Property | Value | Testing Standard | Comment |
---|---|---|---|
Bulk density | 0.64 g/cm³ Show Supplier Material materials with Bulk density of 0.64 g/cm³ | EN ISO 60 | |
Density | 1.31 g/cm³ Show Supplier Material materials with Density of 1.31 g/cm³ | ||
Water absorption | 1.8 % Show Supplier Material materials with Water absorption of 1.8 % | DIN EN ISO 62 | 23°C | 50 % r.h. up to saturation |
Mechanical
Property | Value | Testing Standard | Comment |
---|---|---|---|
Elastic modulus | 18.5 GPa Show Supplier Material materials with Elastic modulus of 18.5 GPa | DIN EN ISO 527-1 | 50 mm/min |
Elongation | 2 % Show Supplier Material materials with Elongation of 2 % | DIN EN ISO 527-1 | 50 mm/min |
Impact strength, Charpy unnotched | 40 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 40 kJ/m² | DIN EN ISO 179-1eU | |
Tensile strength | 200 MPa Show Supplier Material materials with Tensile strength of 200 MPa | DIN EN ISO 527-1 | 50 mm/min |
Thermal
Property | Value | Testing Standard | Pressure | Comment | |||
---|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 9e-06 1/K Show Supplier Material materials with Coefficient of thermal expansion of 9e-06 1/K | DIN EN ISO 11359-1/2 | at 70-120°C | ||||
1.2e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.2e-05 1/K | DIN EN ISO 11359-1/2 | at 23-45°C | |||||
7.8e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7.8e-05 1/K | DIN EN ISO 11359-1/2 | at 23-45°C, Transverse | |||||
0.000117 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.000117 1/K | DIN EN ISO 11359-1/2 | at 70-120°C, Transverse | |||||
Glass transition temperature | 72 °C Show Supplier Material materials with Glass transition temperature of 72 °C | DIN 53765 | |||||
Heat deflection temperature | 255 °C Show Supplier Material materials with Heat deflection temperature of 255 °C | ISO-R 75 Method A | 1.8 MPa | ||||
263 °C Show Supplier Material materials with Heat deflection temperature of 263 °C | ISO-R 75 Method B | 0.45 MPa | |||||
Max service temperature | 110 °C Show Supplier Material materials with Max service temperature of 110 °C | Long | |||||
170 °C Show Supplier Material materials with Max service temperature of 170 °C | Short | ||||||
Melting point | 260 °C Show Supplier Material materials with Melting point of 260 °C | DIN 53765 | |||||
Thermal conductivity | 0.7 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.7 W/(m·K) | DIN EN 821 | through-plane | ||||
1.1 W/(m·K) Show Supplier Material materials with Thermal conductivity of 1.1 W/(m·K) | DIN EN 821 | in-plane | |||||
Flammability | UL94 class HB, DIN IEC 60695-11-10 |
Electrical
Property | Value | Testing Standard |
---|---|---|
Volume resistivity | 52000 Ω·cm Show Supplier Material materials with Volume resistivity of 52000 Ω·cm | DIN EN ISO 3915 |
Rheological Properties
Property | Value | Testing Standard | Comment |
---|---|---|---|
Melt mass-flow rate | 75 g/10min Show Supplier Material materials with Melt mass-flow rate of 75 g/10min | DIN EN ISO 1133 | 280°C/5kg |
Melt volume-flow rate | 65 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 65 cm³/10min | DIN EN ISO 1133 | 280°C/5kg |
Shrinkage | 0.36 % Show Supplier Material materials with Shrinkage of 0.36 % | DIN EN ISO 294-4 | |
1 % Show Supplier Material materials with Shrinkage of 1 % | DIN EN ISO 294-4 | Transverse |
Technological properties
Property | ||
---|---|---|
Application areas | Automotive industry: Seat (bumper, roll), Steering, Gear (shift handle and bearings), electronics (radar) and Mechanical engineering | |
Color | Black | |
Fillers | Carbon Fiber and Solid Lubricants | |
Processing methods | Permissible residual moisture content (%): 0.1, drying temperature (°C): 80, drying time (h): 8, mould temperature (°C): 120, material temperature (°C): 300, cylinder/processing temperature (°C): 300 |