ALLOW™ Primary Foundry Alloy AlSi10MgMn

Want to keep this datasheet? Save it now in your required format

Description

Low Carbon Primary Foundary ALLOW™ produced with renewable hydropower by RUSAL.

Related Standards

Equivalent Materials

This material data has been provided by Rusal.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyValue

Carbon Footprint

Scope 1&2 (direct and indirect smelter emissions) - less than 4 T CO₂ eq / T Al, average 2,6 T CO₂ eq / T Al. Total carbon footprint from cradle to gate is less than 8 T CO₂ eq / T Al.

Dimension

PropertyValue

Dimensions

Weight: 7 kg, 10 kg, 16 kg

Mechanical

PropertyValueTemperatureComment

Elongation A50

0 - 8 %

Show Supplier Material materials with Elongation A50 of 0 - 8 % at 23.0 °C

23.0 °C

according to DIN EN 1706

Hardness, Brinell

0 - 90 [-]

Show Supplier Material materials with Hardness, Brinell of 0 - 90 [-] at 23.0 °C

23.0 °C

according to DIN EN 1706

Tensile strength

0 - 320 MPa

Show Supplier Material materials with Tensile strength of 0 - 320 MPa at 23.0 °C

23.0 °C

according to DIN EN 1706

Yield strength Rp0.2

0 - 220 MPa

Show Supplier Material materials with Yield strength Rp0.2 of 0 - 220 MPa at 23.0 °C

23.0 °C

according to DIN EN 1706

Chemical properties

Property

Aluminium

Balance

Iron

0 - 0.2 %

Magnesium

0.15 - 0.6 %

Manganese

0.4 - 0.8 %

Other

0 - 0.15 %

Silicon

9 - 11.5 %

Titanium

0 - 0.15 %

Technological properties

Property
Application areas

Structural Applications

Processing history

Smelters: Sayanogorsk Aluminium Smelter (SAZ), Khakas Aluminium Smelter (KHAZ), Irkutsk Aluminium Smelter (IrKAZ)