General
Property | Value | Testing Standard | Comment |
---|---|---|---|
Bulk density | 0.7 g/cm³ Show Supplier Material materials with Bulk density of 0.7 g/cm³ | EN ISO 60 | |
Density | 1.5 g/cm³ Show Supplier Material materials with Density of 1.5 g/cm³ | ||
Water absorption | 0.1 % Show Supplier Material materials with Water absorption of 0.1 % | DIN EN ISO 62 | max. | 23°C | 50 % r.h. up to saturation |
Mechanical
Property | Value | Testing Standard |
---|---|---|
Elastic modulus | 14 GPa Show Supplier Material materials with Elastic modulus of 14 GPa | DIN EN ISO 527-1 |
Elongation | 1.2 % Show Supplier Material materials with Elongation of 1.2 % | DIN EN ISO 527-1 |
Impact strength, Charpy unnotched | 17 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 17 kJ/m² | DIN EN ISO 179-1eU |
Tensile strength | 135 MPa Show Supplier Material materials with Tensile strength of 135 MPa | DIN EN ISO 527-1 |
Thermal
Property | Value | Testing Standard | Pressure | Comment | |||
---|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 1.3e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.3e-05 1/K | DIN EN ISO 11359-1/2 | at 23-70°C | ||||
1.5e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.5e-05 1/K | DIN EN ISO 11359-1/2 | at 100-200°C | |||||
3.9e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.9e-05 1/K | DIN EN ISO 11359-1/2 | at 23-70°C, Transverse | |||||
8.3e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 8.3e-05 1/K | DIN EN ISO 11359-1/2 | at 100-200°C, Transverse | |||||
Glass transition temperature | 90 °C Show Supplier Material materials with Glass transition temperature of 90 °C | DIN 53765 | |||||
Heat deflection temperature | 270 °C Show Supplier Material materials with Heat deflection temperature of 270 °C | ISO-R 75 Method A | 1.8 MPa | ||||
Max service temperature | 230 °C Show Supplier Material materials with Max service temperature of 230 °C | Long | |||||
260 °C Show Supplier Material materials with Max service temperature of 260 °C | Short | ||||||
Melting point | 280 °C Show Supplier Material materials with Melting point of 280 °C | DIN 53765 | |||||
Thermal conductivity | 0.45 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.45 W/(m·K) | DIN EN 821 | through-plane | ||||
1.03 W/(m·K) Show Supplier Material materials with Thermal conductivity of 1.03 W/(m·K) | DIN EN 821 | in-plane | |||||
Flammability | UL94 class V0, DIN IEC 60695-11-10 |
Rheological Properties
Property | Value | Testing Standard | Comment |
---|---|---|---|
Melt mass-flow rate | 20 g/10min Show Supplier Material materials with Melt mass-flow rate of 20 g/10min | DIN EN ISO 1133 | 316°C/2.16kg |
Shrinkage | 0.2 % Show Supplier Material materials with Shrinkage of 0.2 % | DIN EN ISO 294-4 | |
0.8 % Show Supplier Material materials with Shrinkage of 0.8 % | DIN EN ISO 294-4 | Transverse |
Technological properties
Property | ||
---|---|---|
Application areas | Automotive industry: Seat (bumper, roll), Steering, Gear (shift handle and bearings), electronics (radar) and Mechanical engineering | |
Color | Black | |
Fillers | Carbon Fiber and Solid lubricants | |
Processing methods | Permissible residual moisture content (%): 0.05, drying temperature (°C): 140-150, drying time (h): 4-6, mould temperature (°C): 140-160, material temperature (°C): 335-360, cylinder/processing temperature (°C): 300-350 |