General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 10.15 g/cm³ Show Supplier Material materials with Density of 10.15 g/cm³ |
Surface roughness | 1 μm Show Supplier Material materials with Surface roughness of 1 μm |
Dimension
Property | Value |
---|---|
Diameter | 4.75 mm Show Supplier Material materials with Diameter of 4.75 mm |
Length | 300 - 1900 mm Show Supplier Material materials with Length of 300 - 1900 mm |
Dimensions | Available dimensions (diameter x length, mm x mm): 6 x 300-3000; 6.35 x 300-3000; 8 x 300-3000; 10 x 100-2900; 12 x 100-3000; 15.875 x 100-1500; 19.05 x 100-1700 |
Mechanical
Property | Temperature | Value |
---|---|---|
Elongation | 23.0 °C | 18 % Show Supplier Material materials with Elongation of 18 % |
Hardness, Vickers | 23.0 °C | 260 - 320 [-] Show Supplier Material materials with Hardness, Vickers of 260 - 320 [-] |
Chemical properties
Property | Value |
---|---|
Aluminium | 1E-4 % Show Supplier Material materials with Aluminium of 1E-4 % |
Cadmium | 1E-4 % Show Supplier Material materials with Cadmium of 1E-4 % |
Chromium | 3E-4 % Show Supplier Material materials with Chromium of 3E-4 % |
Copper | 2E-4 % Show Supplier Material materials with Copper of 2E-4 % |
Iron | 5E-4 % Show Supplier Material materials with Iron of 5E-4 % |
Molybdenum | balance |
Nickel | 1E-4 % Show Supplier Material materials with Nickel of 1E-4 % |
Nitrogen | 5E-4 % Show Supplier Material materials with Nitrogen of 5E-4 % |
Oxygen | 0.01 % Show Supplier Material materials with Oxygen of 0.01 % |
Potassium | 6E-4 % Show Supplier Material materials with Potassium of 6E-4 % |
Silicon | 2E-4 % Show Supplier Material materials with Silicon of 2E-4 % |
Titanium | 0.4 - 0.55 % Show Supplier Material materials with Titanium of 0.4 - 0.55 % |
Tungsten | 0.02 % Show Supplier Material materials with Tungsten of 0.02 % |
Zirconium | 0.06 - 0.12 % Show Supplier Material materials with Zirconium of 0.06 - 0.12 % |
Technological properties
Property | ||
---|---|---|
Application areas | TZM is used in high-temperature applications involving demanding mechanical loads, for example in forging tools or as rotating anodes in X-ray tubes. The recommended temperatures of use are between 700 and 1400 °C. |