Properties
General
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Bulk density | 0.77 g/cm³ Show Supplier Material materials with Bulk density of 0.77 g/cm³ | EN ISO 60 | |
Density | 1.91 g/cm³ Show Supplier Material materials with Density of 1.91 g/cm³ | ||
Water absorption | 0.9 % Show Supplier Material materials with Water absorption of 0.9 % | DIN EN ISO 62 | 23°C | 50 % r.h. up to saturation |
Mechanical
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Elastic modulus | 9.9 GPa Show Supplier Material materials with Elastic modulus of 9.9 GPa | DIN EN ISO 527-1 | 50 mm/min |
Elongation | 1.4 % Show Supplier Material materials with Elongation of 1.4 % | DIN EN ISO 527-1 | 50 mm/min |
Impact strength, Charpy unnotched | 15 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 15 kJ/m² | DIN EN ISO 179-1eU | |
Tensile strength | 80 MPa Show Supplier Material materials with Tensile strength of 80 MPa | DIN EN ISO 527-1 | 50 mm/min |
Thermal
| Property | Value | Testing Standard | Pressure | Comment | |||
|---|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 6.5e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6.5e-05 1/K | DIN EN ISO 11359-1/2 | at 23-80°C | ||||
7e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7e-05 1/K | DIN EN ISO 11359-1/2 | at 23-80°C, Transverse | |||||
Glass transition temperature | 50 °C Show Supplier Material materials with Glass transition temperature of 50 °C | DIN 53765 | |||||
Heat deflection temperature | 189 °C Show Supplier Material materials with Heat deflection temperature of 189 °C | ISO-R 75 Method A | 1.8 MPa | ||||
Max service temperature | 110 °C Show Supplier Material materials with Max service temperature of 110 °C | Long | |||||
170 °C Show Supplier Material materials with Max service temperature of 170 °C | Short | ||||||
Melting point | 255 °C Show Supplier Material materials with Melting point of 255 °C | DIN 53765 | |||||
Specific heat capacity | 1090 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 1090 J/(kg·K) | DIN EN 821 | |||||
Thermal conductivity | 1.1 W/(m·K) Show Supplier Material materials with Thermal conductivity of 1.1 W/(m·K) | DIN EN 821 | in-plane | ||||
1.3 W/(m·K) Show Supplier Material materials with Thermal conductivity of 1.3 W/(m·K) | DIN EN 821 | through-plane | |||||
Thermal diffusivity | 0.5 mm²/s Show Supplier Material materials with Thermal diffusivity of 0.5 mm²/s | DIN EN 821 | through-plane | ||||
0.62 mm²/s Show Supplier Material materials with Thermal diffusivity of 0.62 mm²/s | DIN EN 821 | in-plane | |||||
Flammability | UL94 class V0 for 0.8mm thickness, DIN IEC 60695-11-10 | ||||||
Electrical
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Comparative tracking index | 600 V Show Supplier Material materials with Comparative tracking index of 600 V | DIN EN 60112 | min. |
Dielectric strength | 26.8 kV/mm Show Supplier Material materials with Dielectric strength of 26.8 kV/mm | ISO 60243-1 | |
Surface resistivity | 1e+13 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+13 Ω/sq | DIN EN 61340-2-3 | min. |
Volume resistivity | 1e+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+15 Ω·cm | DIN EN 61340-2-3 |
Rheological Properties
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Melt mass-flow rate | 24 g/10min Show Supplier Material materials with Melt mass-flow rate of 24 g/10min | DIN EN ISO 1133 | 280°C/5kg |
Shrinkage | 1.13 % Show Supplier Material materials with Shrinkage of 1.13 % | DIN EN ISO 294-4 | |
1.22 % Show Supplier Material materials with Shrinkage of 1.22 % | DIN EN ISO 294-4 | Transverse |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electrical engineering, LED lighting technology, Mechanical engineering, Automotive industry camera, moulded interconnect device (PCB, LDS), power distribution in electronics and radar | |
| Color | Gray | |
| Fillers | Mineral Powder | |
| Processing methods | Permissible residual moisture content (%): 0.1, drying temperature (°C): 80, drying time (h): 8, mould temperature (°C): 150, material temperature (°C): 310, cylinder/processing temperature (°C): 310 | |