RADITER B RV300 100 NT

Alternative and trade names
PBT-GF30
Want to keep this datasheet? Save it now in your required format

Description

PBT 30% glass fibre reinforced injection moulding grade. Natural colour.

Suitable for parts requiring high stiffness and good mechanical resistance.

This material data has been provided by Radici Group.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.53 g/cm³

Show Supplier Material materials with Density of 1.53 g/cm³

ISO 1183

Moisture absorption

23.0 °C

0.1 %

Show Supplier Material materials with Moisture absorption of 0.1 %

ISO 62, 50% RH, thickness tested (mm): 2

Water absorption

23.0 °C

0.3 %

Show Supplier Material materials with Water absorption of 0.3 %

ISO 62, thickness tested (mm): 2

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

9.8 GPa

Show Supplier Material materials with Elastic modulus of 9.8 GPa

ISO 527-2/1A, 1mm/min

Elongation

23.0 °C

3 %

Show Supplier Material materials with Elongation of 3 %

ISO 527-2/1A, 5mm/min

Flexural modulus

23.0 °C

8.6 GPa

Show Supplier Material materials with Flexural modulus of 8.6 GPa

ISO 178, 2mm/min

Flexural strength

23.0 °C

210 MPa

Show Supplier Material materials with Flexural strength of 210 MPa

ISO 178, 2mm/min

Impact strength, Charpy notched

23.0 °C

10 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

23.0 °C

60 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 60 kJ/m²

ISO 179/1eU

Tensile strength

23.0 °C

145 MPa

Show Supplier Material materials with Tensile strength of 145 MPa

ISO 527-2/1A, 5mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

2.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 2.5E-5 1/K

ISO 11359-1/-2, 23°C-55°C

Coefficient of thermal expansion, transverse

23.0 °C

9E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 9E-5 1/K

ISO 11359-1/-2, 23°C-55°C

Heat deflection temperature, 0.45 MPa

220 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 220 °C

ISO 75/2Bf

Heat deflection temperature, 1.80 MPa

205 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 205 °C

ISO 75/2Af

Melting point

225 °C

Show Supplier Material materials with Melting point of 225 °C

ISO 11357-1/-3, 10°C/min

Vicat softening temperature

210 °C

Show Supplier Material materials with Vicat softening temperature of 210 °C

ISO 306, 50°C/h 50N

Flammability

Class: HB ,method: UL 94, and thickness tested (mm): 1.6

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

450 V

Show Supplier Material materials with Comparative tracking index of 450 V

IEC 60112, Sol.A

Surface resistivity

23.0 °C

1.00E+12 Ω/sq

Show Supplier Material materials with Surface resistivity of 1.00E+12 Ω/sq

IEC 60093, 500V

Volume resistivity

23.0 °C

1.00E+14 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.00E+14 Ω·cm

IEC 60093, 500V

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

20 g/10min

Show Supplier Material materials with Melt mass-flow rate of 20 g/10min

ISO 1133, 250°C/2.16Kg

Shrinkage

23.0 °C

1 %

Show Supplier Material materials with Shrinkage of 1 %

ISO 294-4, normal

Shrinkage, transverse

23.0 °C

0.3 %

Show Supplier Material materials with Shrinkage, transverse of 0.3 %

ISO 294-4, parallel

Technological properties

Property
Certifications

RoHS 2011/65/UE

Color

Natural

Fillers

30% Glass Fiber

Processing methods

Injection Molding