General
Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|---|
Density | 1.58 g/cm³ Show Supplier Material materials with Density of 1.58 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1.1 % Show Supplier Material materials with Moisture absorption of 1.1 % | 50%RH | ISO 62 | 2 mm | |
Water absorption | 4 % Show Supplier Material materials with Water absorption of 4 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanical
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elastic modulus | 14.2 GPa Show Supplier Material materials with Elastic modulus of 14.2 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
17 GPa Show Supplier Material materials with Elastic modulus of 17 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Elongation | 3 % Show Supplier Material materials with Elongation of 3 % | dry | ISO 527-2/1A | 5mm/min | |
3.1 % Show Supplier Material materials with Elongation of 3.1 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Flexural modulus | 15.4 GPa Show Supplier Material materials with Flexural modulus of 15.4 GPa | 50%RH | ISO 178 | 2mm/min | |
15.5 GPa Show Supplier Material materials with Flexural modulus of 15.5 GPa | dry | ISO 178 | 2mm/min | ||
Flexural strength | 305 MPa Show Supplier Material materials with Flexural strength of 305 MPa | 50%RH | ISO 178 | 2mm/min | |
375 MPa Show Supplier Material materials with Flexural strength of 375 MPa | dry | ISO 178 | 2mm/min | ||
Impact strength, Charpy notched | -30 °C | 16 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 16 kJ/m² | dry | ISO 179/1eA | |
23 °C | 18 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 18 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 25 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 25 kJ/m² | 50%RH | ISO 179/1eA | ||
Impact strength, Charpy unnotched | -30 °C | 102 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 102 kJ/m² | dry | ISO 179/1eU | |
23 °C | 100 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | dry | ISO 179/1eU | ||
23 °C | 112 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 112 kJ/m² | 50%RH | ISO 179/1eU | ||
Tensile strength | 190 MPa Show Supplier Material materials with Tensile strength of 190 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
245 MPa Show Supplier Material materials with Tensile strength of 245 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermal
Property | Temperature | Value | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 1.5e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.5e-05 1/K | ISO 11359-1/-2 | 23°C-55°C | ||
8.5e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 8.5e-05 1/K | ISO 11359-1/-2 | 23°C-55°C, Transverse | |||
Glow Wire Flammability Index | 700 °C Show Supplier Material materials with Glow Wire Flammability Index of 700 °C | IEC 60695-2-12 | 1 mm, 2 mm | ||
Glow Wire Ignition Temperature | 725 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 725 °C | IEC 60695-2-13 | 1 mm, 2 mm | ||
Heat deflection temperature | 215 °C Show Supplier Material materials with Heat deflection temperature of 215 °C | ISO 75/2Af | 8.00 MPa | ||
250 °C Show Supplier Material materials with Heat deflection temperature of 250 °C | ISO 75/2Af | 1.80 MPa | |||
Melting point | 260 °C Show Supplier Material materials with Melting point of 260 °C | ISO 11357-1/-3 | 10°C/min | ||
Thermal conductivity | 23 °C | 0.37 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.37 W/(m·K) | |||
Vicat softening temperature | 255 °C Show Supplier Material materials with Vicat softening temperature of 255 °C | ISO 306 | 50°C/h 50N |
Rheological Properties
Property | Value | Testing Standard | Condition | Comment |
---|---|---|---|---|
Melt mass-flow rate | 8.2 g/10min Show Supplier Material materials with Melt mass-flow rate of 8.2 g/10min | ISO 1133 | 275°C/5Kg | |
Shrinkage | 0.2 % Show Supplier Material materials with Shrinkage of 0.2 % | ISO 294-4 | 300/90/60* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.7 % Show Supplier Material materials with Shrinkage of 0.7 % | ISO 294-4 | 300/90/60* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse | |
Viscosity number | 152 cm³/gr Show Supplier Material materials with Viscosity number of 152 cm³/gr | ISO 307 | Sulfuric acid |
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | RoHS 2011/65/UE | |
Color | Deep black | |
Features | Heat Stabilized | |
Fillers | 50% Glass Fiber | |
Processing methods | Injection Molding |