EN 573-3 Grade AW-1050A H112

Want to keep this datasheet? Save it now in your required format

Description

Food safe aluminum.

Related Standards

Equivalent Materials

Ashby charts

See where EN 573-3 Grade AW-1050A H112 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.7 g/cm³ at 20 °C

Dimension

Dimensions

Dicke

Mechanical

Elastic modulus

E

70 GPa at -270 °C

Show 1000 Series materials with Elastic modulus of 70 GPa at -270 °C

Hide chart

Elongation

A

20 - 25 % at 20 °C

Show 1000 Series materials with Elongation of 20 - 25 % at 20 °C

Elongation A100

A100

20 - 25 % at 20 °C

Show 1000 Series materials with Elongation A100 of 20 - 25 % at 20 °C

Elongation A50

A50

20 - 23 % at 20 °C

Show 1000 Series materials with Elongation A50 of 20 - 23 % at 20 °C

Elongation A50, transverse

A50,trans

20 % at 20 °C

Show 1000 Series materials with Elongation A50, transverse of 20 % at 20 °C

Elongation, transverse

A

20 % at 20 °C

Show 1000 Series materials with Elongation, transverse of 20 % at 20 °C

Hardness, Brinell

HB

20 - 23 [-] at 20 °C

Show 1000 Series materials with Hardness, Brinell of 20 - 23 [-] at 20 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Show 1000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 20 °C

Typical for Wrought 1000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Show 1000 Series materials with Poisson's ratio of 0.33 [-] at 20 °C

Shear modulus

G

25 - 26.5 GPa at 20 °C

Show 1000 Series materials with Shear modulus of 25 - 26.5 GPa at 20 °C

Tensile strength

Rm

60 - 75 MPa at 20 °C

Show 1000 Series materials with Tensile strength of 60 - 75 MPa at 20 °C

Tensile strength, transverse

Rm,trans

70 - 75 MPa at 20 °C

Show 1000 Series materials with Tensile strength, transverse of 70 - 75 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

20 - 30 MPa at 20 °C

Show 1000 Series materials with Yield strength Rp0.2 of 20 - 30 MPa at 20 °C

Yield strength Rp0.2, transverse

Rp0.2,trans

25 - 30 MPa at 20 °C

Show 1000 Series materials with Yield strength Rp0.2, transverse of 25 - 30 MPa at 20 °C

Yield strength Rp1.0

Rp1.0

30 MPa at -270 °C

Show 1000 Series materials with Yield strength Rp1.0 of 30 MPa at -270 °C

Unlock all property charts

Thermal

Coefficient of thermal expansion

α

2.17E-5 1/K at -50 °C

Unlock all property charts

Melting point

Tm

646 - 657 °C

Specific heat capacity

cp

899 - 900 J/(kg·K) at 20 °C

Thermal conductivity

λ

210 - 229 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

3.40E+7 - 3.60E+7 S/m at 20 °C

Electrical resistivity

ρel

2.78E-8 - 2.94E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Other

-

each 0.03

Al

99.5 %

Fe

0.4 %

Si

0.1 - 0.25 %

B

0.05 %

More

Technological properties

Anodizing

decorative: gut (EQ: sehr gut), Protective: very good

Brazing

hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good

Corrosion properties

Seawater: acceptable, weathering: good

Workability

Bending / Spinning (cold): very good / very good, Impact extrusion (cold): very good, Deep drawing / upsetting (Condition) very good (H14) / very good (H12)

This material data has been provided by WIAM,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.