EN 573-3 Grade AW-2219 T851

Want to keep this datasheet? Save it now in your required format

Description

Aluminum Alloy EN AW-2219, an age-hardenable alloy is produced with a copper additive. It is well-known for its excellent structural strength and it’s used for numerous high temperature applications. It is a suitable alloy for many metalworking processes including machining, forming, heat treatment, cold working, and more.

Related Standards

Equivalent Materials

This material data has been provided by WIAM.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueComment

Density

2.75 - 2.84 g/cm³

Show Material materials with Density of 2.75 - 2.84 g/cm³

Typical for Wrought 2000 Series Aluminium

Mechanical

PropertyTemperatureValueConditionRelated StandardsShapeComment

Elastic modulus

-269.0 °C

82.0 GPa

Show Material materials with Elastic modulus of 82.0 GPa

T851

EN 573-3

-195.0 °C

78.6 GPa

Show Material materials with Elastic modulus of 78.6 GPa

T851

EN 573-3

27.0 °C

70.8 GPa

Show Material materials with Elastic modulus of 70.8 GPa

T851

EN 573-3

Plane-Strain Fracture Toughnes

20.0 °C

36.6 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 36.6 MPa·√m

T851

EN 573-3

20.0 °C

32.6 - 36.6 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 32.6 - 36.6 MPa·√m

T851

EN 573-3

20.0 °C

32.6 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 32.6 MPa·√m

T851

EN 573-3

20.0 °C

39.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 39.0 MPa·√m

T851

EN 573-3

Sheet

20.0 °C

36.0 - 39.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 36.0 - 39.0 MPa·√m

T851

EN 573-3

Sheet

20.0 °C

36.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 36.0 MPa·√m

T851

EN 573-3

Sheet

Unlock all property charts

Poisson's ratio

-269.0 °C

0.341 [-]

Show Material materials with Poisson's ratio of 0.341 [-]

T851

EN 573-3

-195.0 °C

0.355 [-]

Show Material materials with Poisson's ratio of 0.355 [-]

T851

EN 573-3

27.0 °C

0.313 [-]

Show Material materials with Poisson's ratio of 0.313 [-]

T851

EN 573-3

Unlock all property charts

Shear modulus

26.0 - 27.5 GPa

Show Material materials with Shear modulus of 26.0 - 27.5 GPa

Typical for Wrought 2000 Series Aluminium

Tensile strength

-269.0 °C

663.9 MPa

Show Material materials with Tensile strength of 663.9 MPa

T851

EN 573-3

-195.0 °C

563.9 MPa

Show Material materials with Tensile strength of 563.9 MPa

T851

EN 573-3

27.0 °C

470.2 MPa

Show Material materials with Tensile strength of 470.2 MPa

T851

EN 573-3

Unlock all property charts

Yield strength

-269.0 °C

461.3 MPa

Show Material materials with Yield strength of 461.3 MPa

T851

EN 573-3

RP02

-195.0 °C

413.7 MPa

Show Material materials with Yield strength of 413.7 MPa

T851

EN 573-3

RP02

27.0 °C

361.2 MPa

Show Material materials with Yield strength of 361.2 MPa

T851

EN 573-3

RP02

20.0 °C

435.0 MPa

Show Material materials with Yield strength of 435.0 MPa

T851

EN 573-3

Sheet

Unlock all property charts

Thermal

PropertyValueComment

Coefficient of thermal expansion

1.6e-05 - 2.4e-05 1/K

Show Material materials with Coefficient of thermal expansion of 1.6e-05 - 2.4e-05 1/K

Typical for Wrought 2000 Series Aluminium

Melting point

500.0 - 650.0 °C

Show Material materials with Melting point of 500.0 - 650.0 °C

Typical for Wrought 2000 Series Aluminium

Specific heat capacity

816.0 - 963.0 J/(kg·K)

Show Material materials with Specific heat capacity of 816.0 - 963.0 J/(kg·K)

Typical for Wrought 2000 Series Aluminium

Thermal conductivity

112.0 - 251.0 W/(m·K)

Show Material materials with Thermal conductivity of 112.0 - 251.0 W/(m·K)

Typical for Wrought 2000 Series Aluminium

Electrical

PropertyValueComment

Electrical conductivity

18000000.0 - 30000000.0 S/m

Show Material materials with Electrical conductivity of 18000000.0 - 30000000.0 S/m

Typical for Wrought 2000 Series Aluminium

Electrical resistivity

3.4e-08 - 6e-08 Ω·m

Show Material materials with Electrical resistivity of 3.4e-08 - 6e-08 Ω·m

Typical for Wrought 2000 Series Aluminium

Chemical properties

PropertyValueConditionRelated StandardsShape

Copper

5.8 - 6.8 %

Show Material materials with Copper of 5.8 - 6.8 %

T851

EN 573-3

Sheet

Iron

0.3

Show Material materials with Iron of 0.3

T851

EN 573-3

Sheet

Magnesium

0.02

Show Material materials with Magnesium of 0.02

T851

EN 573-3

Sheet

Manganese

0.2 - 0.4 %

Show Material materials with Manganese of 0.2 - 0.4 %

T851

EN 573-3

Sheet

Silicon

0.2

Show Material materials with Silicon of 0.2

T851

EN 573-3

Sheet

Titanium

0.02 - 0.1 %

Show Material materials with Titanium of 0.02 - 0.1 %

T851

EN 573-3

Sheet

Vanadium

0.05 - 0.15 %

Show Material materials with Vanadium of 0.05 - 0.15 %

T851

EN 573-3

Sheet

Zinc

0.1

Show Material materials with Zinc of 0.1

T851

EN 573-3

Sheet

Zirconium

0.1 - 0.25 %

Show Material materials with Zirconium of 0.1 - 0.25 %

T851

EN 573-3

Sheet

Technological properties

Property
Workability

Moderate Workability