RADILON NeXTreme RV500HHR 3800 BK

Alternative and trade names
PA-GF50
Want to keep this datasheet? Save it now in your required format

Description

High Temperature polyamide injection moulding grade, 50% glass fibre reinforced. Superior thermal resistance in contact with hot air. Black colour.

Suitable for demanding mechanical applications in very severe temperature conditions, where the parts must endure long term contact with hot air until 220-230 °C. Very good properties retention after ageing. Typical applications in automotive are under bonnet components, like turbo air ducts, intercooler end caps. This material can be processed with water conditioned tools.

This material data has been provided by Radici Group.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting StandardThickness

Density

1.58 g/cm³

Show Supplier Material materials with Density of 1.58 g/cm³

dry

ISO 1183

Moisture absorption

1.2 %

Show Supplier Material materials with Moisture absorption of 1.2 %

50% RH

ISO 62

2 mm

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

18 GPa

Show Supplier Material materials with Elastic modulus of 18 GPa

dry

ISO 527-2/1A

1mm/min

Elongation

3 %

Show Supplier Material materials with Elongation of 3 %

dry

ISO 527-2/1A

5mm/min

Flexural modulus

15 GPa

Show Supplier Material materials with Flexural modulus of 15 GPa

dry

ISO 178

2mm/min

Flexural strength

358 MPa

Show Supplier Material materials with Flexural strength of 358 MPa

dry

ISO 178

2mm/min

Impact strength, Charpy notched

-30 °C

18 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 18 kJ/m²

dry

ISO 179/1eA

23 °C

20 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 20 kJ/m²

dry

ISO 179/1eA

Impact strength, Charpy unnotched

-30 °C

110 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 110 kJ/m²

dry

ISO 179/1eU

23 °C

100 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 100 kJ/m²

dry

ISO 179/1eU

Unlock all property charts

Tensile strength

233 MPa

Show Supplier Material materials with Tensile strength of 233 MPa

dry

ISO 527-2/1A

5mm/min

Thermal

PropertyValueTesting StandardPressureComment

Heat deflection temperature

260 °C

Show Supplier Material materials with Heat deflection temperature of 260 °C

ISO 75/2Bf

0.45 MPa

Melting point

295 °C

Show Supplier Material materials with Melting point of 295 °C

ISO 11357-1/-3

10°C/min

Flammability

Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | Class: HB ,method: UL 94, and thickness tested (mm): 0.8

Electrical

PropertyValueConditionTesting StandardComment

Surface resistivity

1e+10 Ω/sq

Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq

50%RH

IEC 60093

500V

1e+12 Ω/sq

Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq

dry

IEC 60093

500V

Volume resistivity

1e+12 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+12 Ω·cm

50%RH

IEC 60093

500V

1e+14 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+14 Ω·cm

dry

IEC 60093

500V

Technological properties

Property
Certifications

RoHS 2011/65/UE

Color

Black

Fillers

50% Glass Fiber

Processing methods

Injection Molding