General
Property | Value | Testing Standard | Comment |
---|---|---|---|
Bulk density | 0.64 g/cm³ Show Supplier Material materials with Bulk density of 0.64 g/cm³ | EN ISO 60 | |
Density | 1.3 g/cm³ Show Supplier Material materials with Density of 1.3 g/cm³ | ||
Water absorption | 0.4 % Show Supplier Material materials with Water absorption of 0.4 % | DIN EN ISO 62 | 23°C | 50 % r.h. up to saturation |
Mechanical
Property | Value | Testing Standard |
---|---|---|
Elastic modulus | 5.8 GPa Show Supplier Material materials with Elastic modulus of 5.8 GPa | DIN EN ISO 527-1 |
Elongation | 2.5 % Show Supplier Material materials with Elongation of 2.5 % | DIN EN ISO 527-1 |
Impact strength, Charpy unnotched | 30 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 30 kJ/m² | DIN EN ISO 179-1eU |
Tensile strength | 90 MPa Show Supplier Material materials with Tensile strength of 90 MPa | DIN EN ISO 527-1 |
Thermal
Property | Value | Testing Standard | Pressure | Comment | |||
---|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 4e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 4e-05 1/K | DIN EN ISO 11359-1/2 | at 23-80°C | ||||
0.000104 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.000104 1/K | DIN EN ISO 11359-1/2 | at 23-80°C, Transverse | |||||
Glass transition temperature | 15 °C Show Supplier Material materials with Glass transition temperature of 15 °C | DIN 53765 | |||||
Heat deflection temperature | 207 °C Show Supplier Material materials with Heat deflection temperature of 207 °C | ISO-R 75 Method A | 1.8 MPa | ||||
Max service temperature | 100 °C Show Supplier Material materials with Max service temperature of 100 °C | Long | |||||
140 °C Show Supplier Material materials with Max service temperature of 140 °C | Short | ||||||
Melting point | 220 °C Show Supplier Material materials with Melting point of 220 °C | DIN 53765 | |||||
Thermal conductivity | 0.38 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.38 W/(m·K) | DIN EN 821 | through-plane | ||||
0.65 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.65 W/(m·K) | DIN EN 821 | in-plane | |||||
Flammability | UL94 class HB, DIN IEC 60695-11-10 |
Electrical
Property | Value | Testing Standard |
---|---|---|
Surface resistivity | 29000 Ω/sq Show Supplier Material materials with Surface resistivity of 29000 Ω/sq | DIN EN 61340-2-3 |
Volume resistivity | 2.4e+06 Ω·cm Show Supplier Material materials with Volume resistivity of 2.4e+06 Ω·cm | DIN EN 61340-2-3 |
Rheological Properties
Property | Value | Testing Standard | Comment |
---|---|---|---|
Melt mass-flow rate | 20.5 g/10min Show Supplier Material materials with Melt mass-flow rate of 20.5 g/10min | DIN EN ISO 1133 | 240°C/2.16kg |
Melt volume-flow rate | 18 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 18 cm³/10min | DIN EN ISO 1133 | 240°C/2.16kg |
Shrinkage | 0.4 % Show Supplier Material materials with Shrinkage of 0.4 % | DIN EN ISO 294-4 | |
1.1 % Show Supplier Material materials with Shrinkage of 1.1 % | DIN EN ISO 294-4 | Transverse |
Technological properties
Property | ||
---|---|---|
Application areas | Automotive industry: Seat (bumper, roll), Steering, Gear (shift handle and bearings), electronics (radar) and Mechanical engineering | |
Color | Black | |
Fillers | Carbon Fiber | |
Processing methods | Drying temperature (°C): 80, drying time (h): 3, mould temperature (°C): 120, material temperature (°C): , cylinder/processing temperature (°C): 250 |