RADILON DT RV300RKC2 306 BK

Alternative and trade names
PA612-T GF30, PA612-GF30
Want to keep this datasheet? Save it now in your required format

Description

PA612 30% glass fibre reinforced injection moulding grade. Heat stabilized. Black colour.

Suitable for parts requiring good dimensional stability and mechanical resistance. Intended for prolonged contact with drinking water. Improved resistance to peroxides

This material data has been provided by Radici Group.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting StandardThickness

Density

1.29 g/cm³

Show Supplier Material materials with Density of 1.29 g/cm³

dry

ISO 1183

Water absorption

1.9 %

Show Supplier Material materials with Water absorption of 1.9 %

ISO 62

2 mm

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

8 GPa

Show Supplier Material materials with Elastic modulus of 8 GPa

dry

ISO 527-2/1A

1mm/min

8 GPa

Show Supplier Material materials with Elastic modulus of 8 GPa

50%RH

ISO 527-2/1A

1mm/min

Elongation

3 %

Show Supplier Material materials with Elongation of 3 %

dry

ISO 527-2/1A

5mm/min

4 %

Show Supplier Material materials with Elongation of 4 %

50%RH

ISO 527-2/1A

5mm/min

Flexural modulus

6 GPa

Show Supplier Material materials with Flexural modulus of 6 GPa

50%RH

ISO 178

2mm/min

8 GPa

Show Supplier Material materials with Flexural modulus of 8 GPa

dry

ISO 178

2mm/min

Flexural strength

200 MPa

Show Supplier Material materials with Flexural strength of 200 MPa

50%RH

ISO 178

2mm/min

230 MPa

Show Supplier Material materials with Flexural strength of 230 MPa

dry

ISO 178

2mm/min

Impact strength, Charpy notched

23 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²

dry

ISO 179/1eA

23 °C

13 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 13 kJ/m²

50%RH

ISO 179/1eA

Impact strength, Charpy unnotched

23 °C

66 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 66 kJ/m²

dry

ISO 179/1eU

23 °C

70 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 70 kJ/m²

50%RH

ISO 179/1eU

Unlock all property charts

Tensile strength

125 MPa

Show Supplier Material materials with Tensile strength of 125 MPa

50%RH

ISO 527-2/1A

5mm/min

150 MPa

Show Supplier Material materials with Tensile strength of 150 MPa

dry

ISO 527-2/1A

5mm/min

Thermal

PropertyValueTesting StandardComment

Coefficient of thermal expansion

2e-05 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 2e-05 1/K

ISO 11359-1/-2

23°C-55°C

0.00012

Show Supplier Material materials with Coefficient of thermal expansion of 0.00012

ISO 11359-1/-2

23°C-55°C, Transverse

Melting point

212 °C

Show Supplier Material materials with Melting point of 212 °C

ISO 11357-1/-3

10°C/min

Flammability

Class: HB ,method: UL 94, and thickness tested (mm): 3

Rheological Properties

PropertyValueConditionTesting StandardComment

Shrinkage

0.3 %

Show Supplier Material materials with Shrinkage of 0.3 %

dry

ISO 294-4

0.7 %

Show Supplier Material materials with Shrinkage of 0.7 %

dry

ISO 294-4

Transverse

Technological properties

Property
Certifications

RoHS 2011/65/UE, Food and Water Contact (please get in touch with Radici Group): KTW guidlines and DVGW-standard W270 (11/2007), ACS positive lists include the circular DGC/VS4 n°2000/232 dated 27 april 2000

Color

Black

Fillers

30% Glass Fiber

Processing methods

Injection Molding