RADILON S CV300 100 NT

Alternative and trade names
PA6-GB30
Want to keep this datasheet? Save it now in your required format

Description

PA6 30% glass beads filled injection moulding grade. Natural colour.

Suitable for parts requiring good dimensional stability, reduced shrinkage and low warpage. It provides a good surface finish to moulded parts

This material data has been provided by Radici Group.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting StandardThickness

Density

1.34 g/cm³

Show Supplier Material materials with Density of 1.34 g/cm³

dry

ISO 1183

Moisture absorption

2.2 %

Show Supplier Material materials with Moisture absorption of 2.2 %

50% RH

ISO 62

2 mm

Water absorption

8 %

Show Supplier Material materials with Water absorption of 8 %

ISO 62

2 mm

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

2 GPa

Show Supplier Material materials with Elastic modulus of 2 GPa

50%RH

ISO 527-2/1A

1mm/min

4 GPa

Show Supplier Material materials with Elastic modulus of 4 GPa

dry

ISO 527-2/1A

1mm/min

Elongation

12 %

Show Supplier Material materials with Elongation of 12 %

dry

ISO 527-2/1A

50mm/min

50 %

Show Supplier Material materials with Elongation of 50 %

50%RH

ISO 527-2/1A

50mm/min

Elongation at yield

3 %

Show Supplier Material materials with Elongation at yield of 3 %

dry

ISO 527-2/1A

10 %

Show Supplier Material materials with Elongation at yield of 10 %

50%RH

ISO 527-2/1A

Flexural modulus

4 GPa

Show Supplier Material materials with Flexural modulus of 4 GPa

dry

ISO 178

2mm/min

Flexural strength

115 MPa

Show Supplier Material materials with Flexural strength of 115 MPa

dry

ISO 178

2mm/min

Impact strength, Charpy notched

-30 °C

4 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 4 kJ/m²

dry

ISO 179/1eA

23 °C

4 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 4 kJ/m²

dry

ISO 179/1eA

23 °C

6 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 6 kJ/m²

50%RH

ISO 179/1eA

Impact strength, Charpy unnotched

-30 °C

30 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 30 kJ/m²

dry

ISO 179/1eU

23 °C

35 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 35 kJ/m²

dry

ISO 179/1eU

23 °C

40 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 40 kJ/m²

50%RH

ISO 179/1eU

Unlock all property charts

Yield strength

35 MPa

Show Supplier Material materials with Yield strength of 35 MPa

50%RH

ISO 527-2/1A

50mm/min

65 MPa

Show Supplier Material materials with Yield strength of 65 MPa

dry

ISO 527-2/1A

50mm/min

Thermal

PropertyValueThicknessTesting StandardPressureComment

Glow Wire Flammability Index

700 °C

Show Supplier Material materials with Glow Wire Flammability Index of 700 °C

2 mm

IEC 60695-2-12

Heat deflection temperature

70 °C

Show Supplier Material materials with Heat deflection temperature of 70 °C

ISO 75/2Af

2 MPa

170 °C

Show Supplier Material materials with Heat deflection temperature of 170 °C

ISO 75/2Bf

0.45 MPa

Melting point

220 °C

Show Supplier Material materials with Melting point of 220 °C

ISO 11357-1/-3

10°C/min

Vicat softening temperature

200 °C

Show Supplier Material materials with Vicat softening temperature of 200 °C

ISO 306

50°C/h 50N

Flammability

Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | Class: HB ,method: UL 94, and thickness tested (mm): 0.8

Electrical

PropertyValueConditionTesting StandardComment

Comparative tracking index

450 V

Show Supplier Material materials with Comparative tracking index of 450 V

dry

IEC 60112

Sol.A

Surface resistivity

1e+10 Ω/sq

Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq

50%RH

IEC 60093

500V

1e+12 Ω/sq

Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq

dry

IEC 60093

500V

Volume resistivity

1e+12 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+12 Ω·cm

50%RH

IEC 60093

500V

1e+14 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+14 Ω·cm

dry

IEC 60093

500V

Rheological Properties

PropertyValueConditionTesting StandardComment

Shrinkage

1.1 %

Show Supplier Material materials with Shrinkage of 1.1 %

dry

ISO 294-4

1.1 %

Show Supplier Material materials with Shrinkage of 1.1 %

dry

ISO 294-4

Transverse

Technological properties

Property
Certifications

RoHS 2011/65/UE

Color

Natural

Fillers

30% Glass Bead

Processing methods

Injection Molding