TECACOMP PEEK TRM PVX SIC grey 1047410

Want to keep this datasheet? Save it now in your required format

This material data has been provided by Ensinger GmbH.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Bulk density

23.0 °C

0.57 g/cm³

Show Supplier Material materials with Bulk density of 0.57 g/cm³

EN ISO 60

Density

23.0 °C

1 g/cm³

Show Supplier Material materials with Density of 1 g/cm³

Water absorption

23.0 °C

0.1 %

Show Supplier Material materials with Water absorption of 0.1 %

max., DIN EN ISO 62, 23 °C / 50 % relative humidity up to saturation

Mechanical

PropertyTemperatureValueComment

Compressive modulus

23.0 °C

5810 MPa

Show Supplier Material materials with Compressive modulus of 5810 MPa

EN ISO 604

Compressive strength

23.0 °C

65.9 MPa

Show Supplier Material materials with Compressive strength of 65.9 MPa

EN ISO 604, 1%

Elastic modulus

23.0 °C

0.01 GPa

Show Supplier Material materials with Elastic modulus of 0.01 GPa

DIN EN ISO 527-1

Elongation

23.0 °C

2.2 %

Show Supplier Material materials with Elongation of 2.2 %

DIN EN ISO 527-1

Impact strength, Charpy unnotched

23.0 °C

23.6 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 23.6 kJ/m²

DIN EN ISO 179-1eU

Tensile strength

23.0 °C

111 MPa

Show Supplier Material materials with Tensile strength of 111 MPa

DIN EN ISO 527-1

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

81.5 °C

1.9E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.9E-5 1/K

DIN EN ISO 11359-1;2, values applicable for the range 81.5±58.5°C, 232.5±52.5°C

232.5 °C

3.8E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 3.8E-5 1/K

DIN EN ISO 11359-1;2, values applicable for the range 81.5±58.5°C, 232.5±52.5°C

Glass transition temperature

143 °C

Show Supplier Material materials with Glass transition temperature of 143 °C

Max service temperature, long

260 °C

Show Supplier Material materials with Max service temperature, long of 260 °C

Max service temperature, short

300 °C

Show Supplier Material materials with Max service temperature, short of 300 °C

Melting point

343 °C

Show Supplier Material materials with Melting point of 343 °C

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

17.8 g/10min

Show Supplier Material materials with Melt mass-flow rate of 17.8 g/10min

DIN EN ISO 1133, 380°C/5kg

Shrinkage

23.0 °C

0.39 %

Show Supplier Material materials with Shrinkage of 0.39 %

DIN EN ISO 294-4

Shrinkage, transverse

23.0 °C

1.23 %

Show Supplier Material materials with Shrinkage, transverse of 1.23 %

DIN EN ISO 294-4

Technological properties

Property
Application areas

Automotive industry: Seat (bumper, roll), Steering, Gear (shift handle and bearings), electronics (radar)

Color

Gray

Fillers

Silicon Carbide

Processing methods

Permissible residual moisture content (%): 0.02, drying temperature (°C): 140-180, drying time (h): 4-6, mould temperature (°C): 160-200, material temperature (°C): 390-400, cylinder/processing temperature (°C): 360-400