RADILON AESTUS T1 RV300FC 306K BK

Alternative and trade names
PPA-GF30, PPA-T GF30
Want to keep this datasheet? Save it now in your required format

Description

PPA injection moulding grade 30% glass fibre reinforced with high glass transition temperature and high melting point. Black colour.

Suitable for parts requiring high stiffness and strength. Appropriate for foodstuff contact, especially for kitchen tools.

This material data has been provided by Radici Group.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting StandardThickness

Density

1.44 g/cm³

Show Supplier Material materials with Density of 1.44 g/cm³

dry

ISO 1183

Moisture absorption

1.5 %

Show Supplier Material materials with Moisture absorption of 1.5 %

50% RH

ISO 62

2 mm

Water absorption

0.2 %

Show Supplier Material materials with Water absorption of 0.2 %

ISO 62

2 mm

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

12 GPa

Show Supplier Material materials with Elastic modulus of 12 GPa

dry

ISO 527-2/1A

1mm/min

12 GPa

Show Supplier Material materials with Elastic modulus of 12 GPa

50%RH

ISO 527-2/1A

1mm/min

Elongation

2 %

Show Supplier Material materials with Elongation of 2 %

dry

ISO 527-2/1A

5mm/min

2 %

Show Supplier Material materials with Elongation of 2 %

50%RH

ISO 527-2/1A

5mm/min

Flexural modulus

10 GPa

Show Supplier Material materials with Flexural modulus of 10 GPa

dry

ISO 178

2mm/min

Flexural strength

250 MPa

Show Supplier Material materials with Flexural strength of 250 MPa

dry

ISO 178

2mm/min

Impact strength, Charpy notched

-30 °C

7 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 7 kJ/m²

dry

ISO 179/1eA

23 °C

8 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 8 kJ/m²

dry

ISO 179/1eA

23 °C

8 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 8 kJ/m²

50%RH

ISO 179/1eA

Impact strength, Charpy unnotched

-30 °C

45 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 45 kJ/m²

dry

ISO 179/1eU

23 °C

50 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 50 kJ/m²

dry

ISO 179/1eU

Unlock all property charts

Tensile strength

145 MPa

Show Supplier Material materials with Tensile strength of 145 MPa

50%RH

ISO 527-2/1A

5mm/min

160 MPa

Show Supplier Material materials with Tensile strength of 160 MPa

dry

ISO 527-2/1A

5mm/min

Thermal

PropertyValueTesting StandardPressureComment

Heat deflection temperature

290 °C

Show Supplier Material materials with Heat deflection temperature of 290 °C

ISO 75/2Af

2 MPa

Melting point

325 °C

Show Supplier Material materials with Melting point of 325 °C

ISO 11357-1/-3

10°C/min

Flammability

Class: HB ,method: UL 94, and thickness tested (mm): 0.8

Rheological Properties

PropertyValueConditionTesting StandardComment

Shrinkage

0.3 %

Show Supplier Material materials with Shrinkage of 0.3 %

dry

ISO 294-4

0.8 %

Show Supplier Material materials with Shrinkage of 0.8 %

dry

ISO 294-4

Transverse

Technological properties

Property
Certifications

RoHS 2011/65/UE, Food and Water Contact (please get in touch with Radici Group): KTW guidlines and DVGW-standard W270 (11/2007), ACS positive lists include the circular DGC/VS4 n°2000/232 dated 27 april 2000

Color

Black

Fillers

30% Glass Fiber

Processing methods

Injection Molding