Properties
General
Mechanical
| Property | Value | Testing Standard |
|---|---|---|
Elastic modulus | 4 GPa Show Supplier Material materials with Elastic modulus of 4 GPa | DIN EN ISO 527-1 |
Elongation | 2.8 % Show Supplier Material materials with Elongation of 2.8 % | DIN EN ISO 527-1 |
Impact strength, Charpy unnotched | 23 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 23 kJ/m² | DIN EN ISO 179-1eU |
Tensile strength | 65 MPa Show Supplier Material materials with Tensile strength of 65 MPa | DIN EN ISO 527-1 |
Thermal
| Property | Value | Testing Standard | Pressure | Comment | |||
|---|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 3.7e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.7e-05 1/K | DIN EN ISO 11359-1/2 | at 23-100°C | ||||
4.2e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 4.2e-05 1/K | DIN EN ISO 11359-1/2 | at 23-100°C, Transverse | |||||
0.000107 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.000107 1/K | DIN EN ISO 11359-1/2 | at 170-230°C | |||||
0.000113 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.000113 1/K | DIN EN ISO 11359-1/2 | at 170-230°C, Transverse | |||||
Glass transition temperature | 143 °C Show Supplier Material materials with Glass transition temperature of 143 °C | DIN 53765 | |||||
Heat deflection temperature | 165 °C Show Supplier Material materials with Heat deflection temperature of 165 °C | ISO-R 75 Method A | 1.8 MPa | ||||
Max service temperature | 260 °C Show Supplier Material materials with Max service temperature of 260 °C | Long | |||||
300 °C Show Supplier Material materials with Max service temperature of 300 °C | Short | ||||||
Melting point | 343 °C Show Supplier Material materials with Melting point of 343 °C | DIN 53765 | |||||
Thermal conductivity | 0.41 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.41 W/(m·K) | DIN EN 821 | in-plane | ||||
0.49 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.49 W/(m·K) | DIN EN 821 | through-plane | |||||
Flammability | UL94 class V0, DIN IEC 60695-11-10 | ||||||
Electrical
| Property | Value | Testing Standard |
|---|---|---|
Surface resistivity | 2.5e+15 Ω/sq Show Supplier Material materials with Surface resistivity of 2.5e+15 Ω/sq | DIN EN 61340-2-3 |
Volume resistivity | 3.4e+15 Ω·cm Show Supplier Material materials with Volume resistivity of 3.4e+15 Ω·cm | DIN EN 61340-2-3 |
Rheological Properties
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Melt mass-flow rate | 30 g/10min Show Supplier Material materials with Melt mass-flow rate of 30 g/10min | DIN EN ISO 1133 | 380°C/5kg |
Shrinkage | 1.5 % Show Supplier Material materials with Shrinkage of 1.5 % | DIN EN ISO 294-4 | |
1.8 % Show Supplier Material materials with Shrinkage of 1.8 % | DIN EN ISO 294-4 | Transverse |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Automotive industry: Seat (bumper, roll), Steering, Gear (shift handle and bearings), electronics (radar) and Mechanical engineering | |
| Color | Black | |
| Processing methods | Permissible residual moisture content (%): 0.02, drying temperature (°C): 140-180, drying time (h): 4-6, mould temperature (°C): 160-200, material temperature (°C): 390-400, cylinder/processing temperature (°C): 360-400 | |