RADILON DT RV500RKC2 306 BK

Alternative and trade names
PA612-GF50

Want to keep this datasheet? Save it now in your required format

Description

PA612 50% glass fibre reinforced injection moulding grade. Heat stabilized, improved flowability. Black colour.

Suitable for parts requiring very high stiffness and high mechanical resistance in direct contact with drinking water and food. Excellent dimensional stability, improved hydrolytic stability and chemical resistance to disinfectants. Product developed for applications in civil and industrial water management as well as appliances.

Equivalent Materials

PA612-GF50

This material data has been provided by Radici Group.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

RADICIGROUP HIGH PERFORMANCE POLYMERS

MANUFACTURER

Additional services:

CAE Service: Customized technical support contributing to the success of innovative projects, including metal replacement applications, realized using RADILON®, RADITECK®, RADISTRONG®, RADIFLAM® and RADITER® engineering plastics. This is what RadiciGroup High Performance Polymers can offer its customers, thanks to its state-of-the-art computer-aided engineering (CAE) virtual simulation tools and the experience of its technical specialists.

Materials by this supplier

RADILON A CP300K 333 BK

RADILON AESTUS T1 RV300FC 306K BK

TORZEN Marathon G3500XHL BK20

RADILON NeXTreme RV500HHR 3800 BK

RADITER B RV300 100 NT

See all materials by this supplier

Use cases

Webinar: Metal Replacement with Engineering Polymers

Properties

General

Property	Temperature	Value	Condition	Testing Standard	Thickness	Comment
Density		1.51 g/cm³ Show Supplier Material materials with Density of 1.51 g/cm³	dry	ISO 1183
Moisture absorption	23 °C	0.6 % Show Supplier Material materials with Moisture absorption of 0.6 %	50%RH	ISO 62	2 mm
Water absorption		1.5 % Show Supplier Material materials with Water absorption of 1.5 %		ISO 62	2 mm	immersion at 23°C

Mechanical

Property	Temperature	Value	Condition	Testing Standard	Comment
Elastic modulus		13.4 GPa Show Supplier Material materials with Elastic modulus of 13.4 GPa	50%RH	ISO 527-2/1A	1mm/min
		14.9 GPa Show Supplier Material materials with Elastic modulus of 14.9 GPa	dry	ISO 527-2/1A	1mm/min
Elongation		3 % Show Supplier Material materials with Elongation of 3 %	dry	ISO 527-2/1A	5mm/min
		3.2 % Show Supplier Material materials with Elongation of 3.2 %	50%RH	ISO 527-2/1A	5mm/min
Flexural modulus		11.9 GPa Show Supplier Material materials with Flexural modulus of 11.9 GPa	50%RH	ISO 178	2mm/min
		13 GPa Show Supplier Material materials with Flexural modulus of 13 GPa	dry	ISO 178	2mm/min
Flexural strength		265 MPa Show Supplier Material materials with Flexural strength of 265 MPa	50%RH	ISO 178	2mm/min
		295 MPa Show Supplier Material materials with Flexural strength of 295 MPa	dry	ISO 178	2mm/min
Impact strength, Charpy notched	-30 °C	14 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 14 kJ/m²	dry	ISO 179/1eA
	23 °C	15 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 15 kJ/m²	dry	ISO 179/1eA
	23 °C	17 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 17 kJ/m²	50%RH	ISO 179/1eA
Impact strength, Charpy unnotched		80 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 80 kJ/m²	dry	ISO 179/1eU	-30°C
		95 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 95 kJ/m²	dry	ISO 179/1eU	23°C
		100 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 100 kJ/m²	50%RH	ISO 179/1eU	23°C
Tensile strength		170 MPa Show Supplier Material materials with Tensile strength of 170 MPa	50%RH	ISO 527-2/1A	5mm/min
		190 MPa Show Supplier Material materials with Tensile strength of 190 MPa	dry	ISO 527-2/1A	5mm/min

Thermal

Property	Value	Testing Standard	Comment
Heat deflection temperature	200 °C Show Supplier Material materials with Heat deflection temperature of 200 °C	ISO 75/2Af	1.00E+12mm
Melting point	220 °C Show Supplier Material materials with Melting point of 220 °C	ISO 11357-1/-3	10°C/min
Flammability	Thickness tested (mm): 1.6, Class: HB, Standard: UL 94 \| Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3

Electrical

Property	Value	Condition	Testing Standard	Comment
Volume resistivity	1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm	50%RH	IEC 60093	500V
	1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm	dry	IEC 60093	500V

Rheological Properties

Property	Value	Condition	Testing Standard	Comment
Shrinkage	0.2 % Show Supplier Material materials with Shrinkage of 0.2 %	280/90/60*	ISO 294-4	*Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa]
	0.6 % Show Supplier Material materials with Shrinkage of 0.6 %	280/90/60*	ISO 294-4	*Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse

Technological properties

Property
Additives	Release agent
Certifications	Food Contact, Drinking Water, RoHS 2011/65/UE
Color	Black
Features	Hydrolysis Resistance, Heat Stabilized
Fillers	50% Glass Fiber
Processing methods	Injection Molding