General
Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|---|
Density | 1.27 g/cm³ Show Supplier Material materials with Density of 1.27 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1.7 % Show Supplier Material materials with Moisture absorption of 1.7 % | 50%RH | ISO 62 | 2 mm | |
Water absorption | 6 % Show Supplier Material materials with Water absorption of 6 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanical
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Elastic modulus | 14.5 GPa Show Supplier Material materials with Elastic modulus of 14.5 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
23.5 GPa Show Supplier Material materials with Elastic modulus of 23.5 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Elongation | 2.2 % Show Supplier Material materials with Elongation of 2.2 % | dry | ISO 527-2/1A | 5mm/min | |
2.5 % Show Supplier Material materials with Elongation of 2.5 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Flexural modulus | 19.2 GPa Show Supplier Material materials with Flexural modulus of 19.2 GPa | dry | ISO 178 | 2mm/min | |
Flexural strength | 365 MPa Show Supplier Material materials with Flexural strength of 365 MPa | dry | ISO 178 | 2mm/min | |
Impact strength, Charpy notched | -30 °C | 5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 5 kJ/m² | dry | ISO 179/1eA | |
23 °C | 7 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 7 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 9 kJ/m² | 50%RH | ISO 179/1eA | ||
Impact strength, Charpy unnotched | -30 °C | 60 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 60 kJ/m² | dry | ISO 179/1eU | |
23 °C | 65 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 65 kJ/m² | dry | ISO 179/1eU | ||
23 °C | 85 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 85 kJ/m² | 50%RH | ISO 179/1eU | ||
Tensile strength | 160 MPa Show Supplier Material materials with Tensile strength of 160 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
250 MPa Show Supplier Material materials with Tensile strength of 250 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermal
Property | Value | Thickness | Testing Standard | Comment | |||
---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 700 °C Show Supplier Material materials with Glow Wire Flammability Index of 700 °C | 2 mm | IEC 60695-2-12 | ||||
Heat deflection temperature | 235 °C Show Supplier Material materials with Heat deflection temperature of 235 °C | ISO 75/2Af | 1.80 MPa | ||||
250 °C Show Supplier Material materials with Heat deflection temperature of 250 °C | ISO 75/2Bf | 0.45 MPa | |||||
Melting point | 260 °C Show Supplier Material materials with Melting point of 260 °C | ISO 11357-1/-3 | 10°C/min | ||||
Vicat softening temperature | 240 °C Show Supplier Material materials with Vicat softening temperature of 240 °C | ISO 306 | 50°C/h 50N | ||||
Flammability | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): <10 ,method: ISO 3795 and thickness tested (mm): 3 |
Electrical
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Comparative tracking index | 150 V Show Supplier Material materials with Comparative tracking index of 150 V | dry | IEC 60112 | Sol.A |
Surface resistivity | 1000 Ω/sq Show Supplier Material materials with Surface resistivity of 1000 Ω/sq | dry, 50%RH | IEC 60093 | 500V |
Volume resistivity | 100 Ω·cm Show Supplier Material materials with Volume resistivity of 100 Ω·cm | dry, 50%RH | IEC 60093 | 500V |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Shrinkage | 0.2 % Show Supplier Material materials with Shrinkage of 0.2 % | 300/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.4 % Show Supplier Material materials with Shrinkage of 0.4 % | 300/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | Yellow Card, RoHS 2011/65/UE | |
Color | Black | |
Features | Increased Electrical Conductivity | |
Fillers | 30% Carbon Fiber | |
Processing methods | Injection Molding |