TECACOMP PEEK TRM X black 1046849

Want to keep this datasheet? Save it now in your required format

Description

PEEK (Polyetheretherketone) filled wih carbon fiber and solid lubricants, showing very good bearing and wear properties

This material data has been provided by Ensinger GmbH.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Bulk density

23.0 °C

0.66 g/cm³

Show Supplier Material materials with Bulk density of 0.66 g/cm³

EN ISO 60

Density

23.0 °C

1.61 g/cm³

Show Supplier Material materials with Density of 1.61 g/cm³

Water absorption

23.0 °C

0.1 %

Show Supplier Material materials with Water absorption of 0.1 %

max., DIN EN ISO 62, 23 °C / 50 % relative humidity up to saturation

Mechanical

PropertyTemperatureValueComment

Compressive modulus

23.0 °C

4100 MPa

Show Supplier Material materials with Compressive modulus of 4100 MPa

EN ISO 604, 1mm/min

Compressive strength

23.0 °C

185 MPa

Show Supplier Material materials with Compressive strength of 185 MPa

EN ISO 604, 5mm/min

Elastic modulus

23.0 °C

12.5 GPa

Show Supplier Material materials with Elastic modulus of 12.5 GPa

DIN EN ISO 527-1, 50mm/min

Elongation

23.0 °C

1.8 %

Show Supplier Material materials with Elongation of 1.8 %

DIN EN ISO 527-1, 50mm/min

Flexural modulus

23.0 °C

10.3 GPa

Show Supplier Material materials with Flexural modulus of 10.3 GPa

DIN EN ISO 178, 2 mm/min

Impact strength, Charpy unnotched

23.0 °C

28 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 28 kJ/m²

DIN EN ISO 179-1eU

Tensile strength

23.0 °C

155 MPa

Show Supplier Material materials with Tensile strength of 155 MPa

DIN EN ISO 527-1, 50mm/min

Flexural strain

DIN EN ISO 178, 2 mm/min

Flexural strength

DIN EN ISO 178, 2 mm/min

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

34.0 °C

1.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.5E-5 1/K

DIN EN ISO 11359-1;2, values applicable for the range 34±11°C, 250±50°C

250.0 °C

2.8E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 2.8E-5 1/K

DIN EN ISO 11359-1;2, values applicable for the range 34±11°C, 250±50°C

Coefficient of thermal expansion, transverse

34.0 °C

3.7E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 3.7E-5 1/K

DIN EN ISO 11359-1;2, values applicable for the range 34±11°C, 250±50°C

250.0 °C

1.22E-4 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.22E-4 1/K

DIN EN ISO 11359-1;2, values applicable for the range 34±11°C, 250±50°C

Unlock all property charts

Glass transition temperature

143 °C

Show Supplier Material materials with Glass transition temperature of 143 °C

DIN 53765

Heat deflection temperature, 0.45 MPa

335 °C

Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 335 °C

ISO-R 75 Method B

Heat deflection temperature, 1.80 MPa

315 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 315 °C

ISO-R 75 Method A

Max service temperature, long

260 °C

Show Supplier Material materials with Max service temperature, long of 260 °C

Max service temperature, short

300 °C

Show Supplier Material materials with Max service temperature, short of 300 °C

Melting point

343 °C

Show Supplier Material materials with Melting point of 343 °C

DIN 53765

Thermal conductivity, in-plane

23.0 °C

1 W/(m·K)

Show Supplier Material materials with Thermal conductivity, in-plane of 1 W/(m·K)

DIN EN 821

Thermal conductivity, through-plane

23.0 °C

0.7 W/(m·K)

Show Supplier Material materials with Thermal conductivity, through-plane of 0.7 W/(m·K)

DIN EN 821

Flammability

UL94 class V0, DIN IEC 60695-11-10

Electrical

PropertyTemperatureValueComment

Surface resistivity

23.0 °C

160000 Ω/sq

Show Supplier Material materials with Surface resistivity of 160000 Ω/sq

DIN EN 61340-2-3

Volume resistivity

23.0 °C

1.70E+7 Ω·cm

Show Supplier Material materials with Volume resistivity of 1.70E+7 Ω·cm

DIN EN 61340-2-3

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

27 g/10min

Show Supplier Material materials with Melt mass-flow rate of 27 g/10min

DIN EN ISO 1133, 380°C/5kg

Melt volume-flow rate

25 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 25 cm³/10min

DIN EN ISO 1133, 380°C/5kg

Shrinkage

23.0 °C

0.26 %

Show Supplier Material materials with Shrinkage of 0.26 %

DIN EN ISO 294-4

Shrinkage, transverse

23.0 °C

0.64 %

Show Supplier Material materials with Shrinkage, transverse of 0.64 %

DIN EN ISO 294-4

Technological properties

Property
Application areas

Automotive industry: Seat (bumper, roll), Steering, Gear (shift handle and bearings), electronics (radar) and Mechanical engineering

Color

Black

Detectability

Fillers

Carbon Fiber and Solid lubricants

Processing methods

Permissible residual moisture content (%): 0.02, drying temperature (°C): 180, drying time (h): 6, mould temperature (°C): 200, material temperature (°C): 400, cylinder/processing temperature (°C): 400