RADILON A RV500RW 339 BK

Alternative and trade names
PA66-T GF50,PA66-GF50
Want to keep this datasheet? Save it now in your required format

Description

PA66 50% glass fibre reinforced injection moulding grade. Heat stabilized. Deep black colour

Suitable for technical parts requiring very high stiffness and high mechanical resistance. Excellent heat ageing properties retention, improved welding lines strength. Especially fit for demanding metal replacement applications

This material data has been provided by Radici Group.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.58 g/cm³

Show Supplier Material materials with Density of 1.58 g/cm³

ISO 1183, DAM

Moisture absorption

23.0 °C

1.1 %

Show Supplier Material materials with Moisture absorption of 1.1 %

ISO 62, 50% RH, thickness tested (mm): 2

Water absorption

23.0 °C

4 %

Show Supplier Material materials with Water absorption of 4 %

ISO 62, thickness tested (mm): 2

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

17 GPa

Show Supplier Material materials with Elastic modulus of 17 GPa

ISO 527-2/1A, 1mm/min, DAM

Elongation

23.0 °C

3 %

Show Supplier Material materials with Elongation of 3 %

ISO 527-2/1A, 5mm/min, DAM

Flexural modulus

23.0 °C

16 GPa

Show Supplier Material materials with Flexural modulus of 16 GPa

ISO 178, 2mm/min, DAM

Flexural strength

23.0 °C

385 MPa

Show Supplier Material materials with Flexural strength of 385 MPa

ISO 178, 2mm/min, DAM

Impact strength, Charpy notched

23.0 °C

16 - 30 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 16 - 30 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

-30.0 °C

102 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 102 kJ/m²

ISO 179/1eU

23.0 °C

105 kJ/m²

Show Supplier Material materials with Impact strength, Charpy unnotched of 105 kJ/m²

ISO 179/1eU

Tensile strength

23.0 °C

245 MPa

Show Supplier Material materials with Tensile strength of 245 MPa

ISO 527-2/1A, 5mm/min, DAM

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.5E-5 1/K

ISO 11359-1/-2, 23°C-55°C

Coefficient of thermal expansion, transverse

23.0 °C

8.5E-5 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 8.5E-5 1/K

ISO 11359-1/-2, 23°C-55°C

Heat deflection temperature, 1.80 MPa

255 °C

Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 255 °C

ISO 75/2Af

Heat deflection temperature, 8.0 MPa

215 °C

Show Supplier Material materials with Heat deflection temperature, 8.0 MPa of 215 °C

ISO 75/2Af

Melting point

260 °C

Show Supplier Material materials with Melting point of 260 °C

ISO 11357-1/-3, 10°C/min

Thermal conductivity

23.0 °C

0.37 W/(m·K)

Show Supplier Material materials with Thermal conductivity of 0.37 W/(m·K)

Vicat softening temperature

255 °C

Show Supplier Material materials with Vicat softening temperature of 255 °C

ISO 306, 50°C/h 50N

Flammability

Class: HB ,method: UL 94, and thickness tested (mm): 0.8

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

8.2 g/10min

Show Supplier Material materials with Melt mass-flow rate of 8.2 g/10min

ISO 1133, 275°C/5Kg

Shrinkage

23.0 °C

0.2 %

Show Supplier Material materials with Shrinkage of 0.2 %

ISO 294-4, DAM

Shrinkage, transverse

23.0 °C

0.7 %

Show Supplier Material materials with Shrinkage, transverse of 0.7 %

ISO 294-4, DAM

Technological properties

Property
Certifications

RoHS 2011/65/UE

Color

Black

Fillers

50% Glass Fiber

Processing methods

Injection Molding