RADILON A RV350W 333 BK A

Alternative and trade names
PA66-T GF35, PA66-GF35
Want to keep this datasheet? Save it now in your required format

Description

PA66 35% glass fiber reinforced injection moulding grade, heat stabilized. Suitable for parts requiring: high stiffness, good mechanical resistance and excellent heat ageing properties retention.

This material data has been provided by Radici Group.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting StandardThickness

Density

1.4 g/cm³

Show Supplier Material materials with Density of 1.4 g/cm³

dry

ISO 1183

Moisture absorption

1.5 %

Show Supplier Material materials with Moisture absorption of 1.5 %

50% RH

ISO 62

2 mm

Water absorption

5.5 %

Show Supplier Material materials with Water absorption of 5.5 %

ISO 62

2 mm

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

8 GPa

Show Supplier Material materials with Elastic modulus of 8 GPa

50%RH

ISO 527-2/1A

1mm/min

11 GPa

Show Supplier Material materials with Elastic modulus of 11 GPa

dry

ISO 527-2/1A

1mm/min

Elongation

3 %

Show Supplier Material materials with Elongation of 3 %

dry

ISO 527-2/1A

5mm/min

5 %

Show Supplier Material materials with Elongation of 5 %

50%RH

ISO 527-2/1A

5mm/min

Flexural modulus

7 GPa

Show Supplier Material materials with Flexural modulus of 7 GPa

50%RH

ISO 178

2mm/min

10 GPa

Show Supplier Material materials with Flexural modulus of 10 GPa

dry

ISO 178

2mm/min

Flexural strength

230 MPa

Show Supplier Material materials with Flexural strength of 230 MPa

50%RH

ISO 178

2mm/min

285 MPa

Show Supplier Material materials with Flexural strength of 285 MPa

dry

ISO 178

2mm/min

Impact strength, Charpy notched

-30 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²

dry

ISO 179/1eA

23 °C

12 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m²

dry

ISO 179/1eA

23 °C

19 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 19 kJ/m²

50%RH

ISO 179/1eA

Impact strength, Charpy unnotched

-30 °C

70 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 70 kJ/m²

dry

ISO 179/1eU

23 °C

85 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 85 kJ/m²

dry

ISO 179/1eU

23 °C

95 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 95 kJ/m²

50%RH

ISO 179/1eU

Unlock all property charts

Tensile strength

125 MPa

Show Supplier Material materials with Tensile strength of 125 MPa

50%RH

ISO 527-2/1A

5mm/min

190 MPa

Show Supplier Material materials with Tensile strength of 190 MPa

dry

ISO 527-2/1A

5mm/min

Thermal

PropertyValueTesting StandardThicknessPressureComment

Coefficient of thermal expansion

2.4e-05 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 2.4e-05 1/K

ISO 11359-1/-2

23°C-55°C

9.7e-05

Show Supplier Material materials with Coefficient of thermal expansion of 9.7e-05

ISO 11359-1/-2

23°C-55°C, Transverse

Glow Wire Ignition Temperature

700 °C

Show Supplier Material materials with Glow Wire Ignition Temperature of 700 °C

IEC 60695-2-12

2 mm

Heat deflection temperature

250 °C

Show Supplier Material materials with Heat deflection temperature of 250 °C

ISO 75/2Af

2 MPa

Melting point

260 °C

Show Supplier Material materials with Melting point of 260 °C

ISO 11357-1/-3

10°C/min

Vicat softening temperature

250 °C

Show Supplier Material materials with Vicat softening temperature of 250 °C

ISO 306

50°C/h 50N

Flammability

for 0.8mm, HB UL94

Electrical

PropertyValueConditionTesting StandardComment

Surface resistivity

1e+10 Ω/sq

Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq

50%RH

IEC 60093

500V

1e+12 Ω/sq

Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq

dry

IEC 60093

500V

Volume resistivity

1e+13 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm

50%RH

IEC 60093

500V

1e+15 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+15 Ω·cm

dry

IEC 60093

500V

Rheological Properties

PropertyValueConditionTesting StandardComment

Shrinkage

0.3 %

Show Supplier Material materials with Shrinkage of 0.3 %

dry

ISO 294-4

1 %

Show Supplier Material materials with Shrinkage of 1 %

dry

ISO 294-4

Transverse

Technological properties

Property
Certifications

RoHS 2011/65/UE

Color

Black

Fillers

35% Glass Fiber

Processing methods

Injection Molding