TECACOMP PPS TRM XS black 1061043

Alternative and trade names
PPS-CF
Want to keep this datasheet? Save it now in your required format

Description

PPS (Polyphenylensulfide) filled with carbon fibres and solid lubricants with very good bearing and wear properties

This material data has been provided by Ensinger GmbH.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

Properties

General

PropertyTemperatureValueComment

Bulk density

23.0 °C

0.67 g/cm³

Show Supplier Material materials with Bulk density of 0.67 g/cm³

EN ISO 60

Water absorption

23.0 °C

0.1 %

Show Supplier Material materials with Water absorption of 0.1 %

max., DIN EN ISO 62, 23 °C / 50 % relative humidity up to saturation

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

22 GPa

Show Supplier Material materials with Elastic modulus of 22 GPa

DIN EN ISO 527-1

Elongation

23.0 °C

0.9 %

Show Supplier Material materials with Elongation of 0.9 %

DIN EN ISO 527-1

Impact strength, Charpy unnotched

23.0 °C

22 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 22 kJ/m²

DIN EN ISO 179-1eU

Tensile strength

23.0 °C

150 MPa

Show Supplier Material materials with Tensile strength of 150 MPa

DIN EN ISO 527-1

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

51.5 °C

1E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1E-5 1/K

DIN EN ISO 11359-1;2, values applicable for the range 51.5±28.5°C, 175±45°C

175.0 °C

9E-6 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 9E-6 1/K

DIN EN ISO 11359-1;2, values applicable for the range 51.5±28.5°C, 175±45°C

Coefficient of thermal expansion, transverse

51.5 °C

3.3E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 3.3E-5 1/K

DIN EN ISO 11359-1;2, values applicable for the range 51.5±28.5°C, 175±45°C

175.0 °C

6.4E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 6.4E-5 1/K

DIN EN ISO 11359-1;2, values applicable for the range 51.5±28.5°C, 175±45°C

Unlock all property charts

Glass transition temperature

90 °C

Show Supplier Material materials with Glass transition temperature of 90 °C

DIN 53765

Heat deflection temperature, 1.80 MPa

276 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 276 °C

ISO-R 75 Method A

Max service temperature, long

230 °C

Show Supplier Material materials with Max service temperature, long of 230 °C

Max service temperature, short

260 °C

Show Supplier Material materials with Max service temperature, short of 260 °C

Melting point

280 °C

Show Supplier Material materials with Melting point of 280 °C

DIN 53765

Thermal conductivity, in-plane

23.0 °C

1.4 W/(m·K)

Show Supplier Material materials with Thermal conductivity, in-plane of 1.4 W/(m·K)

DIN EN 821

Thermal conductivity, through-plane

23.0 °C

0.59 W/(m·K)

Show Supplier Material materials with Thermal conductivity, through-plane of 0.59 W/(m·K)

DIN EN 821

Flammability

UL94 class V0, DIN IEC 60695-11-10

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

20 g/10min

Show Supplier Material materials with Melt mass-flow rate of 20 g/10min

DIN EN ISO 1133, 316°C/2.16kg

Shrinkage

23.0 °C

0.17 %

Show Supplier Material materials with Shrinkage of 0.17 %

DIN EN ISO 294-4

Shrinkage, transverse

23.0 °C

0.66 %

Show Supplier Material materials with Shrinkage, transverse of 0.66 %

DIN EN ISO 294-4

Technological properties

Property
Application areas

Automotive industry: Seat (bumper, roll), Steering, Gear (shift handle and bearings), electronics (radar) and Mechanical engineering

Color

Black

Fillers

Carbon Fiber and Solid lubricants

Processing methods

Permissible residual moisture content (%): 0.05, drying temperature (°C): 140-150, drying time (h): 4-6, mould temperature (°C): 140-160, material temperature (°C): 335-360, cylinder/processing temperature (°C): 300-350