | 20.0 °C | 4.0 % Show Material materials with Elongation of 4.0 % | T74 | WL 3.4354-1 | Forging | Transverse |
20.0 °C | 5.0 % Show Material materials with Elongation of 5.0 % | T74 | WL 3.4354-1 | Forging | Transverse | |
20.0 °C | 6.0 % Show Material materials with Elongation of 6.0 % | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 7.0 % Show Material materials with Elongation of 7.0 % | T74 | WL 3.4354-1 | Forging, Rod, Profile | ||
20.0 °C | 8.0 % Show Material materials with Elongation of 8.0 % | T74 | WL 3.4354-1 | Profile, Forging | ||
Hardness, Brinell | 20.0 °C | 140.0 [-] Show Material materials with Hardness, Brinell of 140.0 [-] | T74 | WL 3.4354-1 | Forging, Rod | Transverse |
20.0 °C | 140.0 [-] Show Material materials with Hardness, Brinell of 140.0 [-] | T74 | WL 3.4354-1 | Forging, Rod, Profile | ||
Plane-Strain Fracture Toughnes | 20.0 °C | 22.0 - 38.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 38.0 MPa·√m | T74 | WL 3.4354-1 | Rod | |
20.0 °C | 22.0 - 29.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 29.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 22.0 - 36.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 36.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 22.0 - 25.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 25.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 22.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 22.0 - 42.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 42.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 22.0 - 28.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 28.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 24.0 - 31.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 24.0 - 31.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 24.0 - 32.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 24.0 - 32.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 24.0 - 26.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 24.0 - 26.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 24.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 24.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 25.0 - 40.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 25.0 - 40.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 25.0 - 28.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 25.0 - 28.0 MPa·√m | T74 | WL 3.4354-1 | Forging, Rod | ||
20.0 °C | 25.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 25.0 MPa·√m | T74 | WL 3.4354-1 | Forging, Rod | ||
20.0 °C | 25.0 - 26.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 25.0 - 26.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 25.0 - 38.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 25.0 - 38.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 25.0 - 29.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 25.0 - 29.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 25.0 - 36.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 25.0 - 36.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 25.0 - 42.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 25.0 - 42.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 26.0 - 31.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 26.0 - 31.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 26.0 - 32.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 26.0 - 32.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 26.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 26.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 26.0 - 40.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 26.0 - 40.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 26.0 - 28.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 26.0 - 28.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 28.0 - 40.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 28.0 - 40.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 28.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 28.0 MPa·√m | T74 | WL 3.4354-1 | Forging, Rod | ||
20.0 °C | 28.0 - 38.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 28.0 - 38.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 28.0 - 29.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 28.0 - 29.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 28.0 - 36.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 28.0 - 36.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 28.0 - 42.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 28.0 - 42.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 29.0 - 38.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 29.0 - 38.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 29.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 29.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 29.0 - 36.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 29.0 - 36.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 29.0 - 42.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 29.0 - 42.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 31.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 31.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 31.0 - 32.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 31.0 - 32.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 32.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 32.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 36.0 - 38.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 36.0 - 38.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 36.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 36.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 36.0 - 42.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 36.0 - 42.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 38.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 38.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 38.0 - 42.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 38.0 - 42.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
20.0 °C | 40.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 40.0 MPa·√m | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 42.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 42.0 MPa·√m | T74 | WL 3.4354-1 | Rod | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 7000 Series Aluminium | ||||
Shear modulus | 26.4 - 27.1 GPa Show Material materials with Shear modulus of 26.4 - 27.1 GPa | Typical for Wrought 7000 Series Aluminium | ||||
Tensile strength | 20.0 °C | 440.0 MPa Show Material materials with Tensile strength of 440.0 MPa | T74 | WL 3.4354-1 | Forging | Transverse |
20.0 °C | 450.0 MPa Show Material materials with Tensile strength of 450.0 MPa | T74 | WL 3.4354-1 | Forging | Transverse | |
20.0 °C | 460.0 MPa Show Material materials with Tensile strength of 460.0 MPa | T74 | WL 3.4354-1 | Forging, Rod | Transverse | |
20.0 °C | 460.0 MPa Show Material materials with Tensile strength of 460.0 MPa | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 470.0 MPa Show Material materials with Tensile strength of 470.0 MPa | T74 | WL 3.4354-1 | Forging, Rod | Transverse | |
20.0 °C | 470.0 MPa Show Material materials with Tensile strength of 470.0 MPa | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 480.0 MPa Show Material materials with Tensile strength of 480.0 MPa | T74 | WL 3.4354-1 | Forging | Transverse | |
20.0 °C | 480.0 MPa Show Material materials with Tensile strength of 480.0 MPa | T74 | WL 3.4354-1 | Forging | ||
20.0 °C | 490.0 MPa Show Material materials with Tensile strength of 490.0 MPa | T74 | WL 3.4354-1 | Forging | Transverse | |
20.0 °C | 500.0 MPa Show Material materials with Tensile strength of 500.0 MPa | T74 | WL 3.4354-1 | Forging | Transverse | |
20.0 °C | 500.0 MPa Show Material materials with Tensile strength of 500.0 MPa | T74 | WL 3.4354-1 | Profile, Forging | ||
20.0 °C | 510.0 MPa Show Material materials with Tensile strength of 510.0 MPa | T74 | WL 3.4354-1 | Forging, Profile, Rod | ||
20.0 °C | 530.0 MPa Show Material materials with Tensile strength of 530.0 MPa | T74 | WL 3.4354-1 | Rod |
Thermal
Property | Value | Comment |
---|---|---|
Coefficient of thermal expansion | 2.1e-05 - 2.4e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1e-05 - 2.4e-05 1/K | Typical for Wrought 7000 Series Aluminium |
Melting point | 465.0 - 655.0 °C Show Material materials with Melting point of 465.0 - 655.0 °C | Typical for Wrought 7000 Series Aluminium |
Specific heat capacity | 795.0 - 1050.0 J/(kg·K) Show Material materials with Specific heat capacity of 795.0 - 1050.0 J/(kg·K) | Typical for Wrought 7000 Series Aluminium |
Thermal conductivity | 121.0 - 170.0 W/(m·K) Show Material materials with Thermal conductivity of 121.0 - 170.0 W/(m·K) | Typical for Wrought 7000 Series Aluminium |
Electrical
Property | Value | Comment |
---|---|---|
Electrical conductivity | 18000000.0 - 34000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 34000000.0 S/m | Typical for Wrought 7000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5.6e-08 Ω·m Show Material materials with Electrical resistivity of 2.9e-08 - 5.6e-08 Ω·m | Typical for Wrought 7000 Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Chromium | 0.1 - 0.25 % Show Material materials with Chromium of 0.1 - 0.25 % | T74 | WL 3.4354-1 | Forging, Profile, Rod |
Copper | 0.6 - 1.3 % Show Material materials with Copper of 0.6 - 1.3 % | T74 | WL 3.4354-1 | Forging, Profile, Rod |
Iron | 0.2 Show Material materials with Iron of 0.2 | T74 | WL 3.4354-1 | Forging, Profile, Rod |
Magnesium | 2.1 - 2.9 % Show Material materials with Magnesium of 2.1 - 2.9 % | T74 | WL 3.4354-1 | Forging, Profile, Rod |
Manganese | 0.1 Show Material materials with Manganese of 0.1 | T74 | WL 3.4354-1 | Forging, Profile, Rod |
Silicon | 0.2 Show Material materials with Silicon of 0.2 | T74 | WL 3.4354-1 | Forging, Profile, Rod |
Silver | 0.25 - 0.4 % Show Material materials with Silver of 0.25 - 0.4 % | T74 | WL 3.4354-1 | Forging, Profile, Rod |
Titanium | 0.2 Show Material materials with Titanium of 0.2 | T74 | WL 3.4354-1 | Forging, Profile, Rod |
Zinc | 5.5 - 6.5 % Show Material materials with Zinc of 5.5 - 6.5 % | T74 | WL 3.4354-1 | Forging, Profile, Rod |
Technological properties
Property | ||
---|---|---|
Brazing | Excellent |