TORZEN Marathon G3500XHL BK20

Alternative and trade names
PA66-GF35

Want to keep this datasheet? Save it now in your required format

Description

PA66 35% glass fibre reinforced injection moulding grade with enhanced thermal resistance in contact with hot air. High improvement of mechanical properties retention versus standard polyamide 66 after heat ageing. Black colour.

Suitable for parts requiring high stiffness, good mechanical resistance and good heat ageing properties retention.

Equivalent Materials

PA66-GF35

This material data has been provided by Radici Group.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

RADICIGROUP HIGH PERFORMANCE POLYMERS

MANUFACTURER

Additional services:

CAE Service: Customized technical support contributing to the success of innovative projects, including metal replacement applications, realized using RADILON®, RADITECK®, RADISTRONG®, RADIFLAM® and RADITER® engineering plastics. This is what RadiciGroup High Performance Polymers can offer its customers, thanks to its state-of-the-art computer-aided engineering (CAE) virtual simulation tools and the experience of its technical specialists.

Materials by this supplier

RADILON A CP300K 333 BK

RADILON AESTUS T1 RV300FC 306K BK

RADILON NeXTreme RV500HHR 3800 BK

RADITER B RV300 100 NT

RADILON A RV500RW 339 BK

See all materials by this supplier

Use cases

Webinar: Metal Replacement with Engineering Polymers

Properties

General

Property	Temperature	Value	Condition	Testing Standard	Thickness	Comment
Density		1.42 g/cm³ Show Supplier Material materials with Density of 1.42 g/cm³	dry	ISO 1183
Moisture absorption	23 °C	1.7 % Show Supplier Material materials with Moisture absorption of 1.7 %	50%RH	ISO 62	2 mm
Water absorption		1.1 % Show Supplier Material materials with Water absorption of 1.1 %		ISO 62	2 mm	24h immersion at 23°C
		2 % Show Supplier Material materials with Water absorption of 2 %		ISO 62		1mm

Mechanical

Property	Temperature	Value	Condition	Testing Standard	Comment
Elastic modulus		11.5 GPa Show Supplier Material materials with Elastic modulus of 11.5 GPa	dry	ISO 527-2/1A	1mm/min
Elongation		3 % Show Supplier Material materials with Elongation of 3 %	dry	ISO 527-2/1A	5mm/min
Flexural modulus		11 GPa Show Supplier Material materials with Flexural modulus of 11 GPa	dry	ISO 178	2mm/min
Flexural strength		310 MPa Show Supplier Material materials with Flexural strength of 310 MPa	dry	ISO 178	2mm/min
Impact strength, Charpy notched	23 °C	14 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 14 kJ/m²	dry	ISO 179/1eA
Impact strength, Charpy unnotched		79 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 79 kJ/m²	dry	ISO 179/1eU	23°C
Impact strength, Izod unnotched	23 °C	14 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 14 kJ/m²	dry	ISO 180/1U
Tensile strength		210 MPa Show Supplier Material materials with Tensile strength of 210 MPa	dry	ISO 527-2/1A	5mm/min

Thermal

Property	Value	Testing Standard	Comment
Heat deflection temperature	250 °C Show Supplier Material materials with Heat deflection temperature of 250 °C	ISO 75/2Af	1.80 MPa
	260 °C Show Supplier Material materials with Heat deflection temperature of 260 °C	ISO 75/2Bf	0.45 MPa
Melting point	261 °C Show Supplier Material materials with Melting point of 261 °C	ISO 11357-1/-3	10°C/min
Flammability	Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 \| Automotive Interior Flammability(mm/min): <100,method: ISO 3795 and thickness tested (mm): 2

Technological properties

Property
Additives	Release agent
Certifications	RoHS 2011/65/UE
Color	Black
Features	Heat Stabilized
Fillers	35% Glass Fiber
Processing methods	Injection Molding