Property | Value | Testing Standard | Comment |
---|---|---|---|
Bulk density | 0.56 g/cm³ Show Supplier Material materials with Bulk density of 0.56 g/cm³ | EN ISO 60 | |
Water absorption | 0.006 % Show Supplier Material materials with Water absorption of 0.006 % | DIN EN ISO 62 | 50 % r.h. (24 h) |
Mechanical
Property | Value | Testing Standard |
---|---|---|
Elastic modulus | 27 GPa Show Supplier Material materials with Elastic modulus of 27 GPa | DIN EN ISO 527-1 |
Elongation | 0.7 % Show Supplier Material materials with Elongation of 0.7 % | DIN EN ISO 527-1 |
Impact strength, Charpy unnotched | 25 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 25 kJ/m² | DIN EN ISO 179-1eU |
Tensile strength | 160 MPa Show Supplier Material materials with Tensile strength of 160 MPa | DIN EN ISO 527-1 |
Thermal
Property | Value | Testing Standard | Pressure | Comment | |||
---|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 7e-06 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7e-06 1/K | DIN EN ISO 11359-1/2 | at 23-80°C | ||||
1.9e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.9e-05 1/K | DIN EN ISO 11359-1/2 | at 130-220°C | |||||
2.8e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.8e-05 1/K | DIN EN ISO 11359-1/2 | at 23-80°C, Transverse | |||||
6.3e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 6.3e-05 1/K | DIN EN ISO 11359-1/2 | at 130-220°C, Transverse | |||||
Glass transition temperature | 90 °C Show Supplier Material materials with Glass transition temperature of 90 °C | DIN 53765 | |||||
Heat deflection temperature | 277 °C Show Supplier Material materials with Heat deflection temperature of 277 °C | ISO-R 75 Method A | 1.8 MPa | ||||
Max service temperature | 230 °C Show Supplier Material materials with Max service temperature of 230 °C | Long | |||||
260 °C Show Supplier Material materials with Max service temperature of 260 °C | Short | ||||||
Melting point | 280 °C Show Supplier Material materials with Melting point of 280 °C | DIN 53765 | |||||
Thermal conductivity | 0.46 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.46 W/(m·K) | DIN EN 821 | through-plane | ||||
1.21 W/(m·K) Show Supplier Material materials with Thermal conductivity of 1.21 W/(m·K) | DIN EN 821 | in-plane | |||||
Flammability | UL94 class V0 for 1.6 and 3.2mm thickness, DIN IEC 60695-11-10 |
Rheological Properties
Property | Value | Testing Standard | Comment |
---|---|---|---|
Melt mass-flow rate | 6 g/10min Show Supplier Material materials with Melt mass-flow rate of 6 g/10min | DIN EN ISO 1133 | 316°C/2.16kg |
Shrinkage | 0.23 % Show Supplier Material materials with Shrinkage of 0.23 % | DIN EN ISO 294-4 | |
0.51 % Show Supplier Material materials with Shrinkage of 0.51 % | DIN EN ISO 294-4 | Transverse |
Technological properties
Property | ||
---|---|---|
Color | Black | |
Fillers | 30% Carbon Fiber and 15% PTFE | |
Processing methods | Permissible residual moisture content (%): 0.05, drying temperature (°C): 140-150, drying time (h): 4-6, mould temperature (°C): 140-200, material temperature (°C): 335-370, cylinder/processing temperature (°C): 300-370 |