Properties
General
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Density | 1.37 g/cm³ Show Supplier Material materials with Density of 1.37 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1.3 % Show Supplier Material materials with Moisture absorption of 1.3 % | 50%RH | ISO 62 | 2 mm | |
Water absorption | 5.5 % Show Supplier Material materials with Water absorption of 5.5 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanical
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Elastic modulus | 7.3 GPa Show Supplier Material materials with Elastic modulus of 7.3 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
9 GPa Show Supplier Material materials with Elastic modulus of 9 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Elongation | 2.8 % Show Supplier Material materials with Elongation of 2.8 % | dry | ISO 527-2/1A | 5mm/min | |
3.5 % Show Supplier Material materials with Elongation of 3.5 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Flexural modulus | 6 GPa Show Supplier Material materials with Flexural modulus of 6 GPa | 50%RH | ISO 178 | 2mm/min | |
8.7 GPa Show Supplier Material materials with Flexural modulus of 8.7 GPa | dry | ISO 178 | 2mm/min | ||
Flexural strength | 165 MPa Show Supplier Material materials with Flexural strength of 165 MPa | 50%RH | ISO 178 | 2mm/min | |
210 MPa Show Supplier Material materials with Flexural strength of 210 MPa | dry | ISO 178 | 2mm/min | ||
Impact strength, Charpy notched | -30 °C | 8.5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 8.5 kJ/m² | dry | ISO 179/1eA | |
23 °C | 9.5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 9.5 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 14 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 14 kJ/m² | 50%RH | ISO 179/1eA | ||
Impact strength, Charpy unnotched | -30 °C | 58 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 58 kJ/m² | dry | ISO 179/1eU | |
23 °C | 60 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 60 kJ/m² | dry | ISO 179/1eU | ||
23 °C | 75 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 75 kJ/m² | 50%RH | ISO 179/1eU | ||
Tensile strength | 105 MPa Show Supplier Material materials with Tensile strength of 105 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
135 MPa Show Supplier Material materials with Tensile strength of 135 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermal
| Property | Value | Testing Standard | Thickness | Comment | |||
|---|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | ISO 11359-1/-2 | 23°C-55°C | ||||
9.1e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 9.1e-05 1/K | ISO 11359-1/-2 | 23°C-55°C, Transverse | |||||
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | IEC 60695-2-12 | 1 mm, 2 mm | ||||
Glow Wire Ignition Temperature | 725 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 725 °C | IEC 60695-2-13 | 1 mm | ||||
775 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 775 °C | IEC 60695-2-13 | 2 mm | |||||
Heat deflection temperature | 245 °C Show Supplier Material materials with Heat deflection temperature of 245 °C | ISO 75/2Af | 1.80 MPa | ||||
Melting point | 260 °C Show Supplier Material materials with Melting point of 260 °C | ISO 11357-1/-3 | 10°C/min | ||||
Vicat softening temperature | 245 °C Show Supplier Material materials with Vicat softening temperature of 245 °C | ISO 306 | 50°C/h 50N | ||||
Flammability | Thickness tested (mm): 0.8, Class: V-0, Standard: UL 94 | Thickness tested (mm): 1.5, Class: 5VA, Standard: UL 94 | Thickness tested (mm): 1.5, Class: 5VA, Standard: IEC 60695-11-20 at dry condition (Burning behaviour),<p>Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||||
Electrical
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Comparative tracking index | 550 V Show Supplier Material materials with Comparative tracking index of 550 V | dry | IEC 60112 | Sol.A |
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Shrinkage | 0.4 % Show Supplier Material materials with Shrinkage of 0.4 % | 280/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
1 % Show Supplier Material materials with Shrinkage of 1 % | 280/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent, Flame retarding agent | |
| Certifications | Yellow Card, RoHS 2011/65/UE | |
| Color | Black | |
| Features | Flame Retardant, Halogen-free, Heat Stabilized | |
| Fillers | 25% Glass Fiber | |
| Processing methods | Injection Molding | |