extrudr PLA NX2 Filament

Alternative and trade names
PLA

Want to keep this datasheet? Save it now in your required format

Description

PLA NX2 is made from a renewable biodegradable biocompound.

This material data has been provided by extrudr.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Applications

Manufacturing

Additive Manufacturing

Fused Filament Fabrication (Fff)

Consumer Goods

Entertainment

Toys

Construction

Food Industry

Sports Equipment & Facilities

Outdoor Sports Equipment

Show all

Materials by this supplier

extrudr PETG Filament

extrudr PLA NX1 Filament

extrudr Wood Filament

extrudr ABS Filament

extrudr DuraPro ASA Filament

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Bio-based content		100 % Show Supplier Material materials with Bio-based content of 100 %
Density	23.0 °C	1.3 g/cm³ Show Supplier Material materials with Density of 1.3 g/cm³	ISO 1183

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.65 GPa Show Supplier Material materials with Elastic modulus of 2.65 GPa	ISO 178
Elongation	23.0 °C	19 % Show Supplier Material materials with Elongation of 19 %	ISO 527
Flexural modulus	23.0 °C	2.65 GPa Show Supplier Material materials with Flexural modulus of 2.65 GPa	ISO 527
Impact strength, Charpy notched	23.0 °C	7.5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 7.5 kJ/m²	ISO 179-1/1 eA
Impact strength, Izod notched	23.0 °C	64 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 64 kJ/m²	ISO 178
Tensile strength	23.0 °C	49 MPa Show Supplier Material materials with Tensile strength of 49 MPa	ISO 527

Thermal

Property	Value	Comment
Melting point	150 - 170 °C Show Supplier Material materials with Melting point of 150 - 170 °C	ISO 3146-C
Vicat softening temperature	60 °C Show Supplier Material materials with Vicat softening temperature of 60 °C	ISO 306

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		3.5 g/10min Show Supplier Material materials with Melt mass-flow rate of 3.5 g/10min	ISO 1133
Shrinkage	23.0 °C	0.3 % Show Supplier Material materials with Shrinkage of 0.3 %	ISO 294-4

Technological properties

Property
Application areas	Biocompounds with high impact resistance and a matte surface are suitable for industrial use, rapid prototyping, architecture, food applications, toys and outdoor novelties.
Handling recommendations	Store at room temperature (18-27°C / 65-80°F), out of direct heat and sunlight, and in a dry place. When stored correctly, this material has a shelf life of 1 year.