General
Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.77 g/cm³ Show Material materials with Density of 2.77 g/cm³ | O | |
2.78 g/cm³ Show Material materials with Density of 2.78 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 | |
3.0 g/cm³ Show Material materials with Density of 3.0 g/cm³ | O |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Bending Fatigue Strength | 90.0 MPa Show Material materials with Bending Fatigue Strength of 90.0 MPa | O | AA Standards | |
Elastic modulus | 72.4 GPa Show Material materials with Elastic modulus of 72.4 GPa | O | ||
73.0 GPa Show Material materials with Elastic modulus of 73.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 | ||
Elongation | 10.0 % Show Material materials with Elongation of 10.0 % | O | AA Standards, ASTM B209, ASTM B241 | A100 |
12.0 % Show Material materials with Elongation of 12.0 % | O | AA Standards, ASTM B209, ASTM B241 | A50 | |
14.0 % Show Material materials with Elongation of 14.0 % | O | AA Standards, ASTM B211 | A100 | |
16.0 % Show Material materials with Elongation of 16.0 % | O | AA Standards, ASTM B211 | A50 | |
16.0 % Show Material materials with Elongation of 16.0 % | O | |||
20.0 % Show Material materials with Elongation of 20.0 % | O | AA Standards | A50 | |
20.0 % Show Material materials with Elongation of 20.0 % | O | AA Standards | A100 | |
20.0 % Show Material materials with Elongation of 20.0 % | O | |||
Hardness, Brinell | 47.0 [-] Show Material materials with Hardness, Brinell of 47.0 [-] | O | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | O | ||
Shear modulus | 26.0 - 27.5 GPa Show Material materials with Shear modulus of 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||
Tensile strength | 185.0 MPa Show Material materials with Tensile strength of 185.0 MPa | O | AA Standards | |
190.0 MPa Show Material materials with Tensile strength of 190.0 MPa | O | |||
220.0 MPa Show Material materials with Tensile strength of 220.0 MPa | O | AA Standards, ASTM B209, ASTM B210 | ||
240.0 MPa Show Material materials with Tensile strength of 240.0 MPa | O | AA Standards, ASTM B211, ASTM B241, ASTM B316 | ||
Yield strength | 75.0 MPa Show Material materials with Yield strength of 75.0 MPa | O | AA Standards | RP02 |
75.0 MPa Show Material materials with Yield strength of 75.0 MPa | O | |||
95.0 MPa Show Material materials with Yield strength of 95.0 MPa | O | AA Standards, ASTM B209 | RP02 | |
98.0 MPa Show Material materials with Yield strength of 98.0 MPa | O | |||
100.0 MPa Show Material materials with Yield strength of 100.0 MPa | O | AA Standards, ASTM B210 | RP02 | |
130.0 MPa Show Material materials with Yield strength of 130.0 MPa | O | AA Standards, ASTM B241 | RP02 |
Thermal
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Coefficient of thermal expansion | 2.29e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.29e-05 1/K | O | ||
2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | O | |||
20 °C | 2.3199999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3199999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 | |
100 °C | 2.3199999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3199999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 | |
Melting point | 500.0 °C Show Material materials with Melting point of 500.0 °C | O | ||
505.0 - 635.0 °C Show Material materials with Melting point of 505.0 - 635.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 | ||
Specific heat capacity | 870.0 J/(kg·K) Show Material materials with Specific heat capacity of 870.0 J/(kg·K) | O | ||
875.0 J/(kg·K) Show Material materials with Specific heat capacity of 875.0 J/(kg·K) | O | |||
Thermal conductivity | 120.0 W/(m·K) Show Material materials with Thermal conductivity of 120.0 W/(m·K) | O | ||
121.0 - 193.0 W/(m·K) Show Material materials with Thermal conductivity of 121.0 - 193.0 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 | ||
190.0 W/(m·K) Show Material materials with Thermal conductivity of 190.0 W/(m·K) | O |
Electrical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Electrical conductivity | 17000000.0 - 29000000.0 S/m Show Material materials with Electrical conductivity of 17000000.0 - 29000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 | |
29000000 S/m Show Material materials with Electrical conductivity of 29000000 S/m | O | Typical/derived value | ||
Electrical resistivity | 3.4e-08 Ω·m Show Material materials with Electrical resistivity of 3.4e-08 Ω·m | O | Typical value | |
3.45e-08 - 5.88e-08 Ω·m Show Material materials with Electrical resistivity of 3.45e-08 - 5.88e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 | ||
Specific Electrical conductivity | 50.0 % IACS Show Material materials with Specific Electrical conductivity of 50.0 % IACS | O | Typical value |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 90.7 - 94.7 % Show Material materials with Aluminium of 90.7 - 94.7 % | O | |
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 |
Copper | 3.8 - 4.9 % Show Material materials with Copper of 3.8 - 4.9 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 |
Iron | 0.50 % Show Material materials with Iron of 0.50 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 |
0.5 % Show Material materials with Iron of 0.5 % | O | ||
Magnesium | 1.2 - 1.8 % Show Material materials with Magnesium of 1.2 - 1.8 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 |
Manganese | 0.3 - 0.9 % Show Material materials with Manganese of 0.3 - 0.9 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 |
Other | 0.15 % Show Material materials with Other of 0.15 % | O | |
Silicon | 0.5 % Show Material materials with Silicon of 0.5 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B316 |
Zirconium | 0.2 % Show Material materials with Zirconium of 0.2 % | O |
Technological properties
Property | ||
---|---|---|
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: Betriebsschäden in Gebieten mit Zugspannungen quer zur Kornstruktur, Eingeschränkte Schäden an Laborproben (T4,T3, T351, T3510, T3511), d (T6, T861, T81, T851, T8510, T8511), general: sufficient, in principle it should be protected | |
General machinability | General: poor (O), good to acceptable | |
Workability | general (condition): poor(T4, T3, T351, T3510, T3511, T6), not suitable (T361, T861, T81, T851, T8510, T8511) |