AA Standards Grade 1100 O

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey,MakeItFrom.com,ASM Handbook Volume 2 Properties and Selection: Nonferrous Alloys and Special-Purpose Materials,Matmatch,WroughtAl_ElectricalResistivity.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

23.0 °C

2.71 - 2.8 g/cm³

Show Material materials with Density of 2.71 - 2.8 g/cm³

Mechanical

PropertyTemperatureValueComment

Bending Fatigue Strength

23.0 °C

35 MPa

Show Material materials with Bending Fatigue Strength of 35 MPa

Elastic modulus

23.0 °C

69 GPa

Show Material materials with Elastic modulus of 69 GPa

Elongation

-195.0 °C

50 %

Show Material materials with Elongation of 50 %

Elongation in 50 mm

-80.0 °C

43 %

Show Material materials with Elongation of 43 %

Elongation in 50 mm

0.0 °C

40 %

Show Material materials with Elongation of 40 %

Elongation in 50 mm

23.0 °C

31 - 40 %

Show Material materials with Elongation of 31 - 40 %

Elongation in 50 mm

24.0 °C

40 %

Show Material materials with Elongation of 40 %

Elongation in 50 mm

100.0 °C

45 %

Show Material materials with Elongation of 45 %

Elongation in 50 mm

150.0 °C

55 %

Show Material materials with Elongation of 55 %

Elongation in 50 mm

205.0 °C

65 %

Show Material materials with Elongation of 65 %

Elongation in 50 mm

260.0 °C

75 %

Show Material materials with Elongation of 75 %

Elongation in 50 mm

315.0 °C

80 %

Show Material materials with Elongation of 80 %

Elongation in 50 mm

370.0 °C

85 %

Show Material materials with Elongation of 85 %

Elongation in 50 mm

Elongation A100

23.0 °C

22 - 42 %

Show Material materials with Elongation A100 of 22 - 42 %

Elongation A50

23.0 °C

15 - 35 %

Show Material materials with Elongation A50 of 15 - 35 %

Fatigue strength

23.0 °C

34 MPa

Show Material materials with Fatigue strength of 34 MPa

for 5x10⁸ cycles

Hardness, Brinell

23.0 °C

23 [-]

Show Material materials with Hardness, Brinell of 23 [-]

500 kg load, 10 mm ball

Plane-Strain Fracture Toughnes

23.0 °C

22 - 35 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m

Typical for Wrought 1000 Series Aluminium

Poisson's ratio

23.0 °C

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Shear modulus

23.0 °C

25 - 26 GPa

Show Material materials with Shear modulus of 25 - 26 GPa

Shear strength

23.0 °C

60 MPa

Show Material materials with Shear strength of 60 MPa

Tensile strength

-195.0 °C

172 MPa

Show Material materials with Tensile strength of 172 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80.0 °C

103 MPa

Show Material materials with Tensile strength of 103 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

0.0 °C

97 MPa

Show Material materials with Tensile strength of 97 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

23.0 °C

75 - 110 MPa

Show Material materials with Tensile strength of 75 - 110 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

24.0 °C

90 MPa

Show Material materials with Tensile strength of 90 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100.0 °C

70 MPa

Show Material materials with Tensile strength of 70 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

150.0 °C

55 MPa

Show Material materials with Tensile strength of 55 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

205.0 °C

40 MPa

Show Material materials with Tensile strength of 40 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260.0 °C

28 MPa

Show Material materials with Tensile strength of 28 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

315.0 °C

20 MPa

Show Material materials with Tensile strength of 20 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

370.0 °C

14 MPa

Show Material materials with Tensile strength of 14 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Unlock all property charts

Yield strength

23.0 °C

29 - 34 MPa

Show Material materials with Yield strength of 29 - 34 MPa

Yield strength Rp0.2

-196.0 °C

41 MPa

Show Material materials with Yield strength Rp0.2 of 41 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-80.0 °C

38 MPa

Show Material materials with Yield strength Rp0.2 of 38 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

-28.0 °C

34 MPa

Show Material materials with Yield strength Rp0.2 of 34 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

23.0 °C

20 - 35 MPa

Show Material materials with Yield strength Rp0.2 of 20 - 35 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

24.0 °C

34 MPa

Show Material materials with Yield strength Rp0.2 of 34 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

100.0 °C

32 MPa

Show Material materials with Yield strength Rp0.2 of 32 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

149.0 °C

29 MPa

Show Material materials with Yield strength Rp0.2 of 29 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

204.0 °C

24 MPa

Show Material materials with Yield strength Rp0.2 of 24 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

260.0 °C

18 MPa

Show Material materials with Yield strength Rp0.2 of 18 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

316.0 °C

14 MPa

Show Material materials with Yield strength Rp0.2 of 14 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

371.0 °C

11 MPa

Show Material materials with Yield strength Rp0.2 of 11 MPa

up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture

Unlock all property charts

Thermal

PropertyTemperatureValue

Coefficient of thermal expansion

20.0 °C

2.36E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.36E-5 1/K

23.0 °C

2.4E-5 - 2.66E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.4E-5 - 2.66E-5 1/K

100.0 °C

2.36E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.36E-5 1/K

Unlock all property charts

Melting point

640 - 655 °C

Show Material materials with Melting point of 640 - 655 °C

Specific heat capacity

23.0 °C

900 - 904 J/(kg·K)

Show Material materials with Specific heat capacity of 900 - 904 J/(kg·K)

Thermal conductivity

23.0 °C

218 - 222 W/(m·K)

Show Material materials with Thermal conductivity of 218 - 222 W/(m·K)

Electrical

PropertyTemperatureValueComment

Electrical conductivity

23.0 °C

3.30E+7 - 3.40E+7 S/m

Show Material materials with Electrical conductivity of 3.30E+7 - 3.40E+7 S/m

Typical value

Electrical resistivity

23.0 °C

2.9E-8 - 3.03E-8 Ω·m

Show Material materials with Electrical resistivity of 2.9E-8 - 3.03E-8 Ω·m

Typical value

Specific Electrical conductivity

59 % IACS

Show Material materials with Specific Electrical conductivity of 59 % IACS

Typical/Derived value

Chemical properties

PropertyValueComment

Aluminium

99 - 100 %

Show Material materials with Aluminium of 99 - 100 %

Copper

0.05 - 0.2 %

Show Material materials with Copper of 0.05 - 0.2 %

Iron

0 - 1 %

Show Material materials with Iron of 0 - 1 %

Manganese

0 - 0.05 %

Show Material materials with Manganese of 0 - 0.05 %

Other

0 - 0.15 %

Show Material materials with Other of 0 - 0.15 %

each 0.05, total 0.15, Si + Fe < 0.95

Silicon

0 - 1 %

Show Material materials with Silicon of 0 - 1 %

Zinc

0 - 0.1 %

Show Material materials with Zinc of 0 - 0.1 %

Technological properties

Property
Brazing

general: possible with commercial processes and methods

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: not suitable (O, H12), poor (H14, H16, H18)

Workability

general (condition): good (O, H12, H14), acceptable (H16), poor(H18)